• Journal of Powder Materials
• /
• v.1 no.1
• /
• pp.15-20
• /
• 1994

The effect of SiC addition on sintering behaviors and microstructures of TiB2 ceramics were studied. The sintering of TiB2 was limited due to the surface diffusion and rapid grain growth at high temperature. However the addition of SiC to TiB2 ceramics improved the densification to above 99% of the theoretical density. The sintering of TiB2-SiC composite starts at 120$0^{\circ}C$ with the melting of the oxides in particle surface as impurities. After the reduction of the oxide by additional cabon at above 140$0^{\circ}C$, the grain boundary diffusion through the interface of TiB2-SiC play an important role. TEM observation showed neither chemical reactions nor other phases formed at the TiB2-SiC interfaces but the microcracks were observed due to the mismatch of thermal expansion between TiB2-SiC.

• Korean Journal of Materials Research
• /
• v.1 no.4
• /
• pp.191-197
• /
• 1991

The surface roughnesses of titanium silicide films and the diffusion behaviours of dopants in single crystal and polycrystalline silicon substrates durng titanium silicide formation by rapid thermal annealing(RTA) of sputter deposited Ti-filicide film from the composite $TiSi_{2.6}$ target were investigated by the secondary ion mass spectrometry(SIMS), a four-point probe, X-ray diffraction, and surface roughness measurements. The as-deposited films were amorphous but film prepared on single silicon substrate crystallized to the orthorhombic $TiSi_2$(C54 structure) upon rapid thermal annealing(RTA) at $800^{\circ}C$ for 20sec. There was no significant out-diffusion of dopants from both single crystal and polycrystalline silicon substrate into titanum silicide layers during annealing. Most of the implanted dopants piled up near the titanium silicide/silicon interface. The surface roughnesses of titanium silicide films were in the range between 16 and 22nm.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.3
• /
• pp.267-273
• /
• 2016

This study evaluated the mechanical properties and crack-healing abilities of zirconia composite ceramics. The six kinds of specimens used were: partially stabilized zirconia (Z) and five zirconia composite (ZS, ZST1, ZST2, ZST3, and ZST5) with SiC and $TiO_2$. There was not a large difference between the Vickers hardness of the six types of zirconia ceramics. The bending strength of the ZS specimen degraded rapidly, but the zirconia specimens with $TiO_2$ (ZST1, ZST2, ZST3, and ZST5) showed improved strength. Therefore, it was determined that the bending strength is affected by the crystallization, which is due to the addition of SiC and $TiO_2$. From the crack-healing conditions having the highest bending strength, monolithic zirconia retained its cracks, while the specimens of four types with SiC healed their cracks.

• Tribology and Lubricants
• /
• v.4 no.2
• /
• pp.44-51
• /
• 1988

Titanium carbide(TiC), Titanium nitride(TiN), and Titanium carbonnitride(Ti(C,N)) films were deposited on $Si_3N_4$-TiC composite cutting tools by chemical vapor deposition(CVD) using $TiCl_4-CH_4-H_2$, $TiCl_4-N_2-H_2$, and $TiCl_4-CH_4-N_2-H_2$ gas mixtures, respectively. The experimental results indicate that TiC coatings compared with TiN coatings on $Si_3N_4$ -TiC ceramic have an improved microstructural property, good thermal shock resistance, and good interfacial bonding. However TiN coatings compared with TiC coatings have a low friction coefficient with steel and good chemical stability. It is found by cutting test that coated insert compared with $Si_3N_4$-TiC ceramic have a superior flank and crater wear resistance. And multilayer coating compared with monolayer coating shows a improved wear resistance.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2006.11a
• /
• pp.166-168
• /
• 2006

$Si_3N_4/SiC$ composite ceramics was sintered in order to investigate their bending strength behavior after crack healing. $Y_2O_$ and $TiO_2$ power was added as sintering additives to enhance it's sintering property. A three-point bending specimen was cut out from sintered plates. About $100\;{\mu}m$ semi-circular surface cracks were made on the center of the tension surface of the three-point bending specimen using Vickers indenter. After the crack-healing processing from $500^{\circ}C$ to $1300^{\circ}C$, for 1 h, in air, the bending strength behavior of these crack-healed specimen coated with $SiO_2$ colloidal were determined systematically at room temperature. $Si_3N_4/SiC$ ceramics using additive powder ($Y_2O_3+TiO_2$) was superior to that of additive powder $Y_2O_3$. The additive powder $TiO_2$ exerted influence at growth of $Si_3N_4$. The optimum crack healing conditions coated $SiO_2$ colloidal were $1000^{\circ}C$ at $Si_3N_4/SiC$ using additive powder ($Y_2O_3+TiO_2$), and $1300^{\circ}C$ at $Si_3N_4/SiC$ using additive powder $Y_2O_3$.

• Journal of the Korean Ceramic Society
• /
• v.32 no.10
• /
• pp.1194-1202
• /
• 1995

The influences of TiC additions to the α-SiC on microstructural, mechanical, and electrical properties were investigated. Electrical discharge machinability of SiC-TiC composites was also studied. Samples were prepared by adding 30, 45, 60 wt.% TiC particles as a second phase to a SiC matrix. Sintering of SiC-TiC composites was done by hot pressing under a vacuum atmospehre from 1000 to 2000℃ with a pressure of 32 MPa and held for 90 minutes at 2000℃. Samples obtained by hot pressing were fully dense with the relative densities over 99% except 60wt.% TiC samples. Flexural strength and fracture toughness of the samples were increased with the TiC content. In case of SiC samples containing 45 wt.% TiC, the fracture toughness showed 90% increase compared to that of monolithic SiC sample. The crack propagation and crack deflection were observed with a SEM for etched samples after Vicker's indentation. The electrical resistivities of SiC-TiC composites were measured utilizing the four-point probe. The electrical dischage machining of composites was also conducted to evaluate the machinability.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.396-400
• /
• 2003

A new synthesis process for nano laminating Ti$_3$SiC$_2$ has been developed using TiCx (x=0.67) and Si powder as starting materials by a reaction hot pressing. Bulk Ti$_3$SiC$_2$ was fabricated using a green body consisting of TiCx and Si by a hot pressing under the pressures of 25 MPa at 1420-1550 $^{\circ}C$ for 90 min. The synthesized Ti$_3$SiC$_2$ was consisting of only TiCx and Ti$_3$SiC$_2$. The relative density of sintered bulk Ti$_3$SiC$_2$ was increased as the hot pressing temperature was increased, which was mainly due to the increase in TiCx contents in synthesized Ti$_3$SiC$_2$. The synthesized Ti$_3$SiC$_2$ bulk was consisted of nano sized lamella structure of 20-100 nm in thickness. It was found that TiCx particles in Ti$_3$SiC$_2$ would increase the 3-point bending strength of synthesized Ti$_3$SiC$_2$ bulk. The maximum 3-P. bending strength of synthesized Ti$_3$SiC$_2$ bulk was more than 800 MPa. The Vickers hardness of synthesized Ti$_3$SiC$_2$bulk was as low as 5 Gpa, which was decreased with the indentation load. The quasi-plastic deformation behaviors were observed around indentation mark on Ti$_3$SiC$_2$.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.2
• /
• pp.73-78
• /
• 2009

Quinary Ti-Al-Si-C-N films were successfully synthesized on SUS 304 substrates and Si wafers by a hybrid coating system combining an arc ion plating technique and a DC reactive magnetron sputtering technique. In this work, the effect of Si content on the microstructure and mechanical properties of Ti-Al-C-N films were systematically investigated. It was revealed that the microstructure of Ti-Al-Si-C-N coatings changed from a columnar to a nano-composite by the Si addition. Due to the nanocomposite microstructure of Ti-Al-Si-C-N coatings, the microhardness of The Ti-Al-Si-C-N coatings significantly increased up to 56 GPa. In addition the average friction coefficients of Ti-Al-Si-C-N coatings were remarkably decreased with Si addition. Therefore, Ti-Al-Si-C-N coatings can be applicable as next-generation hard-coating materials due to their improved hybrid mechanical properties.

• Tribology and Lubricants
• /
• v.4 no.2
• /
• pp.36-43
• /
• 1988

Titanium carbide(TiC) and titanium nitride(TiN) flims were deposited on $Si_3N_4$-TiC composite cutting tools by chemical vapor deposition(CVD) using $TiCl_4-CH_4-H_2$ and $TiCl_4-H_2-N_2$ gas mixtures, respectively. The nonmetal to metal ratio of deposit increases with increasing $m_{C/Ti}$(mole ratio of CH$_4$ to TiCl$_4$ in the input) for TiC coatings and $m_{N/Ti}$(mole ratio of N$_2$ to TiCl$_4$ in the input) for TiN coatings. The nearly stoiahiometric films could be obtained under the deposition condition of $m_{C/Ti}$ between 1.15 and 1.61 for TiC, and that of $m_{N/Ti}$ between 25 and 28 for TiN. Also maximum microhardness of the coatings can be obtained in these ranges. The interfacial region of TiC coatings on $Si_3N_4$-TiC ceramics is wider than that of TiN coatings according to Auger depth profile analysis, which indicates good interfacial bonding for TiC. Experimental results show that TiC coatings have an randomly equiaxed structure and Columnar structure with(220) preferred orientation can be obtained for TiN coatings. And, multilayer coatings have a dense and equiaxed structure.

• Journal of Korea Foundry Society
• /
• v.20 no.4
• /
• pp.254-259
• /
• 2000

Metal matrix composites(MMCs) reinforced with hard particles have many potential application in aerospace structures, auto parts, semiconductor package, heat resistant panels, wear resistant materials and so on. In this work, the effect of SiC partioel sizes(50 and 100 ${\mu}m$) and additional elements such as Si, Cu and Ti on the microstructure and the wear property of $Al-5Mg-X(Si,Cu,Ti)/SiC_p$ composites produced by pressureless infiltration method have been investigated using optical microscopy, scanning eletron microcopy(SEM) with EDS(energy dispersive spectrometry), hardness test, X-ray diffractometer(XRD) and wear test. In present study, the sound $Al-5Mg-X(Si,Cu,Ti)/SiC_p$(50 and 100 ${\mu}m$) composites were fabricated by pressureless infiltration method. The $Al-5Mg-0.3Si-O.1Cu-O.1Ti/SiC_p$ composite with $50 {\mu}m$ size of SiC particle has higher hardness and better wear property than any other composite with $100{\mu}m$ size of SiC particle produced by pressureless infiltration method. The hardness and wear property of $Al-5Mg/SiC_p$(50 and 100 ${\mu}m$) composites were enhanced by the addition of Si, Cu and Ti in Al-5%Mg matrix alloy.