• 한국세라믹학회지
• /
• 제31권8호
• /
• pp.841-848
• /
• 1994

The sintering behavior of La-modified PbTiO3 ceramics was investigated in order to improve the poor sinterability of PbTiO3. Addition of La improved the sinterability. It was confirmed that this improvement was due to the decrease in tetragonality ratio c/a of crystal lattice. The variations of dielectric constant and pyroelectric coefficient were measured with temperature. It was observed that with the increase of La content, Curie temperature decreased and dielectric constant at room temperature increased. La-modified PbTiO3 ceramics had smaller pyroelectric figure of merits than those of pyroelectric materials in use. The effects of grain size on dielectric and pyroelectric properties were also investigated. The change of grain size had effect on maximum dielectric constant and pyroelectric coefficient, but is had little effect on pyroelectric figure of merit at room temperature. The closer examination near ferro-paraelectric phase transition temperature revealed that the behavior of phase transition approached a more relaxor character with the increase of La content and the decrease of grain size.

• 한국분말재료학회지
• /
• 제4권3호
• /
• pp.196-204
• /
• 1997

Joining of AIN ceramics to W and Cu by active-metal brazing method was tried with use of (Ag-Cu)-Ti alloy as insert-metal. Joints were produced under various conditions of temperature, holding time and Ti-content in (Ag-Cu) alloy Reaction and microstructural development in bonded interface were investigated through observation and analysis by SEM/EDS, EPMA and XRD. Joint strengths were measured by shear test. Bonded interface consists of two layers: an insert-metal layer of eutectic Ag- and Cu-rich phases and a reaction layer of TiN. Thickness of reaction layer increases with bonding temperature, holding time and Ti-content of insert-metal. It was confirmed that the growth of reaction layer is a diffusion-controlled process. Activation energy for this process was 260 KJ/mol which is lower than that for N diffusion in TiN. Maximum shear strength of 108 MPa and 72 MPa were obtained for AIN/W and AIN/Cu joints, respectively. Relationship between processing variables, joint strength and thickness of reaction layer was also explained.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.106-106
• /
• 2015

In this study, we investigated electrochemically formed nanotube shape on ternary Ti-25Ta-xHf alloys with Hf contents. Ti-25Ta-xHf (x=0~15 wt.%) alloys were manufactured by vacuum arc-melting furnace. The obtained ingots were homogenized in an argon atmosphere at $1050^{\circ}C$ for 2h and then water quenching. The specimens were cut from ingots to 4 mm thickness and first ground and polished using SiC paper (grades from #100 to #2000). The anodization treatments on Ti-25Nb-xHf alloys were carried out at room temperature for experiments. The formation of nanotubular film was conducted by electrochemical method in mixed electrolytes with 1 M $H_3PO_4$ + 0.8 wt. % NaF at 30 V for 2 h. The morphologies of nanotube depended on the Hf content in Ti-25Ta-xHf ternary system.

• 한국유기농업학회지
• /
• 제20권3호
• /
• pp.385-397
• /
• 2012

식물미네랄(phyto-minerals) 함량을 높인 미네랄강화 농작물(biofortification foods)을 개발하기 위하여 전기분해를 이용하여 10종(Co, Fe, Mg, Mn, Sr, Zn, Li, Sn, V, Ti, Se, S)의 미량요소를 함유하는 복합미네랄액을 조제하였다. 양액과 SCB 액비에 복합미량요소액을 방울토마토 처리한 결과 양액+복합미량요소액 처리구는 Li, Zn, Sr, Se, Ti이 증가되었고, SCB+복합미량요소액 처리구는 Li, Zn, Se, Co, Sr, Ti 함량이 유의성있게 증가하였다. 양액+SCB+복합미량요소액 처리구는 SCB액비, NS액비 처리구보다 Li, Zn, Se, Co, Ti 함량이 유의성 있게 증가하였다. 토마토의 생육과 수량은 양액처리구에서 가장 높았고, 복합 미량요소액 처리로 감소하였다. 토마토의 수량은 표준양액처리구와 비교할때 NS+복합미량요소액 처리구와 SCB+양액+복합 미량요소액 혼합시용구는 각각 97%와 94%의 토마토 과실 수량를 나타내었으나 미량요소 강화효과가 있었으므로 혼합용액을 조제하면 토마토 재배용 양액으로 활용이 가능할 것으로 보인다.

• Korean Chemical Engineering Research
• /
• 제51권3호
• /
• pp.313-318
• /
• 2013

$V_2O_5-WO_3/TiO_2$ 촉매의 질소산화물 환원반응에 있어서 $V_2O_5$ 함량이 NO 환원 및 $N_2O$ 생성에 미치는 영향을 조사하기 위하여 분말촉매를 사용한 미분반응기에서 실험 연구를 수행하였다. 고정된 비율의 $WO_3$와 $TiO_2$에 $V_2O_5$ 함량을 1에서 8 wt%까지 변화시킨 촉매에서 NO 환원반응과 암모니아 산화반응 특성이 조사되었다. $V_2O_5-WO_3/TiO_2$ 촉매에서 NO 환원 반응은 $200^{\circ}C$ 이하에서도 상당량 진행되지만, $V_2O_5$ 함량을 1 wt% 촉매의 경우 700 ppm의 NO를 99.9%이상 전환시키는 최저 반응온도가 $340^{\circ}C$에서 아주 좁은 활성 온도창으로 일어났다. 그리고 이 활성온도는 촉매의 $V_2O_5$ 함량이 증가됨에 따라 점점 저온 쪽으로 이동하여, 6 wt% 촉매의 경우 $220{\sim}340^{\circ}C$에서 높은 활성을 보였다. $V_2O_5$ 함량이 8 wt% 촉매의 경우 전 온도 구간에서 6 wt% 촉매보다 낮은 NO 환원율을 보였다. 그러나 반응온도 $340^{\circ}C$ 이상에서는 촉매의 $V_2O_5$ 함량이 증가함에 따라 NO 전환율이 감소하였다. 이는 $V_2O_5-WO_3/TiO_2$ 촉매의 NO 환원을 위한 촉매 활성점 상당 크기 이상의 $V_2O_5$ 입자와 관계되는 것으로 판단되며 촉매 입자가 클수록 $320^{\circ}C$ 이상에서 암모니아 산화에 의해 발생되는 $N_2O$ 생성을 고려하여야 한다. $V_2O_5-WO_3/TiO_2$ 촉매는 배기가스 중의 질소산화물 제거를 위하여 현재 통상적으로 $350{\sim}450^{\circ}C$의 영역에서 운전되고 있으나, 고온 영역에선 2차 오염물인 $N_2O$의 발생을 피할 수 없고 에너지 소비량이 많으므로, $250{\sim}320^{\circ}C$의 저온 영역에서 적합한 촉매로써 $V_2O_5$ 함량이 높은 $V_2O_5-WO_3/TiO_2$ 촉매의 사용이 권장되었다.

• 한국재료학회지
• /
• 제5권8호
• /
• pp.945-952
• /
• 1995

기계적합금화한 Al-8wt.%(Ti+Zr)합금의 열적안정성에 미치는 Zr첨가의 영향에 대하여 조사하였다. Ti에 대한 Zr의 첨가비가 증가함에 따라 고온에서 장시간 노출에 따른 합금의 경도감소가 저하되어 합금의 열적안정성이 향상된 결과를 나타내었는데 이는 TEM 관찰결과 분산입자의 조대화가 억제되었기 때문이었다. XRD, SAD 및 EDS 분석결과 이러한 분산입자들은 DO$_{2+}$와 DO$_{23}$구조를 갖는 $Al_3$(Ti+Zr)삼원계 금속간화합물이었으며 특히 DO$_{23}$Al$_3$(Ti+Zr)은 Zr의 첨가비가 증가함에 따라 보다 작은 Al기지와의 격자간불일치도를 갖는 방향으로 격자상수가 변화하여 합금의 열적안정성 향상에 주된 기여를 한 것으로 생각된다

• Journal of Korean Dental Science
• /
• 제10권1호
• /
• pp.10-21
• /
• 2017

Purpose: The purpose of this study was to investigate the electrochemical characteristics of nanotubular Ti-25Nb-xZr ternary alloys for dental implant materials. Materials and Methods: Ti-25Nb-xZr alloys with different Zr contents (0, 3, 7, and 15 wt.%) were manufactured using commercially pure titanium (CP-Ti), niobium (Nb), and zirconium (Zr) (99.95 wt.% purity). The alloys were prepared by arc melting in argon (Ar) atmosphere. The Ti-25Nb-xZr alloys were homogenized in Ar atmosphere at $1,000^{\circ}C$ for 12 hours followed by quenching into ice water. The microstructure of the Ti-25Nb-xZr alloys was examined by a field emission scanning electron microscope. The phases in the alloys were identified by an X-ray diffractometer. The chemical composition of the nanotube-formed surfaces was determined by energy-dispersive X-ray spectroscopy. Self-organized $TiO_2$ was prepared by electrochemical oxidation of the samples in a $1.0M\;H_3PO_4+0.8wt.%$ NaF electrolyte. The anodization potential was 30 V and time was 1 hour by DC supplier. Surface wettability was evaluated for both the metallographically polished and nanotube-formed surfaces using a contact-angle goniometer. The corrosion properties of the specimens were investigated using a 0.9 wt.% aqueous solution of NaCl at $36^{\circ}C{\pm}5^{\circ}C$ using a potentiodynamic polarization test. Result: Needle-like structure of Ti-25Nb-xZr alloys was transform to equiaxed structure as Zr content increased. Nanotube formed on Ti-25Nb-xZr alloys show two sizes of nanotube structure. The diameters of the large tubes decreased and small tubes increased as Zr content increased. The lower contact angles for nanotube formed Ti-25NbxZr alloys surfaces showed compare to non-nanotube formed surface. The corrosion resistance of alloy increased as Zr content increased, and nanotube formed surface showed longer the passive regions compared to non-treatment surface. Conclusion: It is confirmed that corrosion resistance of alloy increased as Zr content increased, and nanotube formed surface has longer passive region compared to without treatment surface.

• 한국세라믹학회지
• /
• 제42권2호
• /
• pp.88-93
• /
• 2005

아크 이온 플레이팅과 스퍼터로 구성된 하이브리드 시스템을 이용하여 다성분계 Ti-Al-Si-N 코팅막을 WC-Co 기판에 증착하였다. 증착시 Si 함량을 변화시켜 코팅막의 마모특성에 Si 함량이 미치는 영향에 대하여 조사하였다. 마모 특성을 관찰하기 위하여 Ti-Al-Si-N 코팅막이 증착된 WC-Co 원판에 3N의 하중, 0.1 m/s의 속도로 볼 온 디스크(ball-on-disk) 형태의 마모시험기를 이용하여 건식 마모 실험을 하였다. 상대재로는 스틸볼과 지르코니아볼을 사용하였다. 상대재가 스틸볼의 경우 Ti-Al-Si-N 코팅막의 마찰계수가 Ti-Al-N 코팅막의 마찰계수보다 낮게 나타났다 이는 Si가 첨가되어 마모시 상대재와 코팅막 사이에 자기윤활효과(self-lubricant effect)에 의한 것으로 여겨진다. 코팅막과 스틸볼 사이에 응착 마모 거동을 보였으며, Si의 함량이 증가함에 따라 마찰계수는 감소하였다. 한편, 상대재가 지르코니아 볼의 경우 코팅막과 지르코니아 볼 사이에서 연삭마모 거동이 더 지배적이었고, Si 함량이 증가할수록 마찰계수는 증가하였다.

• 한국결정성장학회지
• /
• 제20권1호
• /
• pp.21-24
• /
• 2010

고주파 유전체 세라믹 $(Ca_{0.7}Sr_{0.3})_m(Ti_yZr_{1-y})O_3$ 의 미세구조 및 전기적 특성에 대한 Ti 이온 및 몰비의 영향을 조사하였다. $CaZrO_3$의 Zr 위치에 Ti 이온의 치환은 세라믹 소체의 소결밀도 및 미세구조에 큰 영향을 미친다. Zr 위치에 Ti 이온의 치환량 증가에 따라, 소결밀도는 급격히 증가하고, 몰비 m=1.01에서 치밀한 미세조직이 얻어졌다. 한편, 몰비 m=0.99 조성에 대해서는 Ti 치환량이 증가하여도 소결밀도 및 미세구조는 거의 변화가 없이 일정하였다. Ti 치환량 증가에 따라 TCC (temperature coeITicient of capacitance) 곡선은 시계방향으로 회전하여 몰비 m=0.99, 1.01 조성에 대해 COG 특성을 만족하였다. $CaZrO_3$의 TCC 및 소결특성 제어를 위해서는 Ti 치환량이 몰비보다는 효과적임을 보여준다.

• 한국분말재료학회지
• /
• 제4권4호
• /
• pp.283-290
• /
• 1997

$Ti_5Si_3$ intermetallics containing 0-6 wt% of Cu were made by reactive sintering (RS) under vacuum using elemental powder mixtures (Process 1), electro-pressure sintering (EPS) using RS'ed materials (Process2), and EPS using elemental powder mixtures (Process 3). Relatively low dense titanium silicides were gained by process 1, in which porosity decreased with increasing Cu content. For example, porosity changed from 42 to 19.4% with the increase in Cu content from 0 to 6 wt%, indicating that Cu is a useful sintering aid. The titanium silicides fabricated by Process 2 had a higher density than those by Process 1 at given composition, and porosity decreased with increasing Cu content. For example, porosity decreased from 38 to 6.8% with the change in Cu content from 0 to 6 wt%. A high dense titanium silicides were obtained by Process 3. In this Process, porosity decreased a little by Cu addition, and was almost insensitive to Cu content. Namely, about 9 or 7% of porosity was shown in 0 or 1-6 wt% Cu containing silicides, respectively. The hardeness increased by Cu addition, and was not changed markedly with Cu content for the silicides fabricated by Process 3. This tendency was considered to be resulted from porosity, hardening of grain interior by Cu addition, and softening of grain boundary by Cu-base segregates. All these results suggested that EPS using elemental powder mixtures (Process 3) is an effective processing method to achieve satisfactorily dense titanium silicides.