• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1163-1164
• /
• 2006

TZM alloy having elongated coarse-grain structure was developed by three-step internal nitriding treatment at 1423 to 1873 K in $N_2$ and subsequent recrystallization treatment at 2173 K in vacuum. Some specimens were subjected to re-nitriding treatment at 1873 K for 16 h. After the recrystallization treatment, aspect ratio (L/W) of grains for rolling direction was about 50 at the maximum. Yield stress obtained at 1773 K after re-nitriding treatment was about 6 times as large as that of recrystallized specimen. Re-nitriding was very effective in the improvement in strength of TZM alloy having elongated coarse-grain structure.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 추계학술발표대회
• /
• pp.40.1-40.1
• /
• 2011

TZM합금은 융점이 높은 Mo 기지에 미세한 (Zr,Ti)C의 석출물이 분산되어 있어 고온에서 다양한 부품에 응용가능하다. 하지만, TZM합금이 대기중 고온에 노출될 경우, 초기 산화물이며 약 $600^{\circ}C$부터 기화가 시작되는 $MoO_3$상이 형성됨으로써 물성에 치명적인 영향을 미친다. 이러한 산화거동을 막기 위하여 표면보호 코팅을 필요로 한다. 본 연구에서는 복잡한 형상과 대량생산이 가능하며 표면 코팅층과 모재의 접합성이 가장 강하다고 알려진 확산코팅법을 이용하여 Si을 TZM 합금에 코팅하였으며, 코팅층의 형성 속도론을 이해하기 위하여 온도별 및 시간별로 코팅을 수행하여 시간과 온도에 따른 코팅층의 형성 기구를 고찰하고자 하였다. Si의 확산코팅결과, $MoSi_2$층은 $1350^{\circ}C$에서 산화시에 두께가 감소하였으며, $Mo_5Si_3$상은 두께가 성장하였다. 코팅층의 확산거동을 속도론적 분석을 통하여 규명하고 논의하고자 한다.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2004년도 International Symposium on Powder Materials and Processing
• /
• pp.19-19
• /
• 2004