• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.04a
• /
• pp.117-120
• /
• 2009

The rolling of flat slabs or sheet metal is probably the most advanced technique of metalworking technology. In spite of this very intensive activity, the problem if edge cracking has not been resolved. Although edge cracking is a major industrial problem, relatively little well-documented experimental work has been published on subject. Despite the paucity of exact experiments, it is reasonably certain from published data that three causes contribute to its occurrence; (1) limited ductility of the rolled material (2) uneven deformation at the edges and (3) variations in stresses along the width of the rolled material, particular near the edge. The present study was carried out to show the generation of edge cracking using ductile fracture criteria and FE-simulation. The validity of simulated results was verified by rolling experiments of steel strip.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.08a
• /
• pp.412-422
• /
• 1999

Scale defects generated on the strip surface in a tandem finishing mill line are collected from the strip trapped among the production mills by freezing the growing scale on the strip by the melt glass coating and shutting down the line simultaneously. The samples observed of its cross sectional figure showed the process of scale defect formation where the defects are formed at the base metal surface by thicker oxidized scale during each rolling passes. The properties of the oxidized layer growth both at rolling and inter-rolling are detected down sized rolling test simulating carefully the rolling condition of the production line. The thickness of the oxidized layer at each rolling pass are simulated numerically. The critical scale thickness to avoid the defect formation is determined through the expression of mutual relation between oxidized layer thickness and the lanks of the strip called quality for the scale defects. The scale growth of scale less than the critical thickness and also to keep the bulk temperature tuning the water flow rate and cooling time appropriately. Two units of Inerstand Cooler are designed and settled among the first three stands in the production line. Two units of scale defect is counted from the recoiled strip and the results showed distinct decrease of the defects comparing to the conventionaly rolled products.