• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.9 no.4
• /
• pp.48-55
• /
• 2000

For the Tailor Welded Blank sheet used for automobile body panel, the characteristics of fatigue strength and crack propagation behavior were studied. The thickness of specimens was joined to be same (0.9mm+0.9mm) and different (0.9mm+2.0mm) .As a base test, mechanical properties around weld zone were examined . The results indicated that there were no significant decreases in mechanical properties , but hardness around weld bead was 2.3 times greater than base material . The fatigue strength was the highest when the loading direction was parallel to the welding direction, which was about 85% of tensile strength of base material. It was decreased by 8.5% when the thickness of specimens and base metal was different, and it was increased by 25% when pres-strain was applied. The crack propagation rate was noticeably decreased around weld line and rapidly increased as it passed through weld line. Reviewing the shape of the crack propagation , crack width around weld line was around the weld zone due to retardation of crack growth , but is became narrow passing weld line due to decreased toughness.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.6
• /
• pp.455-459
• /
• 2001

In this paper, the dielectric and pizoelectric properties of 0.05Pb(M $n_{04}$ $W_{0.2}$N $b_{0.4}$) $O_3$-0.95(PbZ $r_{x}$ $Ti_{1-x}$ ) $O_3$+yN $b_2$ $O_{5}$ , are investigated as a function of the mole ratio of Zr and the amount of N $b_2$ $O_{5}$ . Also, the phase is analyzed by XRD. When the mole ratio of Zr is 0.51, the electromechanical coupling coefficient( $k_{p}$ ), relative dielectric constant ($\varepsilon$$^{T}$ $_{33}$ /$\varepsilon$$_{0}$ ), piezoelectric stain constrain ( $d_{33}$ and dielectric loss tangent show maximum, while the mechanical quality factor shows minimum value ; $k_{p}$ =56.5%, $d_{33}$ =258pC/N, $\varepsilon$$^{T}$ $_{33}$ /$\varepsilon$$_{0}$ =1170, $Q_{m}$ =1150, tan$\delta$=0.51%. At that composition, MPB which rhombohedral and tetragonal phase coexist in this ternary system is shown by the results of XRD analysis. Also, when the amount of N $b_2$ $O_{5}$ is 0.3wt%, the mechanical quality factor is increased to about 2000. The phase transition temperature of the ternary piezoelectric ceramic system showed about 35$0^{\circ}C$.TEX>.>.>.