• Journal of Dental Rehabilitation and Applied Science
• /
• v.30 no.2
• /
• pp.102-111
• /
• 2014

Purpose: Surface damage and bonding strength difference after micromechanical treatment of zirconia surface are to be studied yet. The aim of this study was to evaluate the difference of fracture resistance and bonding strength between more surface-damaged group from higher air-blasting particle size and pressure, and less damaged group. Materials and Methods: Disk shape zirconia ($LAVA^{TM}$) was sintered and air-blasted with $30{\mu}m$ particle size (Cojet), under 2.8 bar for 15 seconds, $110{\mu}m$ particle size (Rocatec), under 2.8 bar for 15 seconds, and $110{\mu}m$ particle size (Rocatec), under 3.8 bar for 30 seconds respectively. Biaxial flexure test and bonding failure load test were performed serially (n = 10 per group). For bonding test, specimens were bonded on the base material having similar modulus of elasticity of dentin with $200{\mu}m$-thick resin cement for tension of surface damage. Failure load of bonding was detected with acoustic emission (AE) sensor. Results: There were no significant differences both in the biaxial flexure test and bonding failure load test between groups (P > 0.05). Sub-surface cracks were all radial cracks except for two specimens. Conclusion: Within the limitations of no aging under monotonic load test, surface damage from higher air-blasting particle size and pressure was not significant. Evaluations of failure load with bonded zirconia disks was clinically relevant modality for surface damage and bonding strength, simultaneously.

• Journal of dental hygiene science
• /
• v.13 no.3
• /
• pp.290-295
• /
• 2013

The purpose of this study was to investigate the shear bond strength between various commercial all-ceramic system core and veneering ceramics, and evaluate the clinical stability by comparing the conventional metal ceramic system. The test samples were divided into three groups: Ni-Cr alloy (metal bond), yttria-stabilized, tetragonal zirconia polycrystal (Y-TZP) (zirconia bond), lithium disilicate (lithium disilicate bond). The veneering porcelain recommended by the manufacturer for each type of material was fired to the core. After firing, the specimens were subjected to shear force in a universal testing machine. Load was applied at a crosshead speed of 0.50 mm/min until failure. Average shear strengths (mega pascal) were analyzed with a one-way analysis of variance and the Tukey test (${\alpha}$=0.05). The mean shear bond strength${\pm}$SD in MPa was $44.79{\pm}2.31$ in the Ni-Cr alloy group, $28.32{\pm}4.41$ in the Y-TZP group, $15.91{\pm}1.39$ in the Lithium disilicate group. The ANOVA showed a significant difference among groups (p<0.05). None of the all-ceramic system core and veneering ceramics could attain the high bond strength values of the metal ceramic combination.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.37 no.4
• /
• pp.177-185
• /
• 2021

Clinical applications of translucent zirconia as well as traditional zirconia (3 mol% yttria stabilized tetragonal zirconia polycrystal, 3Y-TZP) are increasing. For this reason, studies on factors affecting the optical properties of dental zirconia have been continuously reported. The optical effect of dental zirconia may vary depending on the yttria content, the thickness of the prosthesis, the sintering process, polishing, glazing and cementation in laboratory and clinical procedures. Increasing the yttria concentration can reduce the masking effect. Translucency decreases as the thickness of the restoration increases, but the required thickness may vary depending on the properties of the zirconia block. The high-speed sintering method can shorten the manufacturing time, but in some cases, the translucency of the prosthesis may decrease. In addition, the optical properties can be affected by the surface roughness of zirconia and the polishing process. The use of an appropriate colored cement can help with the masking effect of zirconia and can be useful for color matching for more esthetic results.

• Tribology and Lubricants
• /
• v.21 no.5
• /
• pp.216-220
• /
• 2005

The sliding wear behaviors of three different compositions of novel low temperature degradation-free zirconia/alumina (LTD-free Z/A) composites were examined in a ceramic-ceramic contact pair. The wear tests were performed by using a pin-on-disk type wear tester in a linear reciprocal sliding motion with a line contact in both dry and bovine serum lubricated conditions at room temperature. From the results of dry sliding wear tests, Z/A#1((5.3Y, 4.6Nb)-TZP/80 $vol\%Al_2O_3$) showed the best wear resistance among three kinds of LTD-free Z/A composites. For the bovine serum lubricated sliding wear tests, wear was too little to be measured for all kinds of Z/A composites. These novel LTD-free Z/A composites having excellent wear resistance demonstrated a potential as the alternative materials for the ceramic-ceramic contact pairs of femoral head and acetabular liner in total hip replacement.

• Journal of the Korean Chemical Society
• /
• v.42 no.1
• /
• pp.9-15
• /
• 1998

The geometrical parameters, vibrational frequencies, and IR intensities of dimethyldioxirane had been investigated using high level ab initio quantum mechanical methods with various basis sets. The polarization function decreases C-O and C-C bond distances significantly and the electron correlation effect increases those bond lengths slightly, while other bond lengths and bond angles are relatively stable for basis set size and correlation effect. The experimental and other theoretical vibrational frequencies and IR intensities of dimethyldioxirane will be compared and discussed with our high level theoretical predictions.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2004.11a
• /
• pp.355-361
• /
• 2004

Ceramic femoral heads in the total hip replacement have been developed to reduce the polyethylene liner wear, Alumina and zirconia (3Y-TZP) having the excellent tribological properties are coupled against acetabular cups of polyethylene and are used in clinical application worldwide. However, alumina has a risk of catastrophic failure, and zirconia has the low temperature degradation in spite of enhanced fracture toughness. Recently, novel zirconia/alumina composite is very attractive due to the low temperature degradation (LTD)-free character and high fracture toughness. In the present study, we focus on the wear of ceramic on ceramic, which are able to be used as femoral heads and acetabular cups. Therefore, LTD-free zirconia/alumina composites with three compositions are made in a form of disk and cylinder, and the wear of the composites is performed on pin-on-disk type wear tester. The wear is conducted with or without lubricant. All the composites fabricated with the different composition show the good wear resistance.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.190-193
• /
• 2002

3mol% $Y_2O_3$ Partially-Stabilized Zirconia single Crystals (PSZCs) containing a small quantity (<0.5%) of rare-earth oxides ($CeO_2,\;Tb_2O_3$) were prepared by using a direct high-frequency skull melting technique to evaluate hydrothermal stability in an autoclave. Pole exhibited no $t{\rightarrow}m$ phase transformation during aging for 5h at temperatures from 150 to 250$^{\circ}C$ and 4MPa water vapor pressure in an autoclave, resulting in excellent hydrothermal stability.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.5
• /
• pp.415-422
• /
• 2014

PURPOSE. The purpose of this study was to evaluate and compare the translucency of shaded zirconia allceramic systems. MATERIALS AND METHODS. Translucency of 3 different zirconia all-ceramic systems colored by different techniques was compared with a lithium disilicate glass-ceramic (IPS e.max Press). Square-shaped specimens with 0.5 mm thickness were fabricated from In-Ceram YZ, ICE Zirkon and Katana systems in A1, A2 and A3.5 shades according to Vitapan Classical shade tab (n=11). Specimens were then veneered and glazed with corresponding veneer ceramic recommended by each zirconia system manufacturer and the total thickness was set to 1.5 mm. Translucency measurements were performed with VITA Easyshade Compact spectrophotometer after each stage and translucency parameter was calculated. Data were statistically analyzed with repeated measures ANOVA and Tukey multiple comparison test. RESULTS. The control group was significantly more translucent than the zirconia systems (P<.05). ICE Zirkon cores showed the least translucency; neither In-Ceram YZ nor Katana systems were superior to each other in terms of translucency. Translucency of all specimens was decreased after veneering, and the translucency rankings were changed. CONCLUSION. Coloring technique did not have a significant effect on translucency of zirconia cores. Although zirconia systems were less translucent than lithium disilicate glass ceramic, they had partial translucency and there were translucency differences among the zirconia systems. Chroma affected the translucency of precolored zirconia cores.

• Journal of the Korean Ceramic Society
• /
• v.48 no.2
• /
• pp.152-159
• /
• 2011

The green and hard machining characteristics of dental ceramics are of great interest to dental industry. The green bodies of TZP/$Al_2O_3$ composites were prepared by the cold isostatic pressing, and machined on the CNC lathe using PCD (polycrystalline diamond) insert under various machining conditions. With increasing nose radius of PCD insert, surface roughness initially increased due to increased cutting resistance, but decreased by the onset of sliding fracture. The lowest surface roughness was obtained at spindle speed of 1,300 rpm and lowest feed rate. Hard bodies were prepared by pressureless sintering the machined green bodies at several temperatures. The grinding test for sintered hard body was conducted using electroplated diamond bur with different grit sizes. During grinding, grain pull out in the composite was occurred due to thermal expansion mismatch between the alumina and zirconia. The strength of the composite decreased with alumina contents, due to increased surface roughness and high monoclinic phase transformed during grinding process. The final polished samples represented high strength by the elimination of a phase transformation layer.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2003.11a
• /
• pp.91-94
• /
• 2003

Ceramic femoral heads in the total hip replacement have been developed to reduce the polyethylene liner wear. Alumina and zirconia (3Y-TZP) are using in clinical application worldwide and there are many good test reports. However, alumina has a risk of catastrophic failure, and zirconia has the low temperature degradation in spite of enhanced fracture toughness. Recently, novel zirconia/alumina composite having low temperature degradation-free character and high fracture tough . was developed and it leads the lower wear 3f polyethylene than alumina and zirconia. In the present study, in order to optimise the microstructure of low temperature degradation (LTD)-free zirconia/alumina composite for the best wear resistance of polyethylene, various compositions of (LTD)-free zirconia/alumina composites were fabricated, and the sliding wear of UHMWPE against these novel composites were examined and compared with that against alumina and zirconia ceramics used for total hip joint heads.