• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.8
• /
• pp.1163-1172
• /
• 2001

The two dimensional problem of a layered tribological system(TiN/Steel) containing a vertical surface breaking crack and subject to rolling contact is considered in this study. Using finite elements and stress extrapolation method, a series of preliminary models are developed. Preliminary results indicate that the extrapolation technique is valid to determine Modes I and II stress intensity factors for cracks. In the case of TiN/Steel medium, KI and KII were determined for variations in crack length, layer thickness, and load location. The results show that KII reaches maximum values when the contact is adjacent to the crack where Mode I stresses are compressive. KII values decrease with decreased crack length and significantly decrease for reduced layer thickness.

• Korean Journal of Materials Research
• /
• v.14 no.6
• /
• pp.394-398
• /
• 2004

A Ti47Al1.7W-3.7Zr alloy was oxidized between $900^{\circ}C$ and $1050^{\circ}C$, and the oxide scales formed were studied. The oxide scales consisted primarily of an outer$TiO_2$ layer, an intermediate $Al_2$$O_3$-rich layer, and an inner mixed ($TiO _2$ + $Al_2$$O_3$) layer. Besides $TiO_2$ and $Al_2$$O_3$, oxidation led to the formation of some $Ti_2$AlN and TiN. Both W and Zr were preferentially segregated below the intermediate $Al_2$$O_3$-rich layer. Tungsten in the oxide scale was present as $WO_3$ and ${Ti}_{x}$$W_{1-x}$, whereas zirconium as monoclic-$ZrO_2$ and tetragonal-$ZrO_2$.

• Korean Journal of Metals and Materials
• /
• v.46 no.10
• /
• pp.691-699
• /
• 2008

Electrochemical characteristics of Ti-30Ta-xZr alloys coated with HA/TiN by using magnetron sputtering method were studied. The Ti-30Ta containing Zr(3, 7, 10 and 15wt%) were 10 times melted to improve chemical homogeneity by using a vacuum furnace and then homogenized for 24hrs at $1000^{\circ}C$. The specimens were cut and polished for corrosion test and coating, and then coated with HA/TiN, respectively, by using DC and RF-magnetron sputtering method. The analyses of coated surface and coated layer were carried out by using optical microscope(OM), field emission scanning electron microscope(FE-SEM) and X-ray diffractometer(XRD). The electrochemical characteristics were examined using potentiodynamic (-1,500 mV~ + 2,000 mV) and A.C. impedance spectroscopy(100 kHz ~ 10 mHz) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The microstructure of homogenized Ti-30Ta-xZr alloys showed needle-like structure. In case of homogenized Ti-30Ta-xZr alloys, a-peak was increased with increasing Zr content. The thickness of TiN and HA coated layer showed 400 nm and 100 nm, respectively. The corrosion resistance of HA/TiN-coated Ti-30Ta-xZr alloys were higher than that of the non-coated Ti-30TaxZr alloys, whic hindicate better protective effect. The polarization resistance($R_p$) value of HA/TiN coated Ti-30Ta-xZr alloys showed $8.40{\times}10^5{\Omega}cm^2$ which was higher than that of non-coated Ti-30Ta-xZr alloys.

• Corrosion Science and Technology
• /
• v.22 no.4
• /
• pp.232-241
• /
• 2023

The mechanical properties of the hydrogen valve responsible for supplying and blocking hydrogen gas in a hydrogen fuel cell electric vehicle (FCEV) were researched. Mechanical properties by hydrogen embrittlement were investigated by coating chromium nitride (CrN) and titanium nitride (TiN) on aluminum alloy by arc ion plating method. The coating layer was deposited to a thickness of about 2 ㎛, and a slow strain rate test (SSRT) was conducted after hydrogen embrittlement to determine the hydrogen embrittlement resistance of the CrN and TiN coating layers. The CrN-coated specimen presented little decrease in mechanical properties until 12 hours of hydrogen charging due to its excellent resistance to hydrogen permeation. However, both the CrN and TiN-coated specimens exhibited deterioration in mechanical properties due to the peeling of the coating layer after 24 hours of hydrogen charging. The specimens coated at 350 ℃ presented a significant decrease in ultimate tensile strength due to abnormal grain growth.

• Journal of Surface Science and Engineering
• /
• v.37 no.5
• /
• pp.249-252
• /
• 2004

Effects of HA and TiN coating on the electrochemical characteristics of Ti-6AI-4V alloys for bone plates were investigated using various test methods. Ti-6AI-4V alloys were fabricated by using a vacuum induction furnace and bone plates were made by laser cutting and polishing. HA was made of extracted tooth sintered and then tooth ash was used as HA coating target. The TiN and HA film coating on the surface were carried on using electron-beam physical vapor deposition (EB-PVD) method. The corrosion behaviors of the samples were examined through potentiodynamic method in 0.9% NaCI solutions at $36.5\pm$$1^{\circ}C$ and corrosion surface was observed using SEM and XPS. The surface roughness of TiN coated bone plates was lower than that of tooth ash coated plates. The structure of TiN coated layer showed the columnar structure and tooth ash coated layer showed equiaxed and anisotrophic structure. The corrosion potential of the TiN coated specimen is comparatively high. The active current density of TiN and tooth ash coated alloy showed the range of about $1.0xl0^{-5}$ $A\textrm{cm}^2$, whereas that of the non-coated alloy was$ 1.0xl0^{-4}$ $A\textrm{cm}^2$. The active current densities of HA and TiN coated bone plates were smaller than that of non-coated bone plates in 0.9% NaCl solution. The pitting potential of TiN and HA coated alloy is more drastically increased than that of the non-coated alloy. The pit number and pit size of TiN and HA coated alloy decreased in compared with those of non-coated alloy. For the coated samples, corrosion resistance increased in the order of TiN coated, tooth ash coated, and non-coated alloy.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2002.05a
• /
• pp.49-49
• /
• 2002

독립된 티타늄(Ti)과 실리콘(Si) 타켓을 사용하여 DC reactive magnetron co-sputtering 공 정으로 Ti-Si-N 코탱막을 SKD 11 합금강위에 합성하였다. 고분해능 TEM 및 XPS 분석들로부터 Ti-Si-N 코탱막은 나노미터 크기의 TiN결정체들이 비정질 Si3N4 기지에 분산된 나노복합체의 마세구조를 냐타내었다. 코탱막의 경도는 11 at.%의 Si 함량에서 39 GPa의 최 고 경도값을 나타내었고 이 경우 미셰조직은 5nm 크기의 미세한 TiN 결정이 비정절상의 기지에 균일하게 분포된 특성을 보였다 .. Ti-Si-N 박막내에 Si 함량이 증가할수록 TiN 결정 상들은 다배향성을 나타내었고 크기가 감소하였으며 비정질상에 의해 완전히 둘려싸언 형상 으로 변화하였다. 높은 Si 함량에서는 질소 소스의 부족현상에 의하여 코팅막내에서 free Si 가 나타났다. 상대습도가 증가함에 따라 Ti-Si-N 코탱막의 마찰계수와 마모량이 현저하게 감소하였다. 강재에 대한 Ti-Si-N 코팅막의 마모거동에 있어서 Si02 냐 Si(OH)2 같은 얇은 윤활막의 형성이 중요한 역할을 하는 것으로 판단되어졌다.

• Journal of Hydrogen and New Energy
• /
• v.24 no.4
• /
• pp.320-325
• /
• 2013

TUnitized reversible fuel cells (URFC) combine the functionality of a fuel cell and electrolyzer in one unitized device. For a URFC with proton exchange membrane, a titanium (Ti)-felt is applied to the gas diffusion layer (GDL) substrate at the oxygen electrode, and additionally titanium (Ti)-powders and TiN-powders are loaded in the GDL substrate as a micro porous layer (MPL). Double porous layer with TiN MPL was not acceptable for the URFC because both of fuel cell performance and electrolysis performance are degraded. The double porous layer with Ti-powder loading in the Ti-felt substrate influence rearly for the electrolysis performance. In contrast, the change of pore-size distribution brings a significant improvement of fuel cell performance under fully humidification conditions. This fact indicates that the hydrophobic meso-pores in the GDL play an important role for mass transport.

• Tribology and Lubricants
• /
• v.8 no.1
• /
• pp.63-69
• /
• 1992

In order to gain better understanding of wear behaviors of TiN-coated boron cast iron, tests and analyses were conducted with block-on disc type tribometer. TiN layer of thickness $2 \mu m$ and $4 \mu m$, coated by cathodic arc evaporation process, were experimentally investigated with the variation of applied load and sliding speed under dry sliding condition. Wear characteristics were expressed in terms of the three-dimentional wear map as well as the wear rate vs sliding speed and load. Comparisons of wear and friction characteristics between coated cast irons and uncoated cast irns were also made. Wear mechanism of TiN layer was explained in view of surface interaction between the mating surfaces. The thicker coating exhibited higher hardness and adhesion strength. the significance of stresses at the surface and in the subsurface was briefly discussed in relation to the wear behavior.

• Journal of the Korean Ceramic Society
• /
• v.53 no.4
• /
• pp.393-399
• /
• 2016

We have successfully fabricated 3D (3-dimensional) nanostructures of $TiO_2$ coated with a $g-C_3N_4$ layer via hydrothermal and sintering methods to enhance photoelectrochemical (PEC) performance. Due to the coupling of $TiO_2$ and $g-C_3N_4$, the nanostructures exhibited good performance as the higher conduction band of $g-C_3N_4$, which can be combined with $TiO_2$. To fabricate 3D nanostructures of $g-C_3N_4/TiO_2$, $TiO_2$ was first grown as a double layer structure on FTO (Fluorine-doped tin oxide) substrate at $150^{\circ}C$ for 3 h. After this, the $g-C_3N_4$ layer was coated on the $TiO_2$ film at $520^{\circ}C$ for 4 h. As-prepared samples were varied according to loading of melamine powder, with values of loading of 0.25 g, 0.5 g, 0.75 g, and 1 g. From SEM and TEM analysis, it was possible to clearly observe the 3D sample morphologies. From the PEC measurement, 0.5 g of $g-C_3N_4/TiO_2$ film was found to exhibit the highest current density of $0.12mA/cm^2$, along with a long-term stability of 5 h. Compared to the pristine $TiO_2$, and to the 0.25 g, 0.75 g, and 1 g $g-C_3N_4/TiO_2$ films, the 0.5 g of $g-C_3N_4/TiO_2$ sample was coated with a thin $g-C_3N_4$ layer that caused separation of the electrons and the holes; this led to a decreasing recombination. This unique structure can be used in photoelectrochemical applications.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.37 no.6
• /
• pp.43-49
• /
• 2000

The TiN thin films were deposited by ALE(atomic layer epitaxy) on (100) silicon substrate. The TiN thin films were characterized by means of XRD, 4-point probe, AFM, AES and SEM. TEMAT(terakis(ethyl methy lamino)titanium) and $NH_3$ were injected into the reactor in sequence of TEMAT-$N_2-NH_3-N_2$ to ensure a saturated surface reaction. As a result, the depostion rate of the TiN film was controlled by self-limiting growth mechanism at temperature range form 150 to 220 $^{\circ}C$. Deposited TiN films, all of which show amorphous structure, had a fixed deposition rate of 4.5 ${\AA}$/cycle. The resistivity of 210 ~ 230 ${\mu}{\Omega}{\cdot}$cm and the surface r.m.s. roughness of 7.9 ~ 9.3 ${\AA}$ were measured. When TiN film of 2000 ${\AA}$ were deposited, a excellent step coverage were observed in a trench structure of 0.43${\mu}m$ contacts with 6:1 aspect ratio.