• 전자공학회논문지A
• /
• 제30A권10호
• /
• pp.59-66
• /
• 1993

PZT thin film deposited by rf magnetron sputtering was annealed by rapid thermal process(RTP) in PbO ambient to prevent vaporing of Pb and interface reactions. Si and TiN/Ti/Si substrates were prepared to survey application of TiN/Ti layer which can prevent interface interaction with Si and crack of PZT thin films. As temperature increased. PZT thin films surface on Si substrate appeared more severe cracks which should affect electrical properties deadly. TiN/Ti(40-150${\mu}{\Omega}{\cdot}cm$) layer applied for buffer layer suppressed interface interaction and film cracking. The measured leakage current(LC) and breakdown voltage(BV) of PZT thin film on TiN/Ti/Si substrate annealed at 650$^{\circ}$C for 15 sec (thickness of 2500$\AA$) were 38 nA/cm2 and 3.5 MV/cm and dielectric constant was 310 at 1 MHz, and remanent polarization (Pr) and coercive field (Ec) were 6.4${\mu}C/cm^{2}$ and 0.2MV/cm at 60 Hz, respectively.

• 한국광학회지
• /
• 제11권5호
• /
• pp.323-329
• /
• 2000

[공기 $ISiO_2ITiNI$ 유리]설계의 반사율이 가시광선 영역에서 0이 되는 TiN의 이상적인 복소수 굴절률을 계산하였다. TiN과 $SiO_2$의 각 층의 두께 변화에 따른 2층 무반사 코팅의 반사율을 전사모의하였으며, 그 결과 TiN의 두께를 조절함으로써 최저 반사율 영역의 폭과 반사율을 변화시킬 수 있었고, $SiO_2$층의 두께를 조절함으로써 반사율이 최저가 되는 중심을 이동시킬 수 있었다. RF 마크네트론 스퍼터링 방법으로 증착한 TiN 박막의 화학적, 구조적, 전기적 특성은 각각 Rutherford backscattering spectroscopy (RBS), atomic force microscope(AFM), 4점 탐침 측정기를 이용하였다. 또한 TiN 박막과 2층 무반사 코팅의 광학적 특성은 분광광도계와 variable angle spectroscopic ellipsometer(VASE)를 이용하여 조사하였다. AFM 측정 결과 TiN 박막의 rms 거칠기는 $9~10\AA$으로 비교적 박막의 표면은 균일하고, 높은 기판온도에서 증착한 TiN 박막의 비저항은 4점 탐침측정 결과 $360~730\mu$\Omega $ cm로 매우 낮으며, RBS측정 결과 Ti:O:N=1:0.65:0.95 비율로 산소가 포함되어 있음을 알았다. 이러한 TiN 박막의 특성과 전산모의 바탕으로 증착한 TiN층을 이용한 2층 무반사 무정전 코팅[공기 $ISiO_2ITiNI$ 유리]의 반사율은 440~650 nm영역에서 0.5% 미만이었다.

• 한국분말재료학회지
• /
• 제4권3호
• /
• pp.196-204
• /
• 1997

Joining of AIN ceramics to W and Cu by active-metal brazing method was tried with use of (Ag-Cu)-Ti alloy as insert-metal. Joints were produced under various conditions of temperature, holding time and Ti-content in (Ag-Cu) alloy Reaction and microstructural development in bonded interface were investigated through observation and analysis by SEM/EDS, EPMA and XRD. Joint strengths were measured by shear test. Bonded interface consists of two layers: an insert-metal layer of eutectic Ag- and Cu-rich phases and a reaction layer of TiN. Thickness of reaction layer increases with bonding temperature, holding time and Ti-content of insert-metal. It was confirmed that the growth of reaction layer is a diffusion-controlled process. Activation energy for this process was 260 KJ/mol which is lower than that for N diffusion in TiN. Maximum shear strength of 108 MPa and 72 MPa were obtained for AIN/W and AIN/Cu joints, respectively. Relationship between processing variables, joint strength and thickness of reaction layer was also explained.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2002년도 proceedings of the second asia international conference on tribology
• /
• pp.167-168
• /
• 2002

In this study, the effects of oxide layer formed on the wear tracks of TiN coated silicon wafer on friction characteristics were investigated. Silicon wafer was used for the substrate of coated disk specimens, which were prepared by depositing TiN coating with $1\;{\mu}m$ in coating thickness. AISI 52100 steel balls were used for the counterpart. The tests were performed both in air for forming oxide layer on the wear track and in nitrogen to avoid oxidation. This paper reports characterization of the oxide layer effects on friction characteristics using X-ray diffraction (XRD). scanning electron microscopy (SEM) and friction force microscope (FFM).

• Tribology and Lubricants
• /
• 제26권1호
• /
• pp.68-72
• /
• 2010

A ceramic coating is a surface treatment method that is being used widely in the industrial field, recently. Ni-P plating is also being used widely because of its corrosion resistance and low cost. An anodizing method is applicable to aluminum alloy. An anodizing method generates a thick oxide layer on the surface and then, that heightens hardness and protects the surface. These surface treatments are applied to various mechanical components and treated surfaces relatively move one another. In this study, tribological characteristics of Ni-P plating and TiAlN coating on anodized Al alloy are compared. The counterpart, anodized Al alloy, is worn out abrasively by Ni-P plating and TiAlN coating that have higher hardness. Abrasively worn debris accumulated on the surfaces of Ni-P plating and TiAlN coating, and then transferred layer is formed. This transferred layer affects the amplitude of variation of friction coefficient, which is related to noise and vibration. The amplitude of variation of friction coefficient of Ni-P plating is lower than those of TiAlN coating during the tests.

• 한국세라믹학회지
• /
• 제56권1호
• /
• pp.49-55
• /
• 2019

$Ti_{0.33}Al_{0.67}N/CrN$ nano-multilayers, which are known to have excellent wear resistance, were prepared using an unbalanced magnetron sputter to have various periods of 2-5 nm. $Ti_{0.33}Al_{0.67}N$ had a hexagonal structure in a single layer, but converted to a cubic structure by forming a multilayer with CrN, which has a cubic structure. Thus, $Ti_{0.33}Al_{0.67}N$ formed a superlattice in the multilayer. The $Ti_{0.33}Al_{0.67}/CrN$ multilayer with a period of 2.5 nm greatly exceeded the hardness of the $Ti_{0.33}Al_{0.67}N$ and the CrN single layer, reaching 39 GPa. According to the low angle X-ray diffraction results, the $Ti_{0.33}Al_{0.67}N/CrN$ multilayer maintained its as-coated structure to a temperature as high as $700^{\circ}C$ and exhibited hardness of 30 GPa. The thickness of the oxide layer of the $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating was less than one-tenth of those of the single layers. Thus, $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating had hardness and oxidation resistance far superior to those of its constituent single layers.

• 한국표면공학회지
• /
• 제25권1호
• /
• pp.16-23
• /
• 1992

Generally brittle eta phase produced during TiC deposition has a bad effect on the TRS (transverse rupture strength ; thoughness). Therefore it is necessary to reduce eta(η) phase for the improvement of tool life. At this experiment some properties (TRS, bonding strength, tool life, eta phase) have been investigated by inserting TiN or TiCN underlayer between TiC layer and substrate. The results obtained were as fellows; 1. by inserting underlayer eta phase was decreased and TRS was increased, but the bonding strength was decreased. 2. the diffusion of W, Co from the substrate was hindered by the underlayer. 3. TiC layer with TiCN underlayer had the finsest gain size. 4. by inserting underlayer (TiCN or TiN) the tool life was improved and especially notch and crater wear resistance was greatly improved.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.97.2-97.2
• /
• 2018

This study formed a hard TiAlSiWN coating layer using Ti, Al, Si and W raw powders that were mechanically alloyed and refined. The TiAlSi and TiAlSiW coating targets were fabricated using a single PCAS process in a short time with the optimal sintering conditions. The coating targets were deposited on the WC substrate by forming coating layers using TiAlSiN and TiAlSiWN nitride nano-composite structures with an AIP process. The properties of the nitride nano-composite coating layers were compared according to the addition of W. The microstructure of the nitride nano-composite coating layer was analyzed, focusing on the distribution of the crystalline phases, amorphous phases ($Si_3N_4$), and growth orientation of the columnar crystal depending on the addition of W. The mechanical properties of the coating layers were exhibited a hardness of approximately $3,000kg/mm^2$ and adhesion of about 117.77N in the TiAlSiN. In particular, the TiAlSiWN showed excellent properties with a hardness of more than $4,300kg/mm^2$ and an adhesion of about 181.47N.

• Tribology and Lubricants
• /
• 제27권3호
• /
• pp.147-155
• /
• 2011

The ceramic coatings are excellent materials of cutting tools and sliding parts. To evaluate the wear characteristics of very thin ceramic coated layer, it is very important to investigate its wear process microscopically. An effective method for investigating the wear of a thin layer is the observation of wear process in microscopic detail using in-situ system. In this study, using the SEM Tribosystem as in-situ system, the microscopic wear mode of TiN coatings was investigated in repeated sliding. As results, four modes were observed for TiN coatings: Ploughing, powder formation, flake formation and coating delimitation. The observation of the microscopic wear by in-situ system can clarify the allowable stress of TiN coating.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 추계학술대회논문집
• /
• pp.245-251
• /
• 2004

This paper is studied on the effect of TiAlN coated Ball End Mill and MQL(Minimum Quantity Lubrication) cutting condition on cutting characteristic of high hardness steels. KP4 steels[HRC32] and STD11[HRC60] heat treated steels were used as the workpiece and WC-Co ball end mill and single and multi layer TiAlN coated ball end mill were utilized in the cutting tests. MQL device was used to spray botanical oil coolant. Result showed that TiAlN coated ball end mill were increased the cutting length than WC-Co ball end mill in the cutting speed[$245{\sim}320m/min$] about $2.3{\sim}5.7$ times for KP4 steels and about $2.5{\sim}4.3$ times far STD11 heat treated steels. The multi layer TiAlN coated ball end mill is good for KP4 steels than single layer coated.