• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.5
• /
• pp.791-799
• /
• 1997

The wear characteristics and wear mechanisms of plasma sprayed Al/sub 2/ O/sub 3/-40%TiO/sub 2/ and Cr/sub 2/O/sub 3/ deposited on casting aluminum alloy(AC4C) were investigated. Specimens were processed for various coating thicknesses. Ball on disk type wear tester was used for wear test. The scratch test on plasma sprayed coating surface showed that critical load to break the coating layer was greater than 40 N. The critical load increase with the increase of coating thickness of specimens. The friction coefficient of Cr/sub 2/O/sub 3/ coating layer was less than that of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer. The wear resistance of Cr/sub 2/O/sub 3/ coating layer was greater than that of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer. Microscopic observation of worn surfaces was made by SEM. SEM observation showed that the main mechanism of wear for Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer was abrasive wear under 50 N. For the case of Al/sub 2/O/sub 3/-40%TiO/sub 2/ coating layer, as the surface cracks perpendicular to sliding direction propagated, the wear debris was generated in wear track. However, the main mechanism of wear for Cr/sub 2/O/sub 3/ coating layer was brittle fracture under 150 N.

• Korean Journal of Materials Research
• /
• v.10 no.4
• /
• pp.264-269
• /
• 2000

TiO$_2$thin films were prepared on the glass by a conventional spin coating method with $TiO_2$ sol(30wt%, anatase). The thickness of the thin films were controlled by the number of coating cycles: one cycle is composed of spin coating, drying, and heating process. The reaction rate of the film was obtained by the photodecomposition of gaseous benzene under 0.44 and 2.0mW/$\textrm{cm}^2$ UV light on the film surface. For an incident UV light intensity of 0.44mW/$\textrm{cm}^2$, the reaction rate was increased with the thickness of the film, caused by extent of surface area, but there was no change over the thickness of about 4$\mu\textrm{m}$. The porous $TiO_2$ thin film has comparatively vast effective surface area, which under relatively high-intensity UV illumination causes the reaction rate to be controlled by the film thickness.

• Journal of Welding and Joining
• /
• v.25 no.4
• /
• pp.42-48
• /
• 2007

An inert gas atomized NiTiZrSiSn bulk metallic glass feedstock was sprayed onto the copper plate using vacuum plasma spraying process. In order to change the in-flight particle energy, that is, thermal energy, the hydrogen gas flow rate in plasma gas mixture was increased at the constant flow rate of argon gas. Coating and single pass spraying bead were produced with the least feeding rate. Regardless of the plasma gas composition, fully melted through unmelted particle could be observed on the overlay coating. However, the frequency of the unmelted particle number density was increased with the decrease of the hydrogen gas flow rate. The amorphous phase fraction within coating was also affected by the number density of the unmelted particle.

• Korean Journal of Materials Research
• /
• v.14 no.8
• /
• pp.558-564
• /
• 2004

In order to improve the low hardness and low wear resistance of Ti-6Al-4V alloy, plasma carburization treatment and CrN film coating were carried out. Effects of the plasma carburization and CrN coating were analyzed and compared with the non-treated alloy by mechanical and creep tests. After plasma carburization and CrN coating treatments, the carburized layer was about 150 ${\mu}m$ in depth and CrN coated layer was about 7.5 ${\mu}m$ in thickness. Hardness value of about $H_{v}$ 402 of the non-treated alloy was improved to $H_{v}$ 1600 and 1390 by plasma carburization and CrN thin film coating, respectively. Stress exponent(n) was decreased from 9.10 in CrN coating specimen to 8.95 in carburized specimen. However, the activation energy(Q) was increased from 242 to 250 kJ/mol. It can be concluded that the static creep deformation for Ti-6Al-4V alloy is controlled by the dislocation climb over the ranges of the experimental conditions.

• Journal of the Korean Ceramic Society
• /
• v.40 no.2
• /
• pp.123-127
• /
• 2003

The effects of process parameters on coating formation and coating properties were investigated using a fused and crushed Ti $O_2$powder by the Taguchi method and L$_{9}$(3$^4$) orthogonal array. The Taguchi analysis was conducted through the results of the coating properties affected strongly by plasma spraying parameters and Ti $O_2$powder was sprayed on Ti-6Al-4V alloy substrate. The coating properties were characterized by thickness, microhardness, porosity and surface roughness using optical microscopy, image analyzer and surface roughness tester respectively. An observed optimum condition of plasma spraying process could be found for potential use as a bioceramic coating.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.3 no.2
• /
• pp.115-119
• /
• 2002

This study was performed to improve mechanical properties of rotor and bushing materials. SACD and SKD11 steels as rotor and bushing materials were investigated. Gas nitriding and TiN coating were carried out on SACM and SKD11 steels. TiN coating was deposited on SKD11 steel by reactive sputtering process. This coated layer was picked off during the operation because of insufficient adhesion. Gas nitriding was carried out on SACM and SKD11 steels in an ammonia atmosphere at 51$0^{\circ}C$ for 72 hrs. These gas nitrided parts showed good mechanical properties. SKD11 steels were heat-treated to obtain optimum carbide size and distribution. As a results, the hardness increased.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2000.04a
• /
• pp.164-169
• /
• 2000

The remote measurement system(RMS) as a new experimental method is limited in its application to crack measurements at elevated temperatures because of the oxide layer on the specimen surface. Since TiAlN and Cr coating layers have a high resistance to oxidation and wear, this paper proposed a TiAlN and Cr coating technique for specimens to facilitate the measurement of crack growth behavior using RMS. To investigate the effects of the coating layer, tension and fatigue tests were carried out at room temperature and at 538$^{\circ}C$, using specimens of 1Cr-1Mo-0.25V steel. From the experimental results, it was found that the mechanical properties of the TiAlN and Cr coated specimens were similar to those of the substrate. Accordingly, the TiAlN and Cr coated layer had hardly any influence on the fatigue crack propagation.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2000.05a
• /
• pp.783-791
• /
• 2000

Increasing demands in productivity are propelling the development of new manufacturing methods like hard machining, high speed cutting (HSC) or machining of difficult to machine materials. In these processes the toois are subjected to very severe mechanical, tribological and thermal loads. They fail prematurely by abrasion, cratering, edge breakage and cold welding. The performance of such tools will be enhanced by better and more wear resistant coatings. The development of these new coatings shows a clear trend towards complex multi-component and multi-layer configurations. TiAIN multilayer coating belongs to these coatings for the new cutting tool generation. This paper tries to explain the benefits of the new coatings. TiAIN multilayer coating offers the following advantages: reduction of manufacturing costs. boost productivity, and lower coolant procurement, conditioning and disposal costs.

• Journal of Ocean Engineering and Technology
• /
• v.16 no.2
• /
• pp.60-66
• /
• 2002

The remote measurement system(RMS) as a new experimental method is limited in its application to crack measurement at elevated temperatures because of the oxide layer on the specimen surface. Since TiAIN and Cr coating layers have a high resistance to oxidation and wear, this paper proposed a TiAIN and Cr coating technique for specimens to facilitate the measurement of crack growth behavior using RMS. To investigate the effects of the coating layer, tension and fatigue tests were carried out at room temperature and at $538^{\circ}C$. The test material was 1Cr-1Mo-0.25V steel which is widely used as a turbine rotor material. From the experimental results, it was found that the mechanical properties of the TiAIN and Cr coated specimens were similar to those of the substrate. Accordingly, the TiAIN and Cr coated layer had hardly any influence on the fatigue crack propagation.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.4
• /
• pp.337-341
• /
• 2001

TiN coating of high speed end mill is recently generalized. The study of coating layer using ion plating is mainly about the coating method and the why of the longer life of coated tools. In CNC machning process, metal cutting isn't carry out until the tools including the end-mill and so on are fractured. Namely, it is difficult precision processing when the cutting force of the cutting tool is near the limit the fracture cutting force. So, the estimate of the life by wear and fracture is important. Therefore, this study is about the method to estimate the capacity of the coating layer in relation to the tendency of cutting force and the influence of the cutting capacity of coated end-mill by the condition N2, Ar, temperature. The cutting length is in inverse proportion to the cutting force ratio. So, the life of the TiN coated end mill can be predicated by the ratio of the increase of the cutting force.