• Membrane Journal
• /
• v.15 no.3
• /
• pp.213-223
• /
• 2005

We prepared an anti-adhesion membrane made of sodium hyaluronate/sodium carboxymethylcellulose (HA/CMC) and evaluated its effectiveness for adhesion prevention in a rat model. The anti-adhesion membrane was prepared by lyophilizing HA/CMC solution and cross-linking properly with 1-Ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDAC). In a cecum/abdominal wall abrasion model of Sprague-Dawley rat, cecal serosa and abdominal wall were abraded in $1\times2\;(cm^2)$ with a bone burr after peritoneal midline incision and sutured at 3 points around the injured surface. The denuded cecum was covered with HA/CMC membrane (experimental group), or nothing (control group) and apposed to the abdominal wall. Most of the control group represented 3 or more of adhesion grade at POD 7, 14, 21, and 28, whereas $60\~70\%$ of the experimental group was 2 or less of adhesion grade at 14, 21, and 28. It was similar in the adhesion strength. In a general manner, the adhesion grade and strength showed gradual increasing until POD 14, almost same or a little increasing POD 21, but decreasing POD 28. Also the control group was much higher in adhesion grade, strength, and area than the experimental group. It is expected that the anti-adhesion membrane will have a good clinical result in postoperative adhesion prevention.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.3
• /
• pp.418-426
• /
• 2008

The objectives of this study were to examine the properties of fluoride-releasing resin composite restorative materials. Four commercially available compomer materials (Compoglass F: CF, $Dyract^{(R)}$ AP: DA, $Dyract^{(R)}$ flow: DF, F2000: FT) and one fluoride-releasing composite resin ($Tetric^{(R)}$ Ceram: TC) were selected as experimental materials. Rectangular-shaped tensile test specimens were fabricated in a teflon mold giving 5mm in gauge length and 2mm in thickness. Disk-shaped specimens were fabricated in the split teflon mold with diameter of 15mm and thickness of 1mm. After curing for an hour, specimens were immersed in deionized water at $37^{\circ}C{\pm}1^{\circ}C$ for 30 days. All specimens were thermocycled for 10,000 cycles with 15 seconds of dwelling time in each $5^{\circ}C$ and $55^{\circ}C$ water baths. Toothbrush abrasion test was conducted under a load of 1.5 N and the abraded surfaces were examined with surface roughness tester (SV-3000, Mitutoyo Co, Japan) and SEM (JSM-5800, JEOL, Japan). Fluoride recharging was done by toothbrushing for 3 min. using a fluoride toothpaste (Perio Alpine Herb, LG Household & Health Care, Korea). The results obtained were summarized as follows; 1. The highest tensile strength value of 32.3 MPa was observed in TC group and the lowest value of 16.8 MPa was observed in CF group. The tensile strength of TC group was significantly higher than those of CF and DF groups (P<0.05). 2. The lowest Ra value of 0.287 was observed in TC group and the highest value of 1.516 was observed in FT group. The Ra value of FT group was significantly higher than other groups (P<0.05). 3. The abraded surfaces revealed the increase of surface roughness due to the protrusion and missing of filler particles. 4. The release of fluoride of compomers after tooth brushing by Perio Alpine Herb was initially large and then followed by small and continuously. But it remains small and constant in fluoride-releasing composite resin of TC. 5. The highest value of fluoride release after toothbrushing by Perio Alpine Herb was $2.064{\mu}g/cm^2$ in CF group and the lowest value was $0.1119{\mu}g/cm^2$ in TC group. The amount of fluoride release of CF group was significantly higher than other groups (P<0.05).