• Journal of the Korean Ceramic Society
• /
• v.36 no.1
• /
• pp.7-14
• /
• 1999

TiZrB2 solid solution was synthesized using fine powders of Ti, Zr and B by SHS microwave process. The characterization of the synthesized powder and sintered bodies ws investigated. The combustion temperature and rate were increased with increasing the mole ratio of Zr in temperature profile, and showed the maximum combustion temperature and velocity values of 285$0^{\circ}C$ and 14.6mm/sec in Ti0.2Zr0.8B2 composition. Phase separation has been occured into a composite with TiB2 and ZrB2 phases from TiZrB2 solid solution, which was hot pressed sintering at 30 MPa for an hour at 190$0^{\circ}C$. At the composition of Ti0.8Zr0.2B2 the best properties has been obtained in relative density, bending strength, fracture toughness and hardness, with 99%, 680 MPa, 7.3MPa.m1/2 and 2750 Kg/$\textrm{mm}^2$ respectively.

• Journal of the Korean Ceramic Society
• /
• v.34 no.11
• /
• pp.1099-1106
• /
• 1997

In the present study, the effect of TiB2 addition on the sintering behavior of ZrB2 ceramics was studied with hot pressing under Ar atmosphere. Hot pressing experiments were carried out in graphite dies at the 1$700^{\circ}C$, 180$0^{\circ}C$ under Ar atmosphere. The sintering density increased with increasing TiB2 contents. With the addition of 10wt% TiB2 almost theoretical density could be achieved by hot-pressing at 180$0^{\circ}C$. Zr-Ti-Fe-B compound in liquid phase was observed from the EDS and WDS analysis. It was considered that sinterability was enhanced due to the mass transfer through liquid phase formed at the sintering temperature. In addition of TiB2, transition metal of groups IV, substitutional solid solution could be formed.

• The Korean Journal of Ceramics
• /
• v.6 no.2
• /
• pp.172-176
• /
• 2000

Solid solutions of Ti$_{0.5}$Zr$_{0.5}$B$_2$were successfully synthesized and densified simultaneously from elemental reactants by the use of a field-activated, pressure-assisted synthesis method. The method involves the application of an electric current and mechanical pressure across reactant compacts to achieve combustion synthesis. Dense solid solutions with relative densities of up to 99% were produced and characterized by XRD, SEM, and EPMA methods. With a maximum measured temperature of 145$0^{\circ}C$ under a load of 86 MPa for 30 min, the desired dense solid solution wad synthesized.

• Journal of Hydrogen and New Energy
• /
• v.8 no.3
• /
• pp.101-109
• /
• 1997

We propose a new concept of hydrogen absorbing alloy, "Laves phase related BCC solid solution". It was firstly found among the phases tormed in multicomponent nominal $AB_2$ alloys which consisted of Zr and Ti for the A metal site and 5A, 6A and 7A transition metals for the B metal sites. In these alloys a BCC solid solution often coexisted with a Laves phase. It showed stability of hydrides and reaction kinetics almost identical to intermetallics such as Laves phase alloys. We prepared an almost pure "Laves phase related BCC solid solution" and found that it had a large hydrogen capacity (more than 2 mass%) and fast hydrogen absorption and desorption kinetics at ambient temperature and pressure. This new hydrogen absorbing alloy may open a new era of hydrogen related application such as hydrogen vehicles.

• Journal of the Korean Vacuum Society
• /
• v.17 no.4
• /
• pp.317-321
• /
• 2008

The $0.65Pb(Mg_{1/3}Ta_{2/3})O_3-0.35PbTiO_3$ (PMT-PT)ceramics were near morphotropic phase boundary. The dielectric constant, the loss, and pyroelectric coefficient of the ceramics were measured as a function of temperature ($25^{\circ}C\;{\sim}\;250^{\circ}C$). The dielectric constant, the loss, and the pyroelectric coefficient could be improved with the addition of small amounts of $ZrO_2$ up to 0.2 mol%. The dielectric and pyroelectric peak temperature are slightly shifted to lower temperatrues with the addition of amount of $ZrO_2$.