• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1205-1206
• /
• 2006

Dispersion-strengthened copper with $TiB_2$ was produced by ball-milling and spark plasma sintering (SPS).Ball-milling was performed at a rotation speed of 300rpm for 30 and 60min in Ar atmosphere by using a planetary ball mill (AGO-2). Spark-plasma sintering was carried out at $650^{\circ}C$ for 5min under vacuum after mechanical alloying. The hardness of the specimens sintered using powder ball milled for 60min at 300rpm increased from 16.0 to 61.8 HRB than that of specimen using powder mixed with a turbular mixer, while the electrical conductivity varied from 93.40% to 83.34%IACS. In the case of milled powder, hardness increased as milling time increased, while the electrical conductivity decreased. On the other hand, hardness decreased with increasing sintering temperature, but the electrical conductiviey increased slightly

• The Journal of the Korean dental association
• /
• v.57 no.11
• /
• pp.672-678
• /
• 2019

AIM: The purpose of this study was to evaluate and compare the torsional fracture resistances, cyclic fatigue resistance, and bending stiffness of two nickel-titanium (NiTi) rotary instruments made of different heat-treated alloy: Aurum Blue (heat-treated) and Aurum Pro (conventional). Methods: Forty-five Aurum Blue and Aurum Pro NiTi files were selected for the three mechanical tests (n=15). For the torsional resistance test, 3 mm file tip was fixed and the shaft was driven clockwise at 2 rpm until fracture occurred by using a customized device. Cyclic fatigue resistance was evaluated by rotating instruments in artificial canal with dynamic mode. Bending stiffness was tested by observation of the bending moment on attaining a 45° bend. The results were analyzed by student-t tests at a significance level of 95%. The fractured surface of each groups were examined under a scanning electron microscope (SEM). Results: Aurum Blue showed significantly higher toughness, ultimate strength, distortion angle, and number of cycles to failure than those of Aurum Pro (p < 0.05). However, Aurum Blue and Aurum Pro did not differ significantly in terms of bending stiffness. SEM showed typical topographic appearances of the cyclic fatigue and torsional fracture. Conclusions: Under the limitations of this study, heat-treated instruments showed higher flexibility and fracture resistances than conventional NiTi instruments.

• Korean Journal of Metals and Materials
• /
• v.48 no.6
• /
• pp.575-580
• /
• 2010

Effects of the surface modification on the deposition behaviors of apatite crystals in Zr-1Nb plates were studied. Zr-1Nb alloy plates were polished with abrasive papers to have different roughness and some of them were treated in NaOH or coated with collagen before deposition of apatites in the simulated body fluid (SBF). The weight gain due to the deposition of apatite crystals increased as the surface roughness increased in Zr-1Nb. The size of granular apatite crystals were found to be smaller in Zr-1Nb roughened by $162{\mu}m$ abrasive paper than in Zr-1Nb roughened by $8.4{\mu}m$ paper, suggesting the nucleation rate increased with increase of surface roughness. After, 10 days immersion in a SBF, NaOH-treated Zr-1Nb was completely coated with apatite with the deposited apatite weight comparable to that in Ti-6Al-4V. The deposition rate of Zr-1Nb was not appreciably influenced by NaOH treatment unlike the significant influence of NaOHtreatment on the deposition rate of apatite in Ti-6Al-4V. One significant observation in this study is an appreciable increase of the apatite deposition rate after collagen coating both on Zr-1Nb and Ti-6Al-4V plate, which may be caused by the interaction between collagen and $Ca^{+2}$ ions.

• Korean Journal of Metals and Materials
• /
• v.47 no.1
• /
• pp.13-20
• /
• 2009

This work presents functionally graded coatings (FGC) of hydroxyapatite (HA) and metallic powders on Ti-6Al-4V implants using plasma spray coating method. HA has been the most frequently used coating material due to its excellent compatibility with human bones. However, because of the abrupt changes in thermomechanical properties between HA and the metallic implant across an interface, and residual stress induced on cooling from coating temperture to room temperature, debonding at the interface occurs in use sometimes. In this work, FGC of HA and Ti or Ti-alloy powders is made to mitigate the abrupt property changes at the interface and the effect of FGC on residual stress release is investigated by evaluating the mechanical bond strength between the implant and the HA coating layers. Thermal annealing is done after coating in order to crystallize the HA coating layer which tends to have amorphous structure during thermal spray coating. The effects of types and compositional ratio of metallic powders in FGC and annealing conditions on the bond strength are also evaluated by strength tests and the microstructure analysis of coating layers and interfaces. Finally, biocompatibility of the coating layers are tested under ISO 10993-5.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.25 no.3
• /
• pp.293-306
• /
• 2009

In this study, the biological response of fetal rat calvarial cells on alkali- and heat-treated titanium was assessed. The results were as follows; Cell proliferation on alkali- and heat-treated surfaces showed significantly higher level than on the titanium-6aluminum-4vanadium (weight percentage: 6 % aluminum, 4 % vanadium, Ti-6Al-4V) surface (p<0.01). In ELISA analysis, concentration of $IL-1{\beta}$ and IL-6 were raised when the cells were grown to day 7. Pre-treatment with herbimycin, a known tyrosine kinase inhibitor, suppressed the production of IL-6 (p<0.01). In comparison to commercially pure titanium (grade II, cp-Ti) and Ti-6Al-4V alloy, alkali- and heat-treated titanium enhanced alkaline phosphatase activity (p<0.001). In RT-PCR analysis, alkaline phosphatase, bone sialoprotein, receptor activated nuclear factor ligand mRNA expression was increased alkali- and heat-treated titanium. Herbimycin and SB203580, p38 MAPK inhibitor, were repressed of $IL-1{\beta}-induced$ IL-6 mRNA expression. These results suggest that alkali- and heat-treated titanium stimulate osteoblasts differentiation and facilitate bone remodeling.

• Korean Journal of Materials Research
• /
• v.11 no.6
• /
• pp.502-507
• /
• 2001

The effect of solidification rate on the microstructure of directionally solidified IN792+ Hf superalloy has been studied. Solidification sequence and precipitation behavior of the alloy have been analysed by microstructural observation. The script carbide transformed to faceted carbide with decreasing solidification rates. The incorporation of ${\gamma}$ phase into the faceted carbide was due to dendritic growth of carbides. Some elongated carbide bars formed along the grain boundaries at a solidification rate of 0.5$\mu\textrm{m}$/s. Two zones, ${\gamma}$' forming elements enriched zone and depleted zone, were found in the residual liquid area. Eutectic ${\gamma}$/${\gamma}$' nucleated in the f forming elements enriched zone. Formation of eutectic ${\gamma}$/${\gamma}$' increased the ratio of (Ti+Hf+Ta+W)/Al and induced η phase precipitation. The ratio of (Ti+Hf+Ta+W)/Al decreased at lower solidification rates due to sufficient back diffusion in the residual liquid area. Hence, the Precipitation of the η Phase efficiently suppressed at the lower solidification rate.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.2
• /
• pp.169-181
• /
• 2007

Statement of problem: Titanium is well known as a proper metal for the dental restorations, because it has an excellent biocompatibility, resistance to corrosion, and mechanical property. However, adhesion between titanium and dental porcelains is related to the diffusion of oxygen to the reaction layers formed on cast-titanium surfaces during porcelain firing and those oxidized layers make the adhesion difficult to be formed. Many studies using mechanical, chemical and physical methods to enhance the titanium-ceramic adhesion have been actively performed. Purpose: This study meant to comparatively analyse the adhesion characteristics depending on different titanium surface coatings after coating the casts and wrought titanium surfaces with Au and TiN. Material and method: In this study, the titanium specimens (CP-Ti, Grade 2, Kobe still Co. Japan) were categorized into cast and wrought titanium. The wrought titanium was cast by using the MgO-based investment(Selevest CB, Selec). The cast and wrought titanium were treated with Au coating($ParaOne^{(R)}$., Gold Ion Sputter, Model PS-1200) and TiN coating(ATEC system, Korea) and the ultra low fusing dental porcelain was fused and fired onto the samples. Biaxial flection test was done on the fired samples and the porcelain was separated. The adhesion characteristics of porcelain and titanium after firing and the specimen surfaces before and after the porcelain fracture test were observed with SEM. The atomic percent of Si on all sample surfaces was comparatively analysed by EDS. In addition, the constituents of specimen surface layers after the porcelain fracture and the formed compound were evaluated by X-ray diffraction diagnosis. Result: The results of this study were obtained as follows : 1. The surface characteristics of cast and wrought titanium after surface treatment(Au, TiN, $Al_2O_3$ sandblasting) were similar and each cast and wrought titanium showed similar bonding characteristics. 2. Before and after the biaxial flection test, the highest atomic weight change of Si component was found in $Al_2O_3$ sandblasted wrought titanium(28.6at.% $\rightarrow$ 8.3at.%). On the other hand, the least change was seen in Au-Pd-In alloy(24.5at.% $\rightarrow$ 9.1at.%). 3. Much amount of Si components was uniformly distributed in Au and TiN coated titanium, but less amount of Si's was unevenly dispersed on Al2O3 sandblasting surfaces. 4. In X-ray diffraction diagnosis after porcelain debonding, we could see $Au_2Ti$ compound and TiN coating layers on Au and TiN coated surfaces and $TiO_2$, typical oxide of titanium, on all titanium surfaces. 5. Debonding of porcelain on cast and wrought titanium surface after the biaxial flection is considered as a result of adhesion deterioration between coating layers and titanium surfaces. We found that there are both adhesive failure and cohesive failure at the same time. Conclusion: These results showed that the titanium-ceramic adhesion could be improved by coating cast and wrought titanium surfaces with Au and TiN when making porcelain fused to metal crowns. In order to use porcelain fused to titanium clinically, it is considered that coating technique to enhance the bonding strength between coating kKlayers and titanium surfaces should be developed first.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.273-276
• /
• 2008

In this study, microstructure and distribution of alloy elements were investigated in thermo-mechanically processed C-Mn-Si transformation induced plasticity (TRIP) steels. The microstructures of TRIP steels were investigated by using advanced analysis techniques, such as three dimensional atom probe tomography (3D-APT). At first, the microstructure was observed by using TEM. TEM results revealed that microstructure of C-Mn-Si TRIP steel was composed of ferrite, bainte, and retained austenite. 3D-APT was used to characterize atomic-scale partitioning of added elements at the phase interface. In the retained austenite phase, Ti and B were enriched with C. However, there was no fluctuation of Mn and Si concentration across the interface. Through these analysis techniques, the advanced characteristics of constituent microstructure in C-Mn-Si TRIP steels were identified.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.217-217
• /
• 2012

플라즈마 전해산화(Plasma Electrolytic Oxidation)는 수용액 중에서 Al, Mg, Ti 등의 금속표면에 산화막을 형성시키는 기술로서, 기존의 양극산화법과 유사한 장치에서 고전압을 가해 미세플라즈마 방전을 유도하여 치밀한 산화막을 형성하는 표면처리 기술이다. 본 연구에서는 6061 알루미늄 합금의 대면적 시편을 이용하여 PEO공정으로 산화막을 형성시켰다. 산화막의 조성 및 미세구조는 XRD와 SEM, EDS를 이용하여 분석하였다. 형성된 산화막은 회색에서 밝은 회색으로 시편 전면에 고르게 나타났다. 피막 성장인자를 정교하게 조절함으로써 강한 피막 접착력과 낮은 표면조도를 가지는 매끈한 표면을 얻을 수 있었고, 그에 따른 물성 변화를 분석하였다. 또한 시편의 크기에 관계없이 동일한 조건에서 동일한 물성이 나오는 것으로 분석되었다. 이를 통해 균질한 대면적 피막의 높은 신뢰성을 요구하는 다양한 산업분야에 적합한 표면처리 방법으로서 PEO공정이 활용될 수 있음을 확인하였다.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.05a
• /
• pp.207-210
• /
• 2002

Metal matrix composites(MMCs) are increasingly attractive for high technology components such as aerospace applications and transportations due to their high strength, stiffness, and toughness. Many processes for fabricating MMCs have been developed, and relatively simple Foil-Fiber-Foil method is usually employed in solid state consolidation processes. During the consolidation processes at high temperature, densification occurs by the inelastic flow of the matrix materials, and the process is coupled with the conditions of pressure, temperature and volume fraction of fiber and matrix materials. This is particularly important in titanium matrix composites, and thus a generic model based on micro-mechanical approaches enabling the evolution of density over time to be predicted has been developed. The mode developed is then implemented into FEM so that practical process simulation has been carried out. Further the experimental investigation of the consolidation behavior of SiC/Ti-6Al-4V composites using vacuum hot pressing has been performed, and the results obtained are compared with the model predictions.