• 한국레이저가공학회지
• /
• 제15권1호
• /
• pp.10-14
• /
• 2012

Pulse laser welding was performed on C22 metal bellows. The results can be summarized as follows: Laser welded metal bellows had less thermal distortion, narrow HAZ, high aspect ratio in comparison with other welding processes like TIG, Plasma welding. Laser welded bellows has higher tensile strengths than that C22 base metal. The value of hardness in laser weld metal was measured 100-120 Hv, it was decreased compared to the base metal. It is reasoned that due to the annealed by heat input during the laser welding.

• Journal of Welding and Joining
• /
• 제10권1호
• /
• pp.20-34
• /
• 1992

Characteristics of two correcting methods, a new Autogeneous GTAW heating (TIG) method and the conventional GMAW bead-on plate welding(MIG) method, for distorted aluminum fabrication structures were studied. As a result of microscopic study of Autogeneous GTAW heating and GMAW bead-on plate welding areas, porosities in weld metal and surface cracks in local heating zone were found. Through the mechanical tests, it was verified that porosities decrease tensile strength and surface of distortion, angular displacement and transeverse shrinkage were measures and compared. In order to investigate changes of material properties in heating area and cause of defects such thermal stresses were calculated by ADINA. Through the computations of transient thermal stresses and microscopic observation of fracture surface, thermal stress was found to be the cause of crack during Autogeneous GTAW heating.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2003년도 추계학술대회
• /
• pp.289-294
• /
• 2003

The object of this study is to investigate the effect of compounded welding by using acoustic emission (AE) signals fur weld heat affected zone (HAZ) in tensile testing. This study was carried out a SM 490A high tension steel for electronic shielded metal are welding (SMAW), $\textrm{CO}_2$ gas arc welding and TIG welding. And correspondingly, the root openings are 3, 4 and 2.8mm. Data displays are based on the measured parameters of the AE signals, along with environmental variables such as time and load. These history plots give us useful and powerful information to analyze the results of material evaluation testing.

• 한국공작기계학회논문집
• /
• 제10권1호
• /
• pp.94-100
• /
• 2001

Distortion is a potential problem with all welded fabrication and should be caused dimensional changes and mismatch of joints during welding fabrication. Correction unacceptable weld distortion is extremely costly and in some case impossible. The aim of the present work is to verify the variation of the compressive force, tensile force and distortion during plastic deformation under Tungsten-inert-gas(TIG) welding, on type 304 stainless steel. Experimental results show that possibili-ty if measuring deformation during welding and good correlation was found between analytical and experimental result ad finite element methods have been used to model temperature analysis.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2003년도 춘계학술대회 논문집
• /
• pp.363-370
• /
• 2003

The object of this study is to investigate the effect of compounded welding by using an acoustic emission (AE) signals and doing a source location for weld heat affected zone (HAZ) through tensile testing. This study was carried out a SM 490A high tension steel for electronic shielded metal arc welding (SMAW), $CO_2$ gas arc welding and TIG welding. Data displays are based on the measured parameters of the AE signals, along with environmental variables such as time and load. These history plots are displays showing the chronological course of the test. Also, source location gives the X- and Y-coordinates of the AE source.

• Journal of Advanced Marine Engineering and Technology
• /
• 제19권4호
• /
• pp.42-50
• /
• 1995

To study the effect of welding methods on the Stress Corrosion Cracking (SCC) behavior of welded AISI type 316L and 304 austenitic stainless steel, the Slow Strain Rate Technique(SSRT) has been adopted in the boiling 45 wt% $MgCl_2$ solution. The results are as follows. 1) Welded sections are more susceptible than base metal in SCC, and the rank of SCC, and the rasistance in welding method is TIG, MIG, $CO_2$ and ARC. 2) The Ultimate tensile strength(UTS) and the strain of both base metal and welded joint are reduced as decreasing extension rate. 3) The SCC resistance of 316L base metal and welded sections are superior than that of 304. 4) The tendency of pitting and the SCC suseptibility are agreed well, and the SCC site is welded deposit section in 316L whereas HAZ in 304.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2003년도 춘계학술발표대회 개요집
• /
• pp.155-158
• /
• 2003

Orbital GTA welding is used in the pressure pipe line of auto-mobile, LNG and plant piping. To weld the pipe line safely, to some extent, the back bead must be formed in the root pass. In the plate welding the back bead can be observed, but in the pipe welding, the back bead can not be observed directly. In the welding around circumference, the parameters such as gravity, surface tension and arc force are different at each position. And then D/B for welding condition at each position are required. We also studied about the setting of the optimum orbital welding condition by controlling heat input.

• Journal of Welding and Joining
• /
• 제10권2호
• /
• pp.32-42
• /
• 1992

A method of optimization of process parameters in Arc Welding has been discussed in this paper. The method of investigation is based on the numerical calculation of weld bead by a finite element method and non-linear optimization technique is applied to estimated the optimization process parameters from the numerical calculation. The common package program(ANSYS 4.4A) was used to obtain the process parameters for a thin plate arc welding (TIG, CO$_{2}$). The results on some test are satisfactory and the used method of this paper is a useful guide to the optimum welding condition.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2011년도 제36회 춘계학술대회논문집
• /
• pp.476-479
• /
• 2011

티타늄 합금은 높은 내부식성, 우수한 피로 수명과 무게비에 비해 높은 강도를 가진다는 우수성으로 인해 항공기 부품과 화학 공업 분야등에 다양하게 사용되고 있다. 이번 연구에서는 Ti-3Al-2.5V 합금 TIG 용접부에 대하여 용접부 인성과 기계적 성질에 영향을 주는 가장 중요한 인자인 용접 입열에 대한 영향을 평가하고자 하였다. 이에 입열조건에 대한 용접부에 대한 강도, 충격 인성과 노치 인성을 평가하였으며 적정 입열 조건에서 강도와 인성이 우수한 용접부를 얻을 수 있다는 것을 확인하였다.

• 한국해양공학회지
• /
• 제1권2호
• /
• pp.93-100
• /
• 1987

Corrosion fatigue cracking of the austenitic stainless steel(bese metal & heat affected zone by TIG weld) was studied experimentally under the environments of various specific resistance and air. The characteristics of corrosion fatigue crack growth rate and the environmental constants of paris' rule were investigated for SUS 304 weldments in the various specific resistance. The influences of stress intensity factor range and corrosion on the crack growth rate were compared. The characteristics of corrosion fatigue cracking for the weldments were inspected from mechanical, electrochemical and microstructural point of view. Main results obtained are as follows: 1) As the specific resistance decreases, the environmental constant C of paris'rule increases(hence the corrosion fatigue crack growth rate is rapid), but the environmental constant m decreases, so the effect of corrosion to the crack growth rate is more susceptible than thet of stress intensity factor range. 2) As the stress intensity factor range decreases, the corrosion fatigue crack growth rate of heat affected zone is more susceptible than that of the base metal. 3) The corrosion fatigue crack growth rate of the heat affected zone is more rapid than that of the base metal, because of the phenomenon of softening and the less noble potential coused by wedlding heat cycle. 4) The corrosion fatigue cracking of SUS 304 weldment appears transgranular fracture.