• Korean Journal of Materials Research
• /
• v.24 no.12
• /
• pp.652-657
• /
• 2014

The purpose of this study was to investigate the microstructures and mechanical properties of zirconia toughened alumina (ZTA) ceramics prepared from two kinds of 3Y-TZP powders. ZTA composites were prepared by adding two kinds of 3Y-TZP powders, 3YEH (BET = $7m^2/g$) and 3YEM (BET = $16m^2/g$), to ${\alpha}$-alumina in the range of 5-25 wt%. It was found that the microstructure photographs of the ZTA composites showed that the average grain size of alumina decreased as the content of zirconia increased. In our present study, specimens containing 3YEM zirconia exhibited smaller grain sizes compared to those of 3YEH zirconia. The Vickers hardness of the ZTA composites that were sintered at $1600^{\circ}C$ for 2 hrs was found to smoothly decrease with increasing zirconia content because of the low Young modulus in zirconia. The Vickers hardness of the ZTA containing 3YEH zirconia was greater than that of the 3YEM zirconia. In substance, the fracture toughness ($K_{1c}$) of the ZTA composites increased as the content of zirconia increased. The fracture toughness ($K_{1c}$) of ZTA containing 3YEM zirconia was greater than that of 3YEH zirconia.

• Journal of the Korean Ceramic Society
• /
• v.35 no.5
• /
• pp.429-436
• /
• 1998

The mechanical properties and damage mode of {{{{ {Y}_{2 } {O}_{3} }}-doped tetragonal (Y-TZP) can-didated as biomaterials were performed under indentation stress-strain curve critical load for yield and cracking strength degradation and fatigue behavior with Hertzian indentation tests. This material shows the brittle behavior which is confirmed by indentation stress-strain response. The critical load for cracking(Pc) is much higher than that for yields (Py) indicating crack resistance Strength were strongly dependant on contact area and there were no degradation when the indenter size was ${\gamma}$=3.18 mm suggesting that Y-TZP should be highly damage tolerant to the blunt contacts. Multi-cycle contact were found to be innocuous up to {{{{ {10 }^{6 } }} cycles at 500N and {{{{ {10 }^{5 } }} cycles at 1000N in water. On the other hand contacts at {{{{ {10 }^{6 } }} cycles at 1000 N in water did show some signs of incipient degradation. By contrast contacts with Vickers indenter pro-duced substantial strength losses at much lower loads suggesting that the mechanical integrity of this ma-terial would be compromised by inadvertent sharp contacts.

• Journal of the Korean Ceramic Society
• /
• v.32 no.12
• /
• pp.1337-1348
• /
• 1995

TZP/SUS- and ZT/SUS-functionally gradient materials (FGM) were fabricated by pressureless sintering in Ar-atmosphere. The sintering defects such as warping, frustrum formation, splitting and cracking which originated from shrinkage and sintering behaviors of metal and ceramics different from each other could be controlled by the adjustment with respect to the particle size and phase type of zirconia. The residual stresses generated on the metal and ceramic regions in FGM were characterized with X-ray diffraction method, and relaxed as the thickness and number of compositional gradient layer were increased. The residual stress states in TZP/SUS-FGM have irregular patterns by means of the different sintering behavior and cracking at ceramic-monolith. While in ZT/SUS-FGM, compressive stress is induced on ceramic-monolith by the volume expansion of monoclinic ZrO2 at phase transformation. Also, compressive stress is induced on metal-monolith by the constraint of warping which may be created to the metal direction by the difference of coefficient of thermal expansions. As a consequence, it has been verified that the residual stress generated on FGM is dominantly influenced by the thickness and number of compositional gradient layer, and the sintering defects and residual stress can be controlled by the constraint of the difference of shrinkage and sintering behaviors of each component.

• Journal of Technologic Dentistry
• /
• v.35 no.4
• /
• pp.271-280
• /
• 2013

Purpose: This study was to assess the effect of surface and heat treatment on the bond strength of veneering ceramics to zirconia. Methods: The specimens were divided into 7 groups according to surface treatment and heat treatment conditions prior to porcelain application. ten specimens from each group were subjected to a 3-point flexural test. In addition the influence of surface and heat treatment on surface roughness values and phase transformation of zirconia was evaluated. Statistical analysis was performed with one-way ANOVA and post hoc Tukey's test. Results: Bond strength ranged from $20.67{\pm}3.13MPa$ to $32.69{\pm}4.52$. Bond strength of surface treatment group was lower than that of control group but only $Al_2O_3$ sandblasting group was significant difference. Bond strength of heat treatment group was higher than that of surface treatment group but there was no statistical significance. Conclusion: Bond strength of veneering ceramics to zirconia was affected by surface and heat treatment.

• Journal of the Korean Society for Heat Treatment
• /
• v.36 no.4
• /
• pp.215-222
• /
• 2023

3Y-TZP (3 mol% yttria-stabilized tetragonal zirconia polycrystals, 3Y-TZP) ceramics are emerging as dental implant materials due to their superior optical and mechanical properties as well as excellent biophysical properties, in spite of low bioactivity. In this study, we investigated to sintered properties and microstructural defects of dental zirconia implants fabricated by ceramic injection molding and post-HIP (Hot isostatic pressing) processing and analyzed the processing parameters related with the obtainment of its high sinterd density. Sintered and microstructural parameters, i.e, apparent density, grain size and phase composition of zirconia implants fabricated by injection molding were dependent on the fixtute size and implant type. Maximum sintered density of 99.2% and minimum grain size of 0.3-0.4 ㎛ were obtained from large-scaled 2-body sample. In 1-body ceramic implant, high sintered density of 99.5% was obtained, but it had a little monoclinic phase and wide grain size distribution.

• Journal of Technologic Dentistry
• /
• v.34 no.2
• /
• pp.83-93
• /
• 2012

Purpose: The objective of this study is to find out physical properties and the flexural strength changed by the low temperature degradation of the block which is needed to make bio-prosthetic dentistry which is better than feldspar affiliated ceramic made by building up ceramic powder and also to apply this to the clinical use of zirconia monolithic all-ceramic crown. Methods: Flexural strength of each sample was evaluated before and after the Low Temperature Degradation, and physical properties of the Tetra Zirconia Block containing 3mol % was evaluated as well. The average and standard deviation of each experimental group were came out of the evaluation. Statistical package for social science 18.0 was used for statistics. Results: The average density of the monolithic all-ceramic crown was $6.0280{\pm}0.0147g/cm$, the relative density was 99.01 %. When the sample was sintered at $1480^{\circ}C$ the diameter of average particle was $396.62{\pm}33.71nm$. All the samples had no monolithic peak after XRD evaluation but only had tetragonal peak. There were statistically significant differences in the result of flexural strength of the samples evaluated after and before the low temperature degradation, the flexural strength before the low temperature degradation was $1747.40{\ss}{\acute{A}}$, at the temperature of $130^{\circ}C$ the flexural strength after the low temperature degradation was 1063.99MPa (p<0.001). There was statistically significant difference in the result of strength of 1020.07MPa after the low temperature degradation at the temperature of $200^{\circ}C$ (p<0.001). Conclusion: The block which was made for this evaluation possesses such an excellent strength among dental restorative materials that it is thought to have no problems to use for tetragonal zirconia polycrystal.

• Journal of dental hygiene science
• /
• v.14 no.1
• /
• pp.29-34
• /
• 2014

The purpose of this study was to evaluate the influence of low temperature degradation (LTD) on the bonding strength of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP). The push-shear bond test method was used to investigate the core-veneer bonding strength of industrially manufactured Y-TZP core ceramic and manufacturer recommended veneering ceramic. Four groups from ceramic-zirconia specimens (n=28; n=7 per group) were assigned into four experimental aging conditions, namely storage in an autoclave at $134^{\circ}C$ for 0, 3, 5, 10 hours. Bonding strength was obtained using a universal testing machine with crosshead speed 0.5 mm/min. Data were statistically analyzed using one-way ANOVA and Tukey's test (${\alpha}=0.05$). In bonding strength test, the group which was treated with LTD showed lower bonding strength than no treated group. The ceramic-zirconia bonding strength was affected by LTD (p<0.05). Digital microscope examination of the fracture surface showed mixed failures with adhesive and cohesive types in LTD with treated Y-TZP groups.

• Korean Journal of Materials Research
• /
• v.20 no.10
• /
• pp.518-523
• /
• 2010

In this study, partially stabilized zirconia was synthesized using a chemical $Y_2O_3$ stabilizer and hydrothermal method. First, $YCl_3-6H_2O$ and $ZrCl_2O-8H_2O$ was dissolved in distilled water. Y-TZP (a $Y_2O_3$-doped toughened zirconia polycrystalline precursor) was also prepared by conventional co-precipitates in the presence of an excess amount of $NH_4OH$ solution under a fixed pH of 12. The Y-TZP precursors were filtered and repeatedly washed with distilled water to remove $Cl^-$ ions. $ZrO_2$-Xmol%$Y_2O_3$ powder was synthesized by a hydrothermal method using Teflon Vessels at $180^{\circ}C$ for 6 h of optimized condition. The powder added with the Xmol%- $Y_2O_3$ (X = 0,1,3,5 mol%) stabilizer of the $ZrO_2$ was synthesized. The crystal phase, particle size, and morphologies were analyzed. Rectangular specimens of $33mm{\times}8mm{\times}3$ mm for three-point bend tests were used in the mechanical properties evaluation. A teragonal phase was observed in the samples, which contains more than 3 mol% $Y_2O_3$. The $3Y-ZrO_2$ agglomerated particle size was measured at $7.01{\mu}m$. The agglomerated particle was clearly observed in the sample of 5 mol % $Y_2O_3-ZrO_2$, and and the agglomerated particle size was measured at 16.4 um. However, a 20 nm particle was specifically observed by FE-SEM in the sample of 3 mol% $Y_2O_3-ZrO_2$. The highest bending fracture strength was measured as 321.3 MPa in sample of 3 mol% $Y_2O_3-ZrO_2$.

• Korean Journal of Clinical Laboratory Science
• /
• v.38 no.3
• /
• pp.166-172
• /
• 2006

Metallo-${\beta}$-lactamase (MBL) can hydrolyze all ${\beta}$-lactams except monobactams and frequently coexists with various antibiotic resistance genes such as aminoglycoside resistance, sulfonamide resistance gene, etc. Therefore, the effective antibiotics against infections by these bacteria are markedly limited or can't even be found. We tried to search in-vitro antimicrobial combinations with synergistic effects for a VIM-2 type MBL producing Pseudomonas aeruginosa, isolated from clinical specimen. On the selection of antibiotic combinations with synergistic effects, we performed a one disk synergy test, modified Pestel's method, in agar without aztreonam (AZT). The bacteriostatic synergistic effects of this tests were scored as $S_1$ (by susceptibility pattern in agar without antibiotics), $S_2$ (by the change of susceptibility in agar with or without antibiotics) and $S_3$ ($S_1$ + $S_2$) and was classified into weak (1 point), moderate (2 points) and strong (3 points) by $S_3$ score. Subsequently, we carried out the time-killing curve for the antibiotic combinations with the strong synergistic bacteriostatic effect. One VIM-2 type MBL producing P. aeruginosa confirmed by the PCR showed all resistance against all ${\beta}$-lactams except AZT, aminoglycoside and ciprofloxacin. In the one disk synergy test, this isolate showed a strong bacteriostatic synergistic effect for the antibiotic combination of AZT and piperacillin-tazobactam (PIP-TZP) or AZT and amikacin (AN). On the time-killing curve after six hours of incubation, the colony forming units (CFUs/mL) of this bacteria in the medium broth with both combination antibiotics were decreased to 1/18.7, 1/17.1 of the least CFUs of each single antibiotics. The triple antibiotic combination therapy including AZT, PIP-TZP and AN was shown to be significantly synergistic after 8 hrs of exposure. In a VIM-2 MBL producing P. aeruginosa with susceptibility for AZT, the triple antibiotic combination therapy including AZT, PIP-TZP and AN may be considered as an alternative antibiotics modality against the infection by some MBL type. But the antimicrobial combination therapy for many more MBL producing isolates is essential to know as soon as possible for the selection of effective treatment against the infection by this bacteria.

• Journal of the Korean Ceramic Society
• /
• v.31 no.10
• /
• pp.1197-1201
• /
• 1994

The fracture strength and fracture modes were studied in 3Y-TZP/NiNi bonding which change their interfacial structure with bonding condition. Average 4-point bending strength of 200 MPa to 400 MPa were achieved. The formation of Ti-oxide phase at the interface critically influenced the bonding strength and fracture mode. The fracture surface of Ti-oxide free interface contained multiphase in some case including ZrO2. From the result it was confirmed that in order to maximize the bonding strength crack deflection from interface to ceramic was required.