• Journal of Welding and Joining
• /
• 제21권3호
• /
• pp.78-84
• /
• 2003

The changes of microstructure and hardness of TLP bonds of directionally solidified Ni base superalloy, GTD-111, with variation of homogenizing and aging treatment were investigated. The specimens were bonded at 1403K for 7.2ks using different insert metals such as MBF-50, MBF-80 and MBF-90 and they were homogenized at 1393K with various holding time. At center of bonded interlayer homogenized for hold time 30h, the contents of aluminum and titanium were approximately 90% and 95% of base metal, respectively. In this study, aging was performed at three different kinds : one step aging ; 1113K $\times$ 16h, two step aging ; 1113K $\times$ 10h ⇒ 1103K $\times$ 10h, three step aging ; 1113K $\times$ 10h ⇒ 1103K $\times$ 8h ⇒ 922K $\times$ 24h. ${\gamma}$' volume fraction and hardness of joints were high in the sequence of one step, two step and three step aging, whereas ${\gamma}$' volume fraction and hardness of joints obtained by three step aging treatment were higher than those of raw material. Tensile properties of joints bonded with MBF-80 and MBF-90, homogenized at 1393K for 30h and then three step aged became excellent than those of raw material, however, joint bonded with MBF-50 was poor.

• 열처리공학회지
• /
• 제32권2호
• /
• pp.57-60
• /
• 2019

The impact of two-step treatment on the mechanical properties of the 6061 Al alloy was investigated by testing the hardness and electrical conductance values. After two-step aging treatment, the hardness and electrical conductivity of the alloy was increased, and if the first aging treatment temperature was lower than the secondary aging treatment temperature, both the hardness and the electrical conductivity were not increased. The higher the temperature of the first aging treatment, the higher the hardness. The temperature of the first aging treatment is $175^{\circ}C$, $150^{\circ}C$, $120^{\circ}C$, and the second is $175^{\circ}C$ and $120^{\circ}C$.

• 한국식품저장유통학회지
• /
• 제23권3호
• /
• pp.301-309
• /
• 2016

미숙과의 가공법 제안 및 기능성 규명을 위한 기초 연구의 일환으로 반시 미숙과를 7 step으로 나누어 열처리 숙성하면서 이화학적 특성 및 항산화 활성의 변화를 분석하였다. 반시 미숙과는 숙성됨에 따라 수분함량과 pH는 점차 감소하고, 산도는 증가하는 경향이었다. 숙성이 진행됨에 따라 갈변이 유도되면서 step 3까지 적색도는 급격히 증가하였으며, 황색도는 큰 폭으로 감소하였다. 반시의 탄력성, 씹힘성과 점착성의 경우에는 step 2~3에서 변화한 후에는 유의적인 차이를 보이지 않았다. 숙성 중 반시 미숙과의 fructose의 함량은 감소한데 반해 glucose 함량은 미량 증가하였다. 페놀성 화합물은 gallic acid와 homogentisic acid, 2종이 검출되었는데 이들 화합물은 step 2까지는 검출되지 않았으나, step 3부터 숙성단계가 지남에 따라 함량이 증가하였다. 이와 상반되게 탄닌 함량은 step 1에서 가장 높게 측정되었고 step 2에서 급감하였다. 숙성 단계별 반시 미숙과 물 추출물의 DPPH와 ABTS 라디칼 소거능 및 FRAP법에 따른 항산화 활성은 시료의 농도에 비례하여 유의적으로 증가하였으나, 숙성이 진행될수록 오히려 낮아졌다.

• 한국세라믹학회지
• /
• 제48권4호
• /
• pp.263-268
• /
• 2011

ZnO hexagonal rods grown in aqueous solution can be changed into a tubular shape by two-step aging in the course of the growing process. In the first step, hexagonal ZnO rods is grown by aging at $90^{\circ}C$ under a highly supersaturated aqueous solution giving rise to a fast precipitation rate. Meanwhile, during the second step aging at $60^{\circ}C$ in the same aqueous solution, the hexagonal polar face (001) having higher surface energy than (010) side planes dissolves to minimize surface energy. Hence the flat (001) face changes to a craterlike face and the hexagonal rod length of ZnO decreases at an initial-stage of this step aging. The formation of the (101) wedge-type faces is ascribed to the resultant of competitive reactions between the dissolution of polar face minimizing the surface energy which is a dominant reaction at the initial stage and the precipitation reaction dissipating supersaturation. At a later stage of the second-step the reaction rates of these two processes in the aqueous solution become similar and the overall reaction is terminated.

• 한국공간구조학회논문집
• /
• 제13권4호
• /
• pp.67-74
• /
• 2013

The Age-adjusted effective Modulus Method(AEMM) is one of the methods adopted for the construction stage analysis of concrete structures. The AEMM uses the aging factor to consider the effects of the varying concrete stress. In the aspects of computation time and the accuracy of the results, the AEMM is considered as one of most appropriate methods for construction stage analysis of tall building structures. Previous researches proposed appropriate values of the aging factor in the forms of graphs or using very simple equations. In this paper, an equation for estimating the aging factor as a function of rebar ratio in the section, compressive strength of concrete, notional member dimension, and age of concrete at the load application. The validity of aging factor proposed in this paper were examined by the comparison with the results of step-by step method.

• 한국추진공학회지
• /
• 제24권6호
• /
• pp.101-107
• /
• 2020

본 논문에서는 HTPB/AP 계열의 추진제의 경화 온도를 변화시키는 Step 경화 방법으로 경화일 단축 연구를 진행하였다. 이 연구는 HTPB/AP 계열의 추진기관 제작 시 생산성 향상(제작기간 단축 및 치구회수율 증대)을 목적으로 한다. 정상 경화 대비 추진제의 기계적 물성을 비교하여 정상 경화 시 60℃ 5일 소요되는 경화일을 Step 경화로 4일(60℃ 1일 / 65℃ 3일)로 설정하였다. 경화일 단축을 적용 시 추진제 노화 특성을 알아보기 위해 Step 경화 후 후경화(Post-cure) 시험을 진행하였다. 이를 통해 기계적 물성 및 열팽창 계수를 측정하여 추진제의 후경화 특성을 분석하였다. 또한, Step 경화 후 가속 노화 시험을 진행하여 12주차 경과 후 인장시험을 수행하였다. 그 결과, Sm(bar)은 8 bar 이상, Em(%)은 40%이상으로 요구되는 우수한 기계적 물성을 가지는 것을 알 수 있었다.

• 한국재료학회지
• /
• 제10권7호
• /
• pp.493-498
• /
• 2000

7050 AI합금을 RRA 처리하였을 때 경도, 전기전도도 및 미세조직의 변화를 조사하였다. 120도씨에서 24시간 동안 1차 시효처리한 후 175도씨에서 2차 퇴화처리하였을 때 경도값의 변화는 초기에 감소하다가 피크 경도를 보인 다음 다시 감소하였으며, 3차 재시효처리재가 2차 시효처리재 보다 큰 경도값을 나타내었다. 2차 퇴화처리시 초기 경도 감소는 T6의 주 강화상인 GP zone의 부분적인 분해에 의한 것이며, 3차 재시효 처리하였을 때 강화상은 GP zone과 파이상이었다. 120도씨에서 24시간 동안 1차 시효처리한 후 175도씨에서 2차 퇴화처리하였을 때 전기전도도 변화는 퇴화 쵤부터 연속적으로 증가혀였으며, 3차 재시효처리에 의해 2차 퇴화처리시 보다 %IACS가 0.5 ~ 2.7 증가하였다. 3단시효에 의해 T6정도의 강도를 유지하면서 38%IACS값 이상의 전기전도도를 얻을 수 있는 최적 퇴화처리 조건은 $175^{\circ}C$ 50분이었다. 이는 퇴화처리 경도곡선의 극소점 또는 극대점과 무관하며 오히려 약간 과시효 조건이다.

• 대한금속재료학회지
• /
• 제49권1호
• /
• pp.9-16
• /
• 2011

To develop a 6061 aluminum alloy with low residual stress and high tensile strength, a cryogenic treatment process was investigated. Compared to the conventional heat treatment process for precipitation hardening with artificial aging, the cryogenic treatment process has two additional steps. The first step is cryogenic quenching of the sample into liquid nitrogen, the second step is up-hill quenching of the sample into boiling water. The residual stress for the sample was measured by the $sin^2{\psi}$ method with X-ray diffraction. The 6061 aluminum alloy sample showed 67% relief in stress at the cryogenic treatment process with artificial aging at $175^{\circ}C$. From this study, it was found that the optimum cryogenic treatment process for a sample with low residual stress and high tensile strength is relatively low cooling speed in the cryogenic quenching step and a very high heating speed in the up-hill quenching step.

• 한국세라믹학회지
• /
• 제40권2호
• /
• pp.132-138
• /
• 2003

출발물질의 종류와 몰비 혼합 방법, 숙성, 결정화 온도와 결정화 시간 등 제올라이트 입자를 합성하는 조건이 FAU 형 제올라이트의 입자크기에 미치는 영향을 연구하였다. 동일한 출발물질이라도 혼합 경로에 따라 생성물의 결정상이 달랐다. 일반적으로 숙성과정을 거친 경우, 특히 숙성온도가 낮은 쪽이 입자 크기가 작았다. 2단계의 혼합겔 제조 방법을 거치는 경우 결정화 기간은 크게 단축되고 입자 크기도 작아졌으나. 1단계에서 제조된 2종의 혼합겔을 모두 숙성하지 않는 경우에는 결정화 시간은 단축되지만, 입자크기는 작아지지 않았다. 액상규산나트륨과 알루민산나트륨, 수산화나트륨을 출발물질로 하여. 저농도와 고농도의 혼합겔을 1차 제조하고, 이 혼합겔을 각각 숙성하고 다시 혼합하여 숙성하는 방법으로 결정화 시간을 단축하고 평균입경 0.4$\mu$m. 비표면적 838 $m^2$/g의 우수한 특성을 가지는 FAU혈 제올라이트를 합성하였다.

• 한국재료학회지
• /
• 제9권7호
• /
• pp.695-700
• /
• 1999

7050 Al합금의 응력부식저항성에 미치는 2단 시효처리의 영향을 미세조직관찰, 전기전도도시험 및 SCF값을 평가함으로써 조사하였다. 최대 경도 이상 과시효에 의해 주 강화상인 η'상이 η상으로 변태되었고, 입내 및 입계에 존재하는 η상의 크기와 간격이 커졌으며 그 결과 응력부식저항성이 증대되었다. 2차 시효시간의 증가에 따라 전기전도도값은 증가되었으나 항복강도의 감소로 인하여 SCF값은 감소되었는데, 이러한 결과는 응력부식저항성의 증가를 의미한다. AMS 4107규격을 기준으로 하였을 때 7050 Al합금 단조재의 적정시효조건은 1차시효가 12$0^{\circ}C$에서 6시간, 2차시효는 $175^{\circ}C$에서 12시간이었다.