• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2006.06a
• /
• pp.287-288
• /
• 2006

Cracks on the cylinder block of diesel engines will often happen due to cyclic load and thermal stress. According to the Classification Societies' rules, welding repairs of cylinder block made of cast irons are generally not permitted. However, such welding repairs became inevitable taking enormous cost and time for their renewal into consideration. In this study repair welding methods for the cylinder blocks, made of gray cast irons were reviewed and the tests of their welds were carried out in order to purpose the repair welding methods of packing seat and o-ring seat of cylinder block and apply them to the practice. It is concluding remarks that the suspected crack by a magnetic particle test due to different magnetic permeability can be identified, which are not associated with a mechanical discontinuity.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.4
• /
• pp.781-789
• /
• 1988

The fatigue crack growth and crack closure behavior of long through-thickness cracks and small half-penny shaped surface cracks were investigated in 5083-H113 Aluminum alloy under constant amplitude testing by the unloading elastic compliance method. It was found that, in the Region II, the crack growth behavior of both through-thickness and surface cracks exhibited the tri-linear form with two transitions and no concern with stress ratio R. In the Region I $I_{ab}$ and I $I_{b}$, through-thickness cracks grew faster than surface cracks in length direction, but at .DELTA. K .leq.4 MPa.root.m for R=0.1 the growth rates of surface cracks in depth direction, grew faster than those of through-thickness cracks. When the crack closure was considered, the growth rates of through-thickness cracks lay between the growth rates of depth direction and the growth rates of length direction in surface cracks. It is suspected that this was caused by the difference of crack closure at depth and length direction of surface cracks.s.

• Journal of Advanced Marine Engineering and Technology
• /
• v.23 no.3
• /
• pp.331-337
• /
• 1999

Cracks on the cylinder block of diesel engines will often happen due to cyclic load and thermal stress. According to the Classification Societies' rules welding reparis of cylinder block made of cast irons are generally not permitted. However such welding repairs became inevitable taking enormous cost and time for their renewal into consideration. In this study repair welding methods for the clinder blocks made of gray cast irons were reviewed and the tests of their welds were carried out in order to purpose the repair welding meth-ods of packing seat and o-ring seat of cylinder block and apply them to the practice. The following conclusions are botained :1 The tensile strength of weld of cast iron more than that of base metal can be obtained by means of preheating keeping temperature above $100^{\circ}C$ between welding pass-es preventing slag inclusion peening and cramping weld metal by studs. 2. The suspected crack by a magnetic particle test due to different magnetic permeability can be identified which are not associated with a mechanical discotinuity.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.27 no.2
• /
• pp.97-104
• /
• 2007

An investigation has been made on the relationship between characteristics of Acoustic Emission (AE) signal in welding flaw and the stress corrosion defect in-service for the high pressure pipe steel. In order to tackle the problem of welding flaw in high pressure pipe, specimens were made by the aid of the application of both corrosion liquid usage and a quenching method after local heating. The amplitude of signal was $60{\sim}75\;dB$ in the territory which is suspected for defect, and the specimens which only have welding flaw showed gradients of 0.034, 0.034, 0.035. Moreover, there is a certain increase in gradient even though the differences are very slight. That is, corrosion specimens showed new gradients of 0.040, 0.039, 0.041 which put welding flaw and corrosion mechanism together. After pressurizing 3 minutes, AE signal has been detected from welding flaw easily in each part of the section. It is possible to predict the occurrence and also prevent the damage of stress corrosion crack which has characteristics of cleavage fracture.