• Tribology and Lubricants
• /
• v.4 no.2
• /
• pp.44-51
• /
• 1988

Titanium carbide(TiC), Titanium nitride(TiN), and Titanium carbonnitride(Ti(C,N)) films were deposited on $Si_3N_4$-TiC composite cutting tools by chemical vapor deposition(CVD) using $TiCl_4-CH_4-H_2$, $TiCl_4-N_2-H_2$, and $TiCl_4-CH_4-N_2-H_2$ gas mixtures, respectively. The experimental results indicate that TiC coatings compared with TiN coatings on $Si_3N_4$ -TiC ceramic have an improved microstructural property, good thermal shock resistance, and good interfacial bonding. However TiN coatings compared with TiC coatings have a low friction coefficient with steel and good chemical stability. It is found by cutting test that coated insert compared with $Si_3N_4$-TiC ceramic have a superior flank and crater wear resistance. And multilayer coating compared with monolayer coating shows a improved wear resistance.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.119-120
• /
• 2013

공구, 다이몰드 등에 널리 쓰이는 TiC, TiN, CrN, TiCrN, TiAlN 코팅의 산화특성을 비교하기 위하여 $600^{\circ}C-900^{\circ}C$에서 대기중 산화시험을 실시하였다. 내산화성은 (TiC, TiN), TiAlN, TiCrN, CrN 코팅의 순서로 증가하였다. 코팅원소중 Ti는 $TiO_2$로, Cr은 $Cr_2O_3$로, Al은 $Al_2O_3$로 산화되었다.

• Journal of the Korean Ceramic Society
• /
• v.37 no.12
• /
• pp.1165-1171
• /
• 2000

Ti-C-Ni 혼합분말을 이용하여 SHS 공정에 의해 TiC-Ni 복합체를 제조하였으며, 리칭(leaching) 공정을 통하여 Ni을 제거함으로써 TiC 분말을 얻었다. TiC 분말의 특성분석을 위하여 XRD, SEM, TEM, AES 등을 사용하였다. 리칭 공정에 의해 얻어진 TiC 분말은 구형을 유지하고 있으며, 평균 입자크기는 0.4$\mu\textrm{m}$였다. 구형 TiC 분말을 다시 Ni 분말과 혼합하여 소결한 후 특성을 분석하였다. 140$0^{\circ}C$에서 소결하였을 때 TiC 입자는 구형에서 각진 형태로 변화하였다. 기계적 특성결과 상용 TiC 분말을 사용하였을 때보다 SHS 공정에 의해 제조된 TiC 분말을 사용하여 소결하였을 경우 파괴 인성값이 약 20% 증가하였다.

• Journal of the Korean Ceramic Society
• /
• v.33 no.2
• /
• pp.223-227
• /
• 1996

The effect of ZrC and VC addition on the diffusion induced recrystallization (DIR) of TiC-Cr3C2 has been investigated. With in creasing the amount of added ZrC to Cr3C2 the DIR of TiC was suppressed at the begining and then occurred. On the contrary the DIR was accelerated with the addition of VC to Cr3C2 Because the lattice parameters of (Ti, Cr)C and (Ti,V)C are smaller and that of (Ti, Zr)C is larger than that of TiC the lattice parameter of (Ti,Cr,Zr)C is expected to be similar to that of TiC,. The results indicate that the strain energy due to lattice mismatch between TiC and solid-solution carbide is the driving force of the observed energy due to lattice mismatch between TiC and solid-solution carbide is the driving force of the observed DIR.

• Journal of the Korean Ceramic Society
• /
• v.44 no.1 s.296
• /
• pp.37-42
• /
• 2007

The preparation of $TiC_{0.7}N_{0.3}$ powder by SHS in the system of $Ti-TiH_2-C$ ($N_2$ atmosphere) was investigated in this study. In the preparation of $TiC_{0.7}N_{0.3}$ powder, the effect of gas pressure, compositions such as Ti, $TiH_2$, C, and additive in mixture on the reactivity were investigated. At 50 atm of the initial inert gas pressure in reactor, the optimum composition for the preparation of pure $TiC_{0.7}N_{0.3}$ was $0.75Ti+0.25TiH_2+0.7C+0.5NaCl$. The $TiC_{0.7}N_{0.3}$ powder synthesized in this condition was a single phase with irregular shape.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1114-1118
• /
• 2000

Ti 및 C 입자로 이루어진 다공질 성형체에 용융 Si의 침윤 및 반응으로 새로운 Ti$_3$SiC$_2$합성공정이 개발되었다. 용융 Si 침윤에 의한 Ti$_3$SiC$_2$합성공정에서는 이제까지 연구된 합성방법 보다 넓은 조성 범위에서 Ti$_3$SiC$_2$의 합성이 이루어졌다. 용융 Si을 활성 매질로 사용한 Ti$_3$SiC$_2$의 합성에서는 성형체 조성, 원료 입자 크기 및 침윤되는 용융 Si의 양에 따라 합성되는 상 및 각 합성상의 양이 다르게 나타났다. Ti:Si:C=3:1:6 조성을 제외한 모든 조성의 시편에서 Ti$_3$SiC$_2$상이 합성되었으며, 일부 조성을 제외한 모든 조성의 시편에서 Ti$_3$SiC$_2$, TiC 및 SiC가 함께 합성되었다. 작은 Ti 입자로 이루어진 성형체를 사용하여 합성한 시편에서 Ti$_3$SiC$_2$상의 합성이 용이하게 이루어졌으며, 성형체 조성 및 침윤되는 Si의 양이 화학양론적으로 Ti$_3$SiC$_2$에 근접한 조성을 갖는 시편에서 Ti$_3$SiC$_2$를 높은 수율로 합성할 수 있었다.

• The Korean Journal of Ceramics
• /
• v.3 no.2
• /
• pp.124-128
• /
• 1997

An attempt was made to understand the dissolution and reprecipitation behavior of the constituent phases such as TiC, TiN, and Ti(CN) in TiC-TiN-Ni system. During the liquid-phase sintering the TiC phase was found to dissolve preferentially in Ni binder. The solid-solution phase, Ti(CN), formed around the TiN phase, resulting in a core/rim structure. This result was reproduced when large TiC particles were used with fine TiN particles. The path for the microstructural change in TiC-TiN-Ni system was largely controlled by the difference in the interfacial energy of each phase with the liquid binder phase. The results were discussed with thermodynamic principles.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.396-400
• /
• 2003

A new synthesis process for nano laminating Ti$_3$SiC$_2$ has been developed using TiCx (x=0.67) and Si powder as starting materials by a reaction hot pressing. Bulk Ti$_3$SiC$_2$ was fabricated using a green body consisting of TiCx and Si by a hot pressing under the pressures of 25 MPa at 1420-1550 $^{\circ}C$ for 90 min. The synthesized Ti$_3$SiC$_2$ was consisting of only TiCx and Ti$_3$SiC$_2$. The relative density of sintered bulk Ti$_3$SiC$_2$ was increased as the hot pressing temperature was increased, which was mainly due to the increase in TiCx contents in synthesized Ti$_3$SiC$_2$. The synthesized Ti$_3$SiC$_2$ bulk was consisted of nano sized lamella structure of 20-100 nm in thickness. It was found that TiCx particles in Ti$_3$SiC$_2$ would increase the 3-point bending strength of synthesized Ti$_3$SiC$_2$ bulk. The maximum 3-P. bending strength of synthesized Ti$_3$SiC$_2$ bulk was more than 800 MPa. The Vickers hardness of synthesized Ti$_3$SiC$_2$bulk was as low as 5 Gpa, which was decreased with the indentation load. The quasi-plastic deformation behaviors were observed around indentation mark on Ti$_3$SiC$_2$.

• Journal of Powder Materials
• /
• v.6 no.1
• /
• pp.18-35
• /
• 1999

Phase equilibria in the system Si3N4-TiC-TiCxN1-x-C-N were determined by thermodynamic calculations (CALPHAD-method). The reaction peaction paths for Si3N4-TiC and SiC-TiC composites in the Ti-Si-C-n system were simulated at I bar N2-pressure and varying terpreatures. At a temperature of 1923 K two tie-triangles (TiC0.34N0.66+SiC+C and TiC0.13N0.87+SiC+Si3N4) and two 2-phase fieds (TiCxN1-x+SiC; 0.13

• Journal of the Korean Ceramic Society
• /
• v.38 no.4
• /
• pp.314-318
• /
• 2001

SiC-TiC composites have been fabricated by using a mechanochemical processing of a mixture of Si, Ti, and C at room temperature and subsequent hot pressing. TiC powders have been obtained by the mechanochemical processing of a mixture of Ti and C whereas SiC powders has not been obtained from a mixture of Si and C. By using the exothermic reaction between Ti and C, SiC-TiC powder could be obtained from the mixture of Si, Ti, and C using the mechanochemical processing for more than 12h. The X-ray diffraction analysis has shown that the powder subjected to the mechanochemical processing consisted of the particles having crystallite size below 10nm. Fully densified SiC-TiC composites have been obtained by hot-pressing of the powder at 1850$\^{C}$ for 3h and it has shown comparable mechanical properties to those of the SiC-TiC composites prepared from the commercially available SiC and TiC powders. Flexural strength of 560 MPa and fracture toughness of 4.8 MP$.$am$\_$1/2/ have been shown for the SiC-TiC composites with composition corresponding to 0.75:0.25:1 mole ratio of Si:Ti:C.