• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.403-404
• /
• 2012

We fabricated TFT devices with the GeSe channel. A single device consists of a Pt source and drain, a Ti glue layer and a GeSe chalcogenide channel layer on SiO2/Si substrate which worked as the gate. We confirmed the drain current with variations of gate bias and channel size. The I-V curves of the switching device are shown in Fig. 1. The channel of the device always contains amorphous state, but can be programmed into two states with different threshold voltages (Vth). In each state, the device shows a normal Ovonic switching behavior. Below Vth (OFF state), the current is low, but once the biasing voltage is greater than Vth (ON state), the current increases dramatically and the ON-OFF ratio is high. Based on the experiments, we draw the conclusion that the gate voltage can enhance the drain current, and the electric field by the drain voltage affects the amorphous-amorphous transition. The switching device always contains the amorphous state and never exhibits the Ohmic behavior of the crystalline state.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.280-281
• /
• 2011

We fabricated the devices of TFT type with the amorphous chalcogenide channel. A single device consists of a Pt source and drain, a Ti glue layer and a GeSe chalcogenide channel layer on SiO2/Si substrate which worked as the gate. We confirmed the drain current with variations of gate bias and channel size. The I-V curves of the switching device are shown in Fig. 1. The channel of the device always contains amorphous state, but can be programmed into two states with different threshold voltages (Vth). In each state, the device shows a normal Ovonic switching behavior. Below Vth (OFF state), the current is low, but once the biasing voltage is greater than Vth (ON state), the current increases dramatically and the ON-OFF ratio is about 4 order. Based on the experiments, we contained the conclusion that the gate voltage can enhance the drain current, and the electric field by the drain voltage affects the amorphous-amorphous transition. The switching device always contains the amorphous state and never exhibits the Ohmic behavior of the crystalline state.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.68-68
• /
• 2018

Nanoporous or nanotubular metal oxide can be fabricated by anodization of metal substrate in fluoride contained electrolytes. The approach allows various transition metals such as Zr, Hf, Nb, Ta to form highly ordered oxide nanostructures. These oxide nanostructures have various advantages such as high surface area, fast electron transport rate and slow recombination in semiconductive materials. Recently, vanadium oxide nanostructures have been drawn attentions due to their superior electronic, catalytic and ion insertion properties. However, anodization of vanadium metal to form oxide layers is relatively difficult due to ease formation of highly soluble complex in water contained electrolyte during anodization. Yang et al. reported $[TiF_6]^{2-}$ or $[BF_4]^-$ in electrolyte helps to formation of stable oxide layer [1, 2]. However, the reported approaches are very sensitive in other parameters. In this presentation, we deal with the other important key parameters to form ordered anodic vanadium oxide such as pH, temperatures and applied potential.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.221-221
• /
• 2014

The current energy crisis in many countries has led to the search of an efficient renewable energy source. Among those the solar energy is the most abundant and easily available. However harvesting the solar energy requires a much efficient device. Lot of research has been done in this regard and so far the efficiency of traditional solar cell stands around ~50% and for PET films it is much lesser. The potential application of PET films in the solar cells can be very promising provided the fact that the PET film is lighter and logistically more viable. There is a lot of work that is being done to increase the efficiency of PET based solar cells. The base electrode plays a vital role in increasing the efficiency of the cell.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.281-286
• /
• 2004

The oxide scales formed on Ni-18W(at.%) coating that was electrodeposited on steel were investigated using XRD, SEM and TEM. The oxide scales consisted mainly of an outer NiO layer, and an inner thick ($NiWO_4$+NiO) mixed layer. The unoxidized coating below the oxide scale was rich in Ni and depleted in W, owing to the consumption of Wand the resultant Ni enrichment. The oxidation resistance of Ni-18W coating was poorer than that of the TiN coating, due to the formation of nonprotective NiWO$_4$. During oxidation, Ni and the substrate element of Fe diffused outward, while oxygen inward, according to the concentration gradients.

• Journal of Magnetics
• /
• v.16 no.2
• /
• pp.186-191
• /
• 2011

[ $YBa_2C_3O_{7-x}$ ]films were fabricated on a $SrTiO_3$ (100) substrate using a trimethylaceate propionic acid (TMAP)-based MOD process by controlling the precursor solution viscosity, firing temperature, and by using various coatings. The viscosity of the precursor solution was controlled by the addition of Xylenes. The films were heat treated with different temperatures from 750 to $800^{\circ}C$. c-axis oriented films were obtained. After adding 9 ml of Xylene into the precursor solution, the $T_c$ of the YBCO film, which was coated 2 times and heat treated at $800^{\circ}C$, was 86 K and the measured $J_c$ was above 2.5 MA/$cm^2$ at 77 K in a zero-field.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.11C no.2
• /
• pp.18-22
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Sio$_2$/Si substrate at 4,000 [rpm] for 10 seconds. The structural characteristics of the surface were analyzed by fractal dimension. The thickness of BST ceramics thin films was about 260∼280 [nm]. The property of the leakage current was stable with 10-9∼10-11[A] when the applied voltage was 0∼3[V]. BST thin films ha low leakage current properties when fractal dimension was low and a coating area was high.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.28 no.1
• /
• pp.145-152
• /
• 1999

To explore the possibility of using freeze dried loach for instant choo o tang(Korean traditional loach soup), protein qualities and fatty acid composition were evaluated on boiled and steamed loach. Total lipid and ash content were lowered in both heated(boiled and steamed) loaches due to deboning and eviscerating during cooked meat preparation. Profiles of total amino acids were not changed seriously by the type of cooking, but the amount of essential amino acids were comparable in all samples. Two times more free amino acids were quantified in cooked samples compared to raw meat. Available lysine was marginally decreased by cooking, and that caused some measurable change in typsin indigestible substrate(TI) in streamed whole loach. In vitro protein digestibility of the heated loaches was not altered drastically and the protein quality determined as computed protein efficiency ratio(C PER) was similar for the raw, boiled and steamed loach. The ratios of unsaturated to saturated fatty acids changed measurably in heated whole loach. The results shows that heating caused apparent oxidative deterioration of the polyunsaturated fatty acids.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.3
• /
• pp.70-81
• /
• 1998

Fiber-Fabry-Perot (FFP) tunable filters, the essential component of WDM transmission, were designed, fabricated and characterized. Multi-layered thin film mirrors that consists of an optical collimater's corss section as a substrate and TiO$_{2}$SiO$_{2}$ alternating multi-layered films as a filter wer designed by means of the transfer matrix method. Fabricated mirrors showed the high reflectivity over around 98% as expected. After fabricating the tuneable filters using PZT, we measured FSR, FWHM, finesse , crosstalk and insertion loss, confirming that the built devices satisfied the optical filter's specifications required in the SEDM transmission systems.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.719-720
• /
• 2009

We suggest a new approach to lower the operating voltage of plasma display devices using a piezoelectric transformer (PT). $Pb(Mg_{1/3}Nb_{2/3})O_3-PbTiO_3$ (PMNT) was used as a piezoelectric material. The Rosen-type PT, with a compact size of 10 mm ${\times}$ 20 mm ${\times}$ 0.3 mm, was fabricated on a glass substrate. The fabricated PT was operated as a half-wave vibration mode at around 80~90 kHz. The maximum voltage step-up ratio was 3 at 87.8 kHz when the input voltage was 10.32 V (peak-to-peak).