• Clean Technology
• /
• v.10 no.2
• /
• pp.111-120
• /
• 2004

Manufacturing with a chemical for eco-friendly leather for nitrogen decrease of leather falling hair process waste water and the falling hair process that a number to decrease with sulfuration water decrease, a pollution load of COD, BOD. In this study manufactured lining agent and the unhairing assist product which did urea, mercaptan by basic matter. As a result of having dealt in hair saving process, compared, and was recalled by the existing hair burning process recovered hair, increased approximately 2times. Grain state to influence the yield that was quality of leather and an index of productivity evaluation, an improvement of contraction phenomenon (drawing) were possible. Is increased going seal, tear strength property of matter and softness and touch leather native nature in wet blue. Also, it is possible confirmation with decrease being more possible than about 50% COD, T-N density in a hair saving waste water.

• Journal of the Korea Concrete Institute
• /
• v.16 no.5 s.83
• /
• pp.651-657
• /
• 2004

The effects of polymer-cement ratio, antifoamer content and shrinkage-reducing agent content on the air content, setting time, drying shrinkage and strength of high-fluidity polymer-modified mortars using redispersible polymer powder are examined. As a result, the air content of the polymer-modified mortars using redispersible polymer powder tends to decrease nth increasing polymer-cement ratio and antifoamer content. Regardless of the antifoamer content, the setting time of the polymer-modified mortars using redispersible polymer powder tends to delayed with increasing polymer-cement ratio. Irrespective of the antifoamer content, the drying shrinkage of the polymer-modified mortars using redispersible polymer powder tend to decrease with increasing polymer-cement ratio and shrinkage-reducing agent content. Regardless of the antifoamer content, the flexural and tensile strengths of the polymer-modified mortars using redispersible polymer powder tends to increase with increasing polymer-cement ratio, and tend to decrease with increasing shrinkage-reducing agent content. However, the compressive strength of the polymer-modified mortars using redispersible polymer powder decreases with increasing polymer-cement ratio and shrinkage-reducing agent content.

• Economic and Environmental Geology
• /
• v.41 no.4
• /
• pp.383-392
• /
• 2008

This study aims to evaluate the mechanical-chemical stability of used coal ash blocks, for improving fishing grounds. The surface of weathered ash blocks in seawater showed a decrease in the Ca and an increase in the Mg contents, compared to that of fresh blocks. This result reflects the substitution of Ca by Mg in seawater. The compressive strengths of ash blocks submerged into seawater during 12 months ranged from 235.23 to $447.43\;kgf/cm^2$; this is higher than the standard strength of wave-absorbing blocks($180\;kgf/cm^2)$ that are used for harbor construction. In addition, the compressive strength of ash blocks tends to increase with increasing installation time in seawater. The result of leaching experiments on coal ash blocks by Korean Standard Leaching Test(KSLT) method showed that leached concentrations of most metals except Cr(that leached up to 50 ppb, approaching standard concentration) do not exceed the seawater quality standards. A long-term(112 days) heavy metal leaching test to analyze seawater without mixing-dilution also showed that the concentrations of leached heavy metals, except for Cu, under anaerobic conditions do not exceed the seawater quality standards. Accordingly, the use of coal ash blocks in marine environments appears to be safe from chemical and mechanical factors that decrease the efficiency of concrete. Also, leaching concentration of Cu seems to be stable by decrease of leaching concentration due to dilution of seawater.

• Journal of Korea Foundry Society
• /
• v.41 no.5
• /
• pp.411-418
• /
• 2021

In order to experimentally investigate the effect of Ni or Cu addition on microstructure and mechanical properties of high Si Solution Strengthened Ferritic Ductile cast Iron (SSF DI), a series of lab-scale sand casting experiment were conducted by changing initial concentration of Ni up to 3.0wt% or Cu up to 0.9wt% in the alloy. It was found that increase in Ni or Cu content in the alloy leads to increase in strength properties and hardness as well as decrease in ductility. The higher Ni or Cu content the SSF DI has, the higher fraction of pearlite was observed. At similar levels of Ni or Cu contents in the alloy, higher pearlite area fraction was observed in the Cu-containing SSF DI than that in the Ni-containing SSF DI. When the effect of the microstructure on the mechanical properties of Ni-containing SSF DI was considered, Ni-containing SSF DI was found to have excellent strength and hardness as well as good elongation when the pearlite fraction was controlled less than 10%. As the pearlite fraction in the Ni-containing SSF DI exceeds 10%, however, it shows drastic decrease in elongation. Meanwhile, gradual increase in strength and hardness, and decrease in elongation with respect to increase in pearlite fraction were observed in Cu-containing SSF DI. The different microstructure-mechanical property relationships between Ni-containing and Cu-containing SSF DI were due to the combined effect of the relatively weak pearlite stabilizing effect of Ni compared to that of Cu in high Si SSF DI, and matrix strengthening effect caused by the different amounts of those alloying elements required for similar pearlite fraction.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.04a
• /
• pp.23-26
• /
• 2003

Solid-state extrusion technique was employed for the improvement of mechanical properties of polylactic acid (PLLA) widely used as biodegradable internal fixation devices currently. Cylindrical billets were machined out from the vacuum compression-molded PLLA to have various diameters, and solid-state extrusion of the billets was performed at various drawing rates and at the extrusion temperature of $130^{\circ}C$. Throughout the whole processes the decrease in molecular weight was significantly suppressed to be about $10\%$. Flexural modulus and strength of PLLA increased up to 8.3 GPa and 221 MPa, respectively. Studies on the orientation and crystallinity of extruded PLLA could reveal the effects of billet morphology, draw ratio, and drawing rate on the flexural strengths of PLLA.

• Elastomers and Composites
• /
• v.3 no.1
• /
• pp.32-38
• /
• 1968

The physical properties of NR-SBR and NR-BR blends were studied. 1. In blending, tensile strength decreased with increase in synthetic rubber contents. It was most effective when the ratio of NR/Syn. R is 75/25. 2. Tensile strength decreased with order of NR, SBR and BR and modulus after aging is proportional of synthetic rubber contents. 3. Elongation is less influenced by synthetic rubber ratio that on the other hand, the decrease of elongation is proportional to synthetic rubber contents after aging. 4. Hardness decreased with increase in the synthetic rubber contents and on the other hand, the hardness increased after aging.

• The Transactions of the Korean Institute of Electrical Engineers B
• /
• v.51 no.5
• /
• pp.221-227
• /
• 2002

This paper deals with the mechanical stress analysis due to electromagnetic forces and the optimal design of the link considering the stress. The link in Interior Permanent Magnet Brushless Motor(IPM) have influence on both mechanical and magnetic performance. The decrease of the link thickness serves to improve the torque, whereas this decreases the strength of link. Therefore, it is necessary to determine the appropriate link thickness considering electromagnetic forces and thermal expansion. The effects of the variation of link thickness on the mechanical stress and the electromagnetic performance are analyzed by the structural and electromagnetic Finite Element Method. In addition, the mechanical structure design of the link is performed to reinforce the mechanical strength against magnetic forces while preserving a food magnetic torque.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.641-646
• /
• 2001

Generally, when Fly-Ash was used as replacement material of cement in concrete, it might occur retardation of setting and hardening. So, it is unable to use a large amount of Fly-Ash as replacement for cement. However, if it is used as replacement material of fine aggregate in concrete, we can use a large amount of Fly-Ash and settle a problem of natural-aggregate exhaustion. Furthermore, engineering properties of High Volume Fly-Ash Concrete Is better than that of plain concrete But, the larger Fly-Ash is replaced, the more fluidity of High Volume Fly-Ash Concrete decrease, because porous organization of Fly-Ash adsorb water and Superplasticizer. In this study, after appending additional water to High Volume Fly-Ash Concrete in proportion to weight of Fly-Ash, we intend to find proper ratio which doesn't affect strength and satisfy fluidity As a result of this study, it was found that fluidity of mortar with 25~28 percentage of additional water was satisfied with fluidity of plain mortar, and compressive strength of that was similar to plain mortar's

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2002.05a
• /
• pp.57-60
• /
• 2002

Recently, the coal ash production has been increased by increase of consumption of electric power. So it is important to find a reclaimed place and treatment utility for treating coal ash. Accordingly, in this study we performed an experimental study to compare and analyze the Properties of concrete according to W/C and bottom ash replacement ratio. As a result of this study, it was found that the bleeding content was decreased according to decrease of W/C and increase of bottom ash replacement ratio, and the compressive strength of concrete using bottom ash was similar to plain concrete(replacement ratio 0%).

• Journal of the korean Society of Automotive Engineers
• /
• v.3 no.3
• /
• pp.30-38
• /
• 1981

The fatigue characteristics of Si-Mn spring steel (AISI 9260-H, JIS SUP-6) were investigated on several heat treatment conditions. Repeated impact loads of 10kg-cm and 15kg-cm energy were applied with a cam roller drop hammer type impact fatigue testing machine. Specimens were oil-quenched, and tempered at 350.deg. C, 450.deg. C and 500.deg. C, respectively. Results obtained in these experiments are summarized as follows.; 1) The fatigue life of the specimen is decreased as the magnitude of constant impact energy is increased, regardless of heat treatment. 2) Generally, the fatigue life of the specimen is decreased as the tensile strength of the materials is increased. 3) Within the limit of these experiments, the fatigue life showed abrupt decrease at the tempering temperature of about 400.deg. C 4) The fatigue life is increased as the initial value of applied stress intensity factor(K$_{1}$) is decreased. This tendency is apparent for the low tensile strength materials.