• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.153-156
• /
• 2001

(Ba$_{0.6-x}$Sr$_{0.4}$Ca$_{x}$)TiO$_3$ (x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their dielectric properties were investigated with variation of composition ratio, doped ZrO$_2$ (0.5, 1.0, 1.5, 2.0, 3.0 wt%) and sintered at 145$0^{\circ}C$. The dielectric constant and loss of the x=0.10 specimen applied field were 19.86 and 0.302 % at 0 V/cm, and 25.937 and 0.339 % at 300 V/cm, respectively. Dielectric constant were increased with increased applied field and decreased with increased frequency, and dielectric loss were within 0.1% at applied 800 MHz, respectively. all specimens showed fairly good applied field. Although, dielectric constant and loss of all specimen showed to tend of nearly the same. same.

• Journal of Magnetics
• /
• v.16 no.2
• /
• pp.186-191
• /
• 2011

[ $YBa_2C_3O_{7-x}$ ]films were fabricated on a $SrTiO_3$ (100) substrate using a trimethylaceate propionic acid (TMAP)-based MOD process by controlling the precursor solution viscosity, firing temperature, and by using various coatings. The viscosity of the precursor solution was controlled by the addition of Xylenes. The films were heat treated with different temperatures from 750 to $800^{\circ}C$. c-axis oriented films were obtained. After adding 9 ml of Xylene into the precursor solution, the $T_c$ of the YBCO film, which was coated 2 times and heat treated at $800^{\circ}C$, was 86 K and the measured $J_c$ was above 2.5 MA/$cm^2$ at 77 K in a zero-field.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.31 no.1
• /
• pp.19-23
• /
• 2018

In a Pb-included piezoelectric composition, $Sr_yPb_{1-y}[(Zn_{1/3}Nb_{2/3})_x-(Ni_{1/3}Nb_{2/3})_{0.2}-(Zr_{0.46}Ti_{0.54})_{0.8-x}]O_3$ was selected in order to attain high piezoelectric properties. According to the PZN ratio (x) and the amount of Sr doping (y), the crystal structure, microstructure and piezoelectric properties were measured and evaluated. In the case of Sr 4 mol% doping, the piezoelectric properties were the highest for a PZN ratio of 0.1. In this condition, the grain size was larger and the intensity was higher. With the PZN ratio fixed and varying the Sr doping, the piezoelectric properties increased until 10 mol% doping and then decreased for over 12 mol% doping. In the case of x＝0.1 and y＝10 mol%, the best piezoelectric properties were obtained, i.e., $d_{33}=660pC/N$ and $k_p=68.5%$, and these values seem to be related to the grain size and crystal structure.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1999.07a
• /
• pp.87-87
• /
• 1999

본 연구에서는 Pulsed Laser Deposition(이하 PDL)방법을 이용하여 Si기판에 (Ba,Sr)TiO3(이하 BST)박막을 MFS-FET(Metal-Ferroelectric-Semiconductor Field-effect Transistor)구조로 제조하였으며 BST박막의 강유전성이 BST 박막에 유도되는 응력에 어떤 영향을 받는지 살펴보았다. 본 연구에서는 완충막을 사용함으로써 BST박막과 완충막간의 격자부정합을 이용하여 BST박막에 강유전성을 유도하려고 하였다. 또한 MFS-FET구조의 BST박막에 유도되는 응력조절을 위하여 BST박막과 완충막의 두께를 변화하였으며 XRD를 통한 구조 분석 및 C-V test를 통한 전기적 특성을 관찰을 하였다. PLD법을 통해서 epitaxial 성장된 BST 박막에서는 Si에 epitaxial 성장된 완충막과의 격자부정합에 의한 BST박막내의 자발분극의 발생이 예상된다. 따라서, 본 연구는 강유전체의 자발분극에 의하여 발생되는 C-V 이력현상이 BST박막과 완충막과의 격자부정합에 의한 응력에 의해 발생될 것으로 예상하여, BST 박막에 유도되는 응력과 C-V 이력현상의 관계를 통하여 상온에서 상유전성을 갖는 BST가 응력에 의하여 어느 정도의 강유전성을 나타내는지를 밝히기 위해 진행되었다. 본 연구에서 사용된 완충막은 YSZ(Yttria Stabilized Zirconia)박막으로 0.4mTorrO2 분위기 하에서 600~80$0^{\circ}C$의 온도에서 증착하여 상형성을 살펴보았고 $700^{\circ}C$에서 epitaxial 성장을 확인하였으며 두께는 30~$\AA$으로 변화하였다. 또한 BST박막은 완충막과의 전압분배를 고려해 300~2000$\AA$으로 두께를 변화를 시키며 증착하였다. MFS 구조에서 Al 전극을 사용하여 완충막과 BST박막간의 두께 변화에 따른 Capacitance - Voltage(C-V) 측정을 하였으며 이를 통하여 강유전상의 특성인 C-V 이력현상을 관찰하였다. 그 결과 YSZ 박막에서는 C-V 이력현상이 나타나지 않았으며 BST 박막에서는 약 1.2V의 C-V이력현상이 보였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.171-174
• /
• 2002

The barium strontium titannate (BST) thin films were etched in $CF_{4}/Ar$ inductively coupled plasma (ICP). The high etch rate obtained at a $CF_{4}(20%)/Ar(80%)$ and the etch rate in pure argon was twice higher than that in pure $CF_{4}$. This indicated that BST etching is sputter dominant process. It is impossible to avoid plasma-induced damages by the energetic particles in the plasma and the nonvolatile etch products. The plasma damages were evaluated in terms of leakage current density, residues on the etched sample, and the changes of roughness. After the BST thin films exposed in the plasma, the leakage current density and roughness increases. In addition, there are appeared a nonvolatile etch byproductsand from the result of X-ray photoelectron spectroscopy (XPS). After annealing at ${600^{\circ}C}$ for 10 min in $O_{2}$ ambient, the increased leakage current density, roughness and nonvolatile etch byproducts reduced. From the this results, the plasma induced damage recovered by annealing process owing to the relaxation of lattice mismatches by Ar ions and the desorption of metal fluorides in high temperature.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.11
• /
• pp.1178-1185
• /
• 2004

In the atmosphere of $N_2$ gas, BaZ $r_{0.08}$ $Ti_{0.92}$ $O_3$ polycrystal was grown by floating zone technique using BaZ $r_{0.08}$ $Ti_{0.92}$ $O_3$ ceramics as a feed and SrTi $O_3$(1l0) single cystal as a seed. The dielectric constant and loss at 10 kHz, 100 kHz, and 1 MHz for the as-grown sample were measured as a function of temperature in the temperature range between -10$0^{\circ}C$ and 150 $^{\circ}C$ to find a dielectric peak with frequency dispersion at Curie point. The hysteresis loop showed that the grown sample had very small polarization which was 0-0.01 $\mu$C/$\textrm{cm}^2$ for the applied dc-electric fields from -7 kV/cm to +7 kV/cm. However, the normal hysteresis loop was appeared after oxygen annealing. The electric-field dependence of the dielectric constant for both the as-grown and the post-annealed samples was studied by measuring the dielectric constants as a function of the biased-electric fields and their tunability was figured out from it at room temperature(27 $^{\circ}C$) and cryotemperature( -73$^{\circ}C$). Tunability for the as-grown sample was 51 % and the figure of merit 20.4 at 10kHz with the biased electric-field of 12 kV/cm. The tunability for the grown sample may be increased up to 80 % if the electric field of 25 kV/cm is applied. Tunability for the post-annealed sample was 41 % and the figure of merit 10.3 at 10 kHz with the biased electric-field of 12 kV /cm. Post-annealing improved the crystallinity of the as-grown sample but decreased its tunability.ability.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 1999.02a
• /
• pp.3-9
• /
• 1999

The grain morphology, the changes in morphology and Jc with the thermo-mechanical treatment (TMT) history, the field dependence of Jc and the nature of intergranular bonding were studied in $T_{10.8}$$Pb_{.2}$$Bi_{0.2}$$Sr_{1.8}$$Ba_{0.2}$$Ca_{2.2}$$Cu_{3}$$O_{z}$/Ag tapes. As a result, incorporation of intermediate rolling during the final heat-treatment resulted in of plate-like TI-1223 grains, and thus enhanced Jc. Jc's near 2.5$\times$104 A/cm2 at 77 K and 0 T were obtained in just rolled tapes with an excellent reproducibility. The high Jc's seem to grain-connectivity easy recovery of excellent grain-connectivity during final heat-treatment after inter -mediate rolling, probably due to retarded T1 evaporation and excessive Ca content in the present composition. The strong field dependence of Jc even in low fields, however, indicated that there still existed significant weak-links and the degree of directional grain-alignment was far from the desired one. The intergranular binding in the tapes seemed to be mainly dominated by SIS junctions.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.151.1-151.1
• /
• 2016

Complex oxide heterointerfaces have been extensively explored in the past due to the novel phenomenon emerging at such interfaces that differ from their individual bulk counterparts. The integration of a ferromagnetic (FM) material with the superconducting (SC) material leading to proximity effect is one of the commonly studied phenomenon in these heterostructures. In continuation, we have stabilized the FM layer La0.7Ca0.3MnO3 (LCMO) on SC material YBa2Cu3O7-${\delta}$ (YBCO) using pulsed laser deposition technique and explored the structural, magnetic, electrical and magneto-transport properties of this heterostructure. ${\Phi}$-scan measurements confirm the epitaxial nature of LCMO/YBCO heterostructure grown on single crystalline SrTiO3 substrate. The FM transition of LCMO and SC transition of YBCO are observed in the magnetization measurements of the bilayer structure. Through electrical measurements, we understood that the proximity effect leads to lowering of the SC transition of YBCO. The role of interface in the bilayer structure is also realized through electrical transport measurements.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2009.08a
• /
• pp.137-137
• /
• 2009

• Transactions on Electrical and Electronic Materials
• /
• v.4 no.4
• /
• pp.10-12
• /
• 2003

NBCO thin films have been fabricated by magnetron sputtering technique on heated $SrTiO_3$ substrates. The oxidation and crystallization of the films were strongly dependent on the distance between the targets and the substrate, as well as on the oxygen partial pressure. The critical temperatures were above 80K for the films prepared under the condition of a small target to substrate gap, in spite of a very low oxygen pressure of 0.2Pa. The results suggest the importance of the activated oxygen uptake into the films during sputtering.