In this study, the substitution fumigation gases (15% Ethylene Oxide + 85% HFC 134a, 20% Ethylene Oxide + 80% $CO_2$, 99% Sulfuryl Fluoride + 1% Inert Gas) were applied on the metal, pigment, fabric and paper specimen. The result of the fumigation treatment with 15% Ethylene Oxide + 85% HFC 134a (200g/$m^3$, 48hours) is the color changes (${\Delta}E$) of 1st and 2nd Cu specimens showed significant difference as 3.40, 4.17. On the other hand, other specimens except for Cu showed less than 3.0 in chrominance values. The result with 20% Ethylene Oxide + 80% $CO_2$ (150g/$m^3$, 48hours) is that the color changes (${\Delta}E$) of 1st and 2nd specimens were overall less than 3.0 so that color differences were subtle and hardly recognized with naked eyes. So it is proved that the fumigation treatment with Ethylene Oxide 20% + $CO_2$ 80% is relatively stable on materials in this study. In the case of 99% Sulfuryl Fluoride + 1% Inert Gas (50g/$m^3$, 48hours), the color difference of Lead red ($PbO_4$) of pigment was more than 3.0 that was compared with contrast specimens. But chrominance values in the other specimens were less than 3.0 on average.

• Journal of Conservation Science
• /
• v.25 no.3
• /
• pp.283-291
• /
• 2009

Methyl Bromide that was used as fumigation gas turned out to be the substance of destroying the ozone layer. For that reason, at the Montreal Protocol in 1987 the use of methyl bromide was forbidden starting 2005 in the advanced country. Also according to the 2007 Bali Protocolly methyl bromide is expected to be forbidden and therefore the purpose of this study is to find out the effects of substitution fumigation gas (Ethylene Oxide+HFC 134a, Methyl Iodide, Cyanogen and Argon) on the metal(silver, copper and iron), wood(oregon pine), pigment(yellow, red, blue, white and black), textile(hemp, ramie, jute, silk1 and silk2 / indigo, safflower and cork) and paper. After the fumigation test, ethylene oxide+HFC 134a did not have changes in the weight and color of the material itself before and after the experiment. On exterior alteration, color change occurred partly on paper and metal. Also, in most materials color change extent was 0.5 to 1.5 on the average and showed scanty difference. The materials after the fumigation test with methyl iodide did not show weight changes after the test. However, color changes more than 1.0 was shown in most of the materials especially in dyed textile material. In blue pigment, the discoloration on the surface could be seen by naked eyes. Fumigation test with cyanogen gas did not show weight changes and discoloration is more than 1.5 before and after the test. The weight changes of test materials with the argon gas was decreased about 3 to 6%. It can be observed that discoloration on paper was generated. Color changes can be seen on jute dyed with safflower and cork for two weeks with argon gas and the extent was 6.3 and 6.0.