• Journal of the Korean institute of surface engineering
• /
• v.37 no.5
• /
• pp.289-295
• /
• 2004

A dense palladium-nikel (Pd-Ni) alloy composite membrane has been fabricated on microporous nickel support mixed with submicron/micron nickel powder instead of mesoporous stainless steel support. Plasma treatment process is introduced as pre-treatment process instead of HCI activation. Pd-Ni alloy composite membrane prepared by electro plating was fairly a uniform and dense surface morphology. The membrane was characterized by permeation experiments with hydrogen and nitrogen gases at temperature 773 K and pressure 2.2 psi. The results showed that hydrogen ($H_2$) permeance was 27 ml/$\textrm{cm}^2$ㆍatmㆍmin and hydrogen/ nitrogen ($_H2$$N_2$) selectivity was 8 at 773 K.

• Bulletin of the Korean Chemical Society
• /
• v.18 no.6
• /
• pp.612-618
• /
• 1997

$LiMn_2O_4$ powders were prepared by burning and subsequent calcination of PEG-metal nitrate precursor. After the burning stage of the precursor, some minor phases such as $Mn_2O_3$ (or $Mn_3O_4$), MnO, and carbonate were formed and single phases of $LiMn_2O_4$ were obtained by further calcinations above 400 ℃. From thermal analysis of the precursor, a violent thermal decomposition, which was indicated by a drastic weight loss accompanied by a sharp and strong exothermic peak, was observed and probably caused by an oxidation-reduction reaction between oxidizer and fuel. The formation of the minor phases could be explained in terms of the burning behavior of the precursor by employing valence concepts of propellant chemistry. The calcined powders were composed of submicron-sized but highly agglomerated particles and showed very broad particle size distribution.

• Journal of the Korean Ceramic Society
• /
• v.42 no.6 s.277
• /
• pp.432-436
• /
• 2005

Nickel powders synthesized by the reduction of hydrazine of nickel salts fiom diethanolamine(DEA) solution, and investigated the morphological characteristics of nickel powders with the addition of hydrazine, reaction temperature, the composition of mixed solvents. The addition of hydrazine in DEA solution largely affected on size control of nickel powders. Under $N_2H_4/Ni^{2+}$ molar ratio= 1.5 and 2.0 conditions, spherical nickel powders in the submicron range obtained, owing to higher the reduction rate. An increase of temperature increased the size of nickel particles. At $220^{\circ}C$ for 40 min, the nickel powders composed of polyhedral particles with high crystalline in the submicron range. The mixed volume ratio of TEA to DEA affected on the increase of particle size and the inhibition of agglomerate between particles.

• Journal of Powder Materials
• /
• v.24 no.6
• /
• pp.464-471
• /
• 2017

A metal mesh TCE film is fabricated using a series of processes such as UV imprinting of a transparent trench pattern (with a width of $2-5{\mu}m$) onto a PET film, filling it with silver paste, wiping of the surface, and heat-curing the silver paste. In this work nanosized (40-50 nm) silver particles are synthesized and mixed with submicron (250-300 nm)-sized silver particles to prepare silver paste for the fabrication of metal mesh-type TCE films. The filling of these silver pastes into the patterned trench layer is examined using a specially designed filling machine and the rheological testing of the silver pastes. The wiping of the trench layer surface to remove any residual silver paste or particles is tested with various mixture solvents, and ethyl cellosolve acetate (ECA):DI water = 90:10 wt% is found to give the best result. The silver paste with 40-50 nm Ag:250-300 nm Ag in a 10:90 wt% mixture gives the highest electrical conductance. The metal mesh TCE film obtained with this silver paste in an optimized process exhibits a light transmittance of 90.4% and haze at 1.2%, which is suitable for TSP application.

• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.1
• /
• pp.40-46
• /
• 2017

We reviewed the electrical properties of SOFC anode manufactured using spherical Ni and nano YSZ powder. When core-shell is fabricated by using submicron Ni as core and nano-sized YSZ as shell for SOFC anode, the electrical conductivity of the $0.2{\mu}m$ Ni-YSZ core-shell was 3 times higher than that of $1.0{\mu}m$ NiO or $1.0{\mu}m$ Ni-YSZ. Hydrogen selectivity was similar at $800^{\circ}C$, but hydrogen selectivity and methane conversion rate under $750^{\circ}C$ was 10~25% higher, Power density was more than 2 times, ASR was about 1/3, when exposed to $H_2$ atmosphere at $750^{\circ}C$ for a long time, Ni particles did not have any growth or cut off conduction path.

• Journal of Powder Materials
• /
• v.12 no.3
• /
• pp.201-207
• /
• 2005

Nickel powders were synthesized by the hydrazine reduction of nickel chloride solution containing ammonia in DEA solutions. The size distribution of nickel powders were investigated as a function of ammonia concentration, hydrazine concentration and the mixed composition ratio of diethanolammine (DEA) and triethanolammine (TEA). Nickel powders with the size in submicron range were obtained at $185^{\circ}C$ for 45 minutes by hydrazine reduction of nickel chloride solution in DEA solutions. The hydrazine concentrations showed significant effects on the particle size and shape distribution of nickel powders under $NH_3/Ni^{2+}$ molar ratio of 2.0 condition. As the mixed volume ratio of TEA and DEA increased, nickel powders with relatively larger particle size and low agglomeration were obtained. Nickel powders with particle size in the ranged from 0.4 to $0.9\;{\mu}m$ were obtained at the 50 $vol.%$ of TEA.

• Analytical Science and Technology
• /
• v.6 no.2
• /
• pp.197-205
• /
• 1993

Blends of elemental Ni and 20 weight % Cr powder were milled for different period in a laboratory attritor. Powder size distribution, microstructure and X-ray diffraction characteristics were investigated as a function of processing period. Saturated magnetization, Ms and coercive force, Hc we also measured and compared with plasma melted ingot to confirm the mechanically alloyed states. Mechanical alloying occurred as a consequence of the partition of powders and the increase of interfacial area driving diffusing of Cr into Ni. However, magnetic properties of chemically homogeneous solid solution like melted ingot has not been observed even though steady state of submicron grain size has been achieved after milling over 15 hrs. Further mechanical alloying period gave refinement of grain size, which resulted in the increase of alloyed layer. It is concluded that homogenization should be controlled by the increase of interfacial area between constitutive powders caused by plastic particle deformation and by the diffusion of Cr within the alloyed phase into Ni-rich phase through lattice defects.

• Journal of Powder Materials
• /
• v.15 no.6
• /
• pp.482-488
• /
• 2008

The indentation technique has been one of the most commonly used techniques for the measurement of the mechanical properties of materials due to its experimental ease and speed. Recently, the scope of indentation has been enlarged down to the nanometer range through the development of instrumentations capable of continuously measuring load and displacement. In addition to testing hardness, the elastic modulus of submicron area could be measured from an indentation load-displacement (P-h) curve. In this study, the hardness values of the constituent phases in Ti($C_{0.7}N_{0.3}$)-NbC-Ni cermets were evaluated by nanoindentation. SEM observation of the indented surface was indispensable in order to separate the hardness of each constituent phase since the Ti($C_{0.7}N_{0.3}$)-based cermets have relatively inhomogeneous microstructure. The measured values of hardness using nanoindentation were ${\sim}20$ GPa for hard phase and ${\sim}10$ GPa for binder phase. The effect of NbC addition on hardness was not obvious in this work.

• Transactions of the Korean hydrogen and new energy society
• /
• v.23 no.5
• /
• pp.455-460
• /
• 2012

This work describes the hydriding chemical vapor synthesis (HCVS) of the $MgH_2$ in a hydrogen atmosphere and the product's hydriding-dehydridng properties. Mg powder was used as a starting material to synthesize $MgH_2$ and uniformly heated to a temperature of $600^{\circ}C$ for Mg vaporization. The effects of hydrogen pressure on the morphology and the composition of HCVS-$MgH_2$ were examined by using X-ray diffraction (XRD) and scanning electron microscopy (SEM). It is clearly seen that after the HCVS process, the particle size of synthesized $MgH_2$ was drastically reduced to the submicron or micrometer-scale and these showed different shapes (needle-like nanofibers and angulated plate) depending on the hydrogen pressure. It was found that after the HCVS process, the $H_2$ desorption temperature of HCVS-$MgH_2$ decreased from 380 to $410^{\circ}C$, and the minimum hydrogen desorption tempreature of HCVS-$MgH_2$ powder with needle-like shape can be obtained. In addition, the enhanced hydrogen storage performance for needle-like $MgH_2$ was achieved during subsequent hydriding-dehydriding cycles.

• Applied Microscopy
• /
• v.29 no.1
• /
• pp.67-73
• /
• 1999

It is practically hard to prepare good TEM specimens from powders which are embedded in epoxy materials for ion milling, because the milling rate difference between powders and epoxy is quite large. In order to overcome this problem, we tried to find methods to increase the density of powders in the embedding epoxy without loosing the adhesive strength between them. Powder density was considerably increased by employing a centrifuge for embedding, compared to the result by a conventional vacuum embedding. In addition, mixing powders of different sizes after sieving also enhanced the final density by allowing smaller particles filling in the gaps of larger particles. Ion milling of powders embedded by these methods resulted in thin specimens good enough for normal TEM works. TEM specimens from spherical, platy and fibrous powders of submicron size were successfully prepared by this centrifuging method.