• Restorative Dentistry and Endodontics
• /
• 제22권1호
• /
• pp.1-33
• /
• 1997

The objective of this study was to analyze the in vitro and in vivo corrosion products of low and high copper amalgams. The four different types of amalgam alloy used in this study were Fine cut, Caulk spherical, Dispersalloy, and Tytin. After each amalgam alloy and Hg were triturated according to the directions of the manufacturer by means of the mechanical amalgamator(Amalgam mixer. Shinhung Co. Korea), the triturated mass was inserted into a cylindrical metal mold which was 12mm in diameter and 10mm in height. The mass was condensed by 150Kg/cm compressive force. The specimen was removed from the mold and aged at room temperature for about seven days. The standard surface preparation was routinely carried out by emery paper polishing under running water. In vitro amalgam specimens were potentiostatically polarized ten times in a normal saline solution at $37^{\circ}C$(potentiostat : HA-301. Hukuto Denko Corp. Japan). Each specimen was subjected to anodic polarization scan within the potential range -1700mV to+400mV(SCE). After corrosion tests, anodic polarization curves and corrosion potentials were obtained. The amount of component elements dissolved from amalgams into solution was measured three times by ICP AES(Inductive Coupled Plasma Atomic Emission Spectrometry: Plasma 40. Perkim Elmer Co. U.S.A.). The four different types of amalgam were filled in occlusal and buccal class I cavities of four human 3rd molars. After about five years the restorations were carefully removed after tooth extraction to preserve the structural details including the deteriorated margins. The occlusal surface, amalgam-tooth interface and the fractured surface of in vivo amalgam corrosion products were analyzed. In vivo and in vitro amalgam specimens were examined and analyzed metallographically by SEM(Scanning Electron Microscope: JSM 840. Jeol Co. Japan) and EDAX(Energy Dispersive Micro X-ray Analyser: JSM 840. Jeol Co. Japan). 1. The following results are obtained from in vitro corrosion tests. 1) Corrosion potentials of all amalgams became more noble after ten times passing through the in vitro corrosion test compared to first time. 2) After times through the test, released Cu concentration in saline solution was almost equal but highest in Fine cut. Ag and Hg ion concentration was highest in Caulk spherical and Sn was highest in Dispersalloy. 3) Analyses of surface corrosion products in vitro reveal the following results. a)The corroded surface of Caulk spherical has Na-Sn-Cl containing clusters of $5{\mu}m$ needle-like crystals and oval shapes of Sn-Cl phase, polyhedral Sn oxide phase. b)In Fine cut, there appeared to be a large Sn containing phase, surrounded by many Cu-Sn phases of $1{\mu}m$ granular shapes. c)Dispersalloy was covered by a thick reticular layer which contained Zn-Cl phase. d)In Tytin, a very thin, corroded layer had formed with irregularly growing Sn-Cl phases that looked like a stack of plates. 2. The following results are obtained by an analysis of in vivo amalgam corrosion products. 1) Occlusal surfaces of all amalgams were covered by thick amorphous layers containing Ca-P elements which were abraded by occlusal force. 2) In tooth-amalgam interface, Ca-P containing products were examined in all amalgams but were most clearly seen in low copper amalgams. 3) Sn oxide appeared as a polyhedral shape in internal space in Caulk spherical and Fine cut. 4) Apical pyramidal shaped Sn oxide and curved plate-like Sn-Cl phases resulted in Dispersalloy. 5) In Tytin, Sn oxide and Sn hydroxide were not seen but polyhedral Ag-Hg phase crystal appeared in internal space which assumed a ${\beta}_l$ phase.

• 한국결정학회지
• /
• 제7권1호
• /
• pp.8-19
• /
• 1996

콜레스테롤 메틸카보네이트와 프로필카보네이트의 결정구조를 X-선 회절법으로 연구하였다. 이 결정들은 단사정계이고 공간군은 P21이다. 회절반점들의 세기는 흑연 단색화 장치가 있는 Enraf-Nonius CAD-4 X-선 회절계로 얻었으며, Cu-Kα X-선(λ=1.5418Å)을 사용하였다. 콜레스테롤 메틸카보네이트의 단위세포 길이 a=17.014(1), b=7.682(1), c=10.612(1)Å이며, β=103.05(1)°, Z=2이다. 한편 콜레스테롤 프로필카보네이트의 단위세포길이는 a=13.683(1), b=11.864(2), c=18.904(2)Å이며, β=106.30(1)°, Z=4이다. 분자구조들은 직접법으로 풀었으며 최소자승법으로 정밀화하였다. 최종신뢰도 R값은 메틸카보네이트는 2323개의 회절반점에 대하여 0.051이고, 프로필카보네이트는 3323개의 회절반점에 대하여 0.074이다. 이들 화합물들의 콜레스테롤부분의 분자구조들은 다른 관련 화합물에서 밝혀진 구조와 잘 일치하고 있다. 이의 두 화합물을 포함하여 콜레스테롤 카보네이트들의 결정구조들은 단분자층을 이루면서 쌓여 있어서 독특한 결정구조를 보여주며 같은 계열의 알킬 카보네이트들과 일련의 유사한 결정구조의 구룹들을 보여준다. 콜레스테롤 메틸카보네이트 분자들은 monolayer를 이루면서 쌓여있으며, monolayer 중심부에서는 cholesteryl-C(17) side chain 상호작용이 강하며 layer 사이에는 카보네이트사슬들이 느슨하게 모여있다. 프로필카보네이트 결정에서는 두 개의 결정학적으로 독립된 분자들(A and B)이 있다. A분자들간의 cholesterol-cholesterol상호작용과 B분자들간의 cholesteryl-C(17) side chain 상호작용들이 layer의 중심부에서 일어나며, 이들 분자들은 나사축 방향을 따라서 쌓여있다. 콜레스테롤 카보네이트의 구조들은 액체결정 상태의 특질을 가지고 있고, 이런 성질들을 결정구조와 관련하여 논의하였다.

• 한국기록관리학회지
• /
• 제5권2호
• /
• pp.27-48
• /
• 2005

이 논문은 한국의 세계기록유산에 대하여 먼저 그 의미와 가치를 재확인하고, 이들 세계기록유산에 대한 보존 관리 및 그 현황을 조사하며, 한국의 기록유산을 디지털화 하는데 있어서의 문제점과 해결책을 모색하고, 추후 한국의 기록유산 중 세계기록유산으로 등록되기를 희망하는 4종의 기록물들에 대한 가치와 의의를 고찰한 연구이다. 본 연구의 상세 사항은 다음과 같다. 첫째, 제2장에서는 한국의 세계기록유산에 대한 가치와 의의를 고찰하였다. 먼저 세계기록유산의 선정기준과 절차 등을 먼저 파악하고, 한국의 세계기록유산인 "훈민정음" "조선왕조실록" "승정원일기" "직지(백운화상초록불조직지심체요절(白雲和尙抄錄佛祖直指心體要節))"에 대하여 각각 그 가치와 의미를 분석하였다. 둘째, 제3장에서는 '한국의 세계기록유산 보존 관리 현황'에서는 세계기록유산을 보존하고 있는 <서울대학교 규장각> <국가기록원 부산기록정보센터> <간송미술관>의 기관별로 그 보존 관리 현황을 고찰하였다. 그 결과, 이 3기관 모두 세계기록유산 보존 관리 현황은 '매우 우수하다'고 평가할 수 있었다. 즉, 1)그 세부적인 보안대책이 완벽하다. 2)그 보존방법에 있어서도 항온 항습의 특별한 서고를 별도로 마련하고, 이 서고 내에서 다시 '오동나무 상자 서장(書欌)'을 설치한 후, 이들 상자와 서장 속에 세계기록유산을 납입하여 보존하고 있다. 3)방화장치와 서고조명 및 소독 등에도 철저를 기하고 있음 등을 파악하였다. 셋째, 제4장에서는 '한국의 기록유산 디지털화 과제'에 대하여 개괄적으로 고찰하였다. 그 결과, 한국 기록유산의 디지털작업 및 DB구축에서 '디지털화 표준'이 가장 중요한 문제이며, 이 문제의 해결을 위해서는 디지털화(Digitization)에 대한 총체적이고 표준적인 시스템의 개발이 시급함을 지적하였다. 그리고 국가기록관리시스템을 개발한 경험이 있는 <국가기록원>과 한국학 고기록물의 디지털화에 많은 관심을 가진 <문화재청>이 공동으로 노력하여, 한국학 관련 기록유산의 디지타이제이션(Digitization)에 대한 총체적이고 표준적인 시스템의 개발이 요구됨을 파악하였다. 넷째, 제5장 '세계기록유산 등록을 추후 희망하는 한국의 기록유산'에서는 한민족의 기록유산 중에서 차후 세계기록유산으로 등재되기를 희망하는 4종 즉, 1)<해인사 고려대장경 경판>, 2)"동의보감", 3)"삼국유사", 4)"무구정광대다라니경"의 기록물에 국한하여, 그 어떤 의미에서 세계적인 가치와 의의가 있는가를 고찰하였다.