• Journal of the Korean Magnetics Society
• /
• v.5 no.1
• /
• pp.64-70
• /
• 1995

The authors have studied crystallographic and magrletic properties of $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$ by X-ray diffraction, VSM magnetometer, and Mossbauer spectrometer. The Alloys were prepared by arc-melting under argon atmosphere. The $NdFe_{10.7}TiM_{0.3}$ has pure single phase, whereas the $NdFe_{10.7}Ti_{1.3}$ contains some $\alpha-Fe$, from powder X-ray diffractometry. The $NdFe_{10.7}TiM_{0.3}$ has the $ThMn_{12}$-type tetragonal structure with $a_{0}=8.587\;{\AA}\;and\;c_{0}=4.788\;{\AA}$. The Curie temperature ($T_c$) is $570{\pm}3\;K$ from $M\"{o}ssbauer$ spectroscopy performed at various temperatures ranging from 13 to 770 K. Each spectrum of below $T_c$ was fitted with five subspectra of Fe sites in the structure ($8i_{1},\;8i_{2},\;8j_{1},\;8j_{2}\;and\;8f$). The area fraction of the subspectra at room temperature are 16.4, 8.2, 14.8, 21.3 and 39.3 %, respectively. Magenetic hyperfine fields for the Fe sites decrease in the order, $H_{hf}(8i)>H_{hf}(8j)>H_{hf}(8f)$.

• Transactions of the Korean hydrogen and new energy society
• /
• v.11 no.4
• /
• pp.189-202
• /
• 2000

$AB_2$ type Zr-based Laves phases alloys have been studied for potential application as a negative electrode in a Ni-MH battery. The $AB_2$-type electrodes have a much higher energy density than $AB_5$-type electrodes per weight, however they have some disadvantages such as poor activation behavior and cycle life etc. Nonetheless, the $AB_2$-type electrodes have been studied very extensively due to their high energy density. In this study, in order to develop the cycle life, the Mn of $AB_2$ alloy composition was substituted partially by Mo. The alloys were melted by arc furnace and remelted 4-5 times for homogeneity. The alloy powder was used below 200-325 mesh for experiments. The structures and phases of the alloys were analyzed by XRD, SEM and EDS, and measured the curve of a pressure-composition isotherms. The electrodes were prepared by cold pressing of the copper-coated(25 wt%) alloy powders, and tested by a half cell. The results are summarized as follows. The cycle life was improved with the increase of Mo amount in $Zr_{1-x}Ti_xV_{0.4}Ni_{1.2}Mn_{0.4}Mo_y$(x=0.3, 0.4) and the activation was faster, whereas the discharge capacity decreased.

• Korean Journal of Materials Research
• /
• v.3 no.2
• /
• pp.131-139
• /
• 1993

Abstract Alloying elements such as AI, Ti, Nb and B in the extra low carbon AI-killed steel precipitate as nitrides or carbides and change the recrystallization texture structure of the steel during heattreatment with the result of strong effects on the deep drawability of the steel sheet. In this study the effects of fine precipitates such as nitrides and carbides on the texture of extra low carbon steels into which Ti, Nb, B, P, Si and Mn were added as alloying elements were investigated by means of TEM, SEM and optical microscopic analyses. Fine N$b_2$C and T$i_2$AIN precipitates are mainly observed in the steel containing both Nb and Ti, while fine AIN and coarse BN precipitates are observed in the Nb~containing steel and coarse T${i_4}{N_3}$ and ${N_10}{N_22}$/T$i_68$ precipitates are observed in the Ti-containing steel. The grain size of the Ti containing steel is larger than that of the Nb containing steel and that of the one containing both Nb and Ti.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.18 no.7
• /
• pp.97-103
• /
• 2019

Mn+1AXn (MAX) phases are a family of nano-laminated compounds that possess unique combination of typical ceramic properties and typical metallic properties. As a member of MAX-phase, $Ti_2AlN$ bulk materials are attractive for some high temperature applications. In this study, $Ti_2AlN$ bulk with high density were synthesized by spark plasma sintering method. X-ray diffraction, micro-hardness, electrical and thermal conductivity were measured to compare the effect of material properties both $Ti_2AlN$ bulk samples and a conventional Ti-6Al-4V alloy. A femto-second laser conditions were conducted at a repetition rate of 6 kHz and laser intensity of 50 %, 70% and 90 %, respectively, laser confocal microscope were used to evaluate the width and depth of ablation. Consequently, the laser ablation result of the $Ti_2AlN$ sample than that of the Ti-6Al-4V alloys show a considerably good ablation characteristics due to its higher thermal conductivity regardless of to high densification and high hardness.

• Journal of the Korean Magnetics Society
• /
• v.6 no.6
• /
• pp.361-366
• /
• 1996

$NdFe_{10.7}Ti_{1.3}$ has been studied with X-ray diffraction, Mossbauer spectroscopy and vibrating sample magnet-ometer(VSM). The alloys were prepared by arc-melting under an argon atmosphere. The $NdFe_{10.7}Ti_{1.3}$ contains some $\alpha-Fe$, from X-ray and Mossbauer measurements. The $NdFe_{10.7}Ti_{1.3}$ has the $ThMn_{12}$-type tetragonal struc-ture with $a_{0}=8.607{\AA}\;and\;c_{0}=4.790{\AA}$. The Curie temperature ($T_c$) of the $NdFe_{10.7}Ti_{1.3}$ is 590 K from $M\"{o}ssbauer$ spectroscopy performed at various temperatures ranging from 13 to 800 K. Each spectrum below $T_c$ was fitted with six subspectra of Fe sites in the structure$(8i_{1},\;8i_{2},\;8j_{2},\;8j_{1},\;8f\;and\;{\alpha}-Fe)$. The area fractions of the subspectra at room temperature are 13.8%, 15.4%, 17%, 16.4%, 34.1% and 3.3%, respectively. Magenetic hyperfine fields for the Fe sites decrease in the order, $H_{hf}(8i)>H_{hf}(8j)>H_{hf}(8f)$. The abrupt changes in the magnetic hyperfine field, isomer shift and magnetic moment observed at about 180 K in $NdFe_{10.7}Ti_{1.3}$ are attributed to spin reorientation.

• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.134-146
• /
• 1995

Aluminium nitride(AlN) is currently under investigation as potential candidate for replacing alumium oxide(Al$_{2}$ $O_{3}$) as a substrate material for for electronic circuit packaging. Brazing of aluminium nitride(AlN) to Cu with Ag base active alloy containing Ti has been investigated in vacuum. Binary Ag$_{98}$ $Ti_{2}$(AT) and ternary At-1wt.%Al(ATA), AT-1wt.%Ni(ATN), AT-1wt.% Mn(ATM) alloys showed good wettability to AlN and led to the development of strong bond between brate alloy and AlN ceramic. The reaction between AlN and the melted brazing alloys resulted in the formation of continuous TiN layers at the AlN side iterface. This reaction layer was found to increase by increase by increasing brazing time and temperature for all filler metals. The bond strength, measured by 4-point bend test, was increased with bonding temperature and showed maximum value and then decreased with temperature. It might be concluded that optimum thickness of the reaction layer was existed for maximum bond strength. The joint brazed at 900.deg.C for 1800sec using binary AT alloy fractured at the maximum load of 35kgf which is the highest value measured in this work. The failure of this joint was initiated at the interface between AlN and TiN layer and then proceeded alternately through the interior of the reaction layer and AlN ceramic itself.

• Journal of the Korean institute of surface engineering
• /
• v.54 no.2
• /
• pp.43-52
• /
• 2021

The Ni-based superalloy, Inconel 740, was corroded between 800 and 1100℃ for up to 100 hr in air and Ar-0.2%SO₂ gas in order to study its corrosion behavior in air and sulfur/oxygen environment. It displayed relatively good corrosion resistance in both environment, because its corrosion was primarily dominated by not sulfidation but oxidation especially in Ar-0.2%SO₂ gas. Such was attributed to the thermodynamic stability of oxides of alloying elements when compared to corresponding sulfides. The scales consisted primarily of Cr₂O₃, together with some NiAl₂O₄, MnCr₂O₄, NiCrMnO₄, and rutile-TiO₂. Sulfur from SO₂ gas made scales prone to spallation, and thicker. It also widened the internal corrosion zone when compared to air. The corrosion resistance of IN740 was mainly indebted to the formation of protective Cr₂O₃-rich oxides, and suppression of the sulfide formation.

• Transactions of the Korean hydrogen and new energy society
• /
• v.17 no.4
• /
• pp.418-424
• /
• 2006

In order to improve the activation properties of the $AB_2$ type hydrogen storage alloys for Ni-MH battery, the alloy surface was modified by employing high energy ball milling. The $Zr_{0.54}Ti_{0.45}V_{0.54}Ni_{0.87}Cr_{0.15}Co_{0.21}Mn_{0.24}$ alloy powder was ball milled for various period by using the high energy ball mill. As the ball milling time increased, activation of the $AB_2$ type composite powder electrodes were enhanced regardless of additives. When the ball milling time was small discharge capacities of the $AB_2$ type composite powder electrodes increased with the milling time. On the other hand for large milling time it decreased with increasing milling time. The maximum discharge capacity was obtained by ball milling for 3-4 min.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.3
• /
• pp.105-112
• /
• 2013

The microstructural changes of Fe-20Mn-12Cr-1Cu alloy have been studied during high temperature gas nitriding (HTGN) at the range of $1000^{\circ}C{\sim}1150^{\circ}C$ in an atmosphere of nitrogen gas. The mixed microstructure of austenite and ${\varepsilon}$-martensite of as-received alloy was changed to austenite single phase after HTGN treatment at the nitrogen-permeated surface layer, however the interior region that was not affected nitrogen permeation remained the structure of austenite and ${\varepsilon}$-martensite. With raising the HTGN treatment temperature, the concentration and permeation depth of nitrogen, which is known as the austenite stabilizing element, were increased. Accordingly, the depth of austenite single phase region was increased. The outmost surface of HTGN treated alloy at $1000^{\circ}C$ appeared Cr nitride. And this was in good agreement with the thermodynamically calculated phase diagram. The grain growth was delayed after HTGN treatment temperature ranges of $1000^{\circ}C{\sim}1100^{\circ}C$ due to the grain boundary precipitates. For the HTGN treatment temperature of $1150^{\circ}C$, the fine grain region was shown at the near surface due to the grain boundary precipitates, however, owing to the depletion of grain boundary precipitates, coarse grain was appeared at the depth far from the surface. This depletion may come from the strong affinity between nitrogen and substitutional element of Al and Ti leading the diffusion of these elements from interior to surface. Because of the nitrogen dissolution at the nitrogen-permeated surface layer by HTGN treatment, the surface hardness was increased above 150 Hv compared to the interior region that was consisted with the mixed microstructure of austenite and ${\varepsilon}$-martensite.

• Journal of the Korean Society for Heat Treatment
• /
• v.27 no.1
• /
• pp.1-9
• /
• 2014

For connector material applications, the influence alloying elements of Mn, Cr, Fe, and Ti and cold rolling reduction on the mechanical property, electrical conductivity and bendiability of Cu-Ni-Si-P alloy was investigated. The hot rolled plates were solution treated at $980^{\circ}C$ for 1.5 h, quenched into water, cold rolled by 10% and 30% reduction in thickness, and then aged at $440{\sim}500^{\circ}C$ for 3, 4, 5 times. respectively. Cu-Ni-Si-P-x alloys cold rolled by 10 reduction before heat treatment have a good bendability compare to cold rolled by 30 reduction. Cu-3.4Ni-0.8Si-0.03P-0.1Ti shows the peak strength value of 759 MPa, an electrical conductivity of 39%IACS, an elongation of 10% and a hardness of 256 Hv aged at $440^{\circ}C$ for 6 hrs. Thus it is suitable for lead frame and connector.