• Journal of Korea Foundry Society
• /
• v.17 no.5
• /
• pp.502-509
• /
• 1997

The mechanical behavior and microstructural evolution in the ignition-proof Mg-Zn-Ca-Zr alloy produced by the semisolid squeeze casting are clarified and the mechanical properties are also compared with those of squeeze cast Mg-Zn-Ca-Zr alloy. The tensile strength and elongation increase slightly as the solid fraction depending on temperature decreases, while the 0.2% proof stress decreases. The size of primary crystal increases with increasing holding time. The tensile strength and 0.2% proof stress of the semi-solid squeeze cast Mg-Zn-Ca-Zr alloy decrease as the size of primary crystal increases, indicating the dependence of strength on the size of primary crystal. The elongation of the semi-solid squeeze cast Mg-Zn-Ca-Zr alloy is two times as large as the squeeze cast Mg-Zn-Ca-Zr alloy and the tensile strength is unchanged despite the growth of primary crystal, resulting from the refining of the melted ${\alpha}Mg$ phase and the brittle eutectic compound as well as the reduction of solidification shrinkage and porosities.

• Journal of Korea Foundry Society
• /
• v.19 no.1
• /
• pp.47-53
• /
• 1999

Squeeze casting process has been used in the field of a commercial manufacturing method, in which metal is enforcedly solidified under pressure enough to prevent the cast defects such as either gas porosity or shrinkage defect. In this paper, to clarify the relationship between applied pressures and macro ${\cdot}$ microstructural behaviors in gravity and direct squeeze casts, specimens were cast by various squeezing pressures during solidification of 7000 series Al wrought alloy in the metal die designed specially. The applied pressures used in this study were 0, 25, 50, and 75 MPa. The microstructural morphologies of squeeze cast were more fine and dense with increasing the applied pressures, because of the greater solidification rate of billet resulting from the applied pressure. A normal segregation phenomenon of an increasing in amount of eutectics towards the center of the billet was observed for squeeze casts, whereas gravity cast showed an inverse segregation phenomenon of an increasing in amount of eutectics towards the edge in the billet. This change in segregation pattern which is normal or inverse is due to a higher radial temperature gradient and reduced time in the semi solid state for squeeze casting.

• Journal of Korea Foundry Society
• /
• v.12 no.3
• /
• pp.238-247
• /
• 1992

A carbon fiber(CF) reinforced Cu-10%Sn alloy matrix composite was successfully fabricated by squeeze casting method employing preheated graphite mold and proper process controlling factors. The matrix solidification microstructure of the Cu-10%Sn/CF composite reveals ${\alpha}-dendrite$ and ${\alpha}+{\delta}$ eutectoid. To compare the squeeze cast Cu-10%Sn/CF compostie with PM route fabricated Cu-graphite composites for electric contact material, mechanical wear and electrical arc wear tests were performed. Mechanical wear rate of the Cu-10%Sn/CF is much lower than that of the Cu-graphite composite. Weight loss with a variation of contact number in electrical arc wear tests shows a similar trend between the squeeze cast Cu-10%Sn/CF and PM Cu-graphite composites.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2000.04a
• /
• pp.109-115
• /
• 2000

In the present study, (10%$Al_2O_3$+5%Si)/AZ91 Mg hybrid composite was fabricated using the squeeze casting method. During squeeze casting, molten Mg was infiltrated into the preform of 10%$Al_2O_3$+5%Si and reaction product of $Mg_2Si$ intermetallic compound was formed by the reaction between molten Mg and Si powder. Microstructure has been observed and mechanical properties were evaluated for the reaction squeeze cast (RSC) hybrid composite. It was found that Si powder totally reacted with molten Mg to form $Mg_2Si$. Reinforcement ($Al_2O_3$) and the reaction product ($Mg_2Si$) are fairly uniformly distributed in Mg matrix for the squeeze cast hybrid composite. Mechanical properties were improved with hybridization of reinforcements, namely higher hardness and enhanced wear resistance comparing squeeze cast (15%$Al_2O_3$)/AZ91 Mg composite.

• Journal of Korea Foundry Society
• /
• v.19 no.6
• /
• pp.484-492
• /
• 1999

The microstructures and mechanical properties of high strength yellow brass, Al bronze and Sn bronze alloys fabricated by gravity die casting and squeeze casting were investigated. A rapid cooling of casting was enhanced by pressure applied during solidification of Cu alloys, the cooling rate of casting was more great for high strength yellow brass alloy than other Cu alloys. Grain size and phases of the squeeze cast products become refined to 1/2 level compared to gravity die castings. Squeeze cast Al bronze and high strength yellow brass has about 10-20% higher yield and tensile strength and slighter decreased or nearly same elongation, compared to gravity die cast ones. Sn bronze has nearly same strength and hardness, but shows increased in elongation, compared to gravity die cast ones.

• Journal of Korea Foundry Society
• /
• v.11 no.3
• /
• pp.208-216
• /
• 1991

The solidification behavior of the squeeze cast composites of aluminum alloys reinforced with boron fiber($100{\mu}m$) and silicon carbide fibers($140{\mu}m$ and $15{\mu}m$) were investigated. Al-4.5wt%Cu and Al-l0wt%Mg were chosen for the matrix phase of the composites. In the squeeze cast specimen with high thermal difference between fiber and melt, the average secondary dendrite arm spacing(DAS) in reinforced alloy is smaller than that in unreinforced alloy. It was also observed that primary ${\alpha}$ and non-equilibrium eutectic, which seems to be penetrated and solidified at the final stage of the solidification of the matrix, are irregularly distributed around fibers. It is considered that cold fibers serve as heterogeneous nucleation site. While in the remelted and resolidified specimen without temperature difference, the DAS was not changed with reinforcement and microstructure reveals non-equilibrium eutectic with relatively uniform thickness around fibers. It might be evident the nucleation starts at interfiber region. Microsegregation decreases with the decrease in cooling rate and with reinforcement in the as-squeeze cast specimen. Al-10wt% Mg alloy shows less microsegregation than Al-4.5wt%Cu alloy.

• Journal of Korea Foundry Society
• /
• v.20 no.1
• /
• pp.13-20
• /
• 2000

In the present study,($10%Al_2O_3+5%Si$)/AZ91 Mg hybrid composite was fabricated using the squeeze casting method. During squeeze casting, Molten Mg was infiltrated into the preform of $10%Al_2O_3+5%Si$ and reaction product of $Mg_2Si$ intermetallic compound was formed by the reaction between molten Mg and Si Powder. Microstructure has been observed and mechanical properties were evaluated for the reaction squeeze cast(RSC) hybrid composite. It was found that Si powder totally reacted with molten Mg to form $Mg_2Si$. Reinforcement($Al_2O_3$) and the reaction product ($Mg_2Si$) are fairly uniformly distributed in Mg Matrix for the squeeze cast hybrid composite. Mechanical Properties were improved with hybridization of reinforcements, namely higher hardness and enhanced wear resistance comparing squeeze cast($15%Al_2O_3$)/AZ91 Mg composite.

• Journal of Korea Foundry Society
• /
• v.21 no.2
• /
• pp.127-134
• /
• 2001

Misch metal (rare earth element, Ce, La, Nd, Pr) which has large influence on high-temperature stability and toughness was added to the Al-5%Ni-5%Mg alloy, and squeeze casting was used for Al-5%Ni-5%Mg-(Mm) alloys. The effect of applied pressure and misch metal additions on mechanical properties in Al-5%Ni-5%Mg alloy by direct squeeze casting has been investigated. The applied pressure were 0 MPa(gravity casting), 25, 50 and 75 MPa. Squeeze-cast Al-5%Ni-5%Mg-(Mm) alloys had better mechanical properties than those of non-pressurized cast alloys because of the increased cooling rate by the application of pressure during solidification. By the addition of misch metal in Al-5%Ni-5%Mg alloy, better combination of strength and elongation was obtained. The addition of 0.3%Mm in Al-5%Ni-5%Mg alloy improved the heat resistant property due to the formation of fine eutectic phases.

• Journal of Korea Foundry Society
• /
• v.13 no.1
• /
• pp.71-80
• /
• 1993

Squeeze casting has advantages to improve mechanical properties of nonferrous castings without losing high productivity. Sound pore free structure makes it possible to be subjected to heat treatment and welding. This process became popular to produce lighter automobile parts alternating cast iron parts. It has, however, two disadvantages of segregation and scattered structure due to the solidified layers in sleeve. In this study segregation behavior of squeeze cast Al-7%Si-0.3%Mg alloy bars was investigated using HVSC machine under various injection conditions. Degree of segregation decreased with injection pressure and effect of injection velocity on it was small. Segregation mode of solute was strongly governed by solidification mode and flow pattern.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.1
• /
• pp.1-8
• /
• 1999

This study has investigated the effect of aging treatment on the microstructure and mechanical properties of Mg-6Al-xZn(x = 1.5, 2.5) alloys fabricated by the squeeze casting process. The microstructures of as-squeeze cast were composed of pro-eutectic ${\alpha}$, super saturated ${\alpha}$ and ${\beta}(Mg_{17}Al_{12})$ compound. Aged at both $200^{\circ}C$ and $240^{\circ}C$, Mg-6Al-xZn alloys showed the peak hardness due to the formation of ${\beta}(Mg_{17}Al_{12})$ precipitates. The discontinuous precipitates of the lamella type are predominant at $200^{\circ}C$ aging treatment, while the finely dispersed continuous precipitates were dominant at $240^{\circ}C$ aging treatment. Mg-6Al-xZn alloys fabricated by the squeeze casting process had the better combination of tensile strength and elongation compared to the conventionally cast alloys. As zinc contents increased, the tensile strength was increased by the solid solution strengthening effect of zinc.