• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.1
• /
• pp.7-15
• /
• 2004

The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{\circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{\circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{\circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $\mu$C/$\textrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.

• Journal of the Korean Ceramic Society
• /
• v.38 no.10
• /
• pp.942-947
• /
• 2001

Thickness dependence of orientation on piezoelectric and electrical properties was investigated by PZT (52/48) films by diol based sol-gel method. The thickness of each layer by spinning at one time was $0.2{\mu}m$ and crack-free films could be successfully deposited on 4 inches Pt/Ti/$SiO_2$/Si substrates by 0.5 mol solutions in the range from $0.2{\mu}m$ to $3.8{\mu}m$. Excellent P-E hysteresis curves were achieved, which were attributed to the well-densified PZT films and columnar grain without pores or any defects between interlayers. The (111) preferred orientation of films were shown in the range of thickness below $1{\mu}m$. As the thickness increased, the (111) preferred orientation disappeared from $1{\mu}m$ to $3{\mu}m$ region, and the orientation of films became random above $3{\mu}m$. Dielectric constants and longitudinal piezoelectric coefficient, $d_{33}$, measured by pneumatic method were saturated around the value of about 1400 and 300 pC/N respectively above the thickness of $1{\mu}m$.