• Bulletin of the Korean Chemical Society
• /
• v.32 no.7
• /
• pp.2193-2198
• /
• 2011

We prepared polycatenar 1H-imidazole amphiphiles having a structure in which a 1H-imidazole head was connected through a benzene ring to a pheny group having two or three oligo(ethylene glycol) chains and studied their supramolecular assembly by fluorescence spectroscopy, transmission electron microscopy (TEM) and atomic force microscopy (AFM). When the aqueous solutions of the amphiphiles ($5{\times}10^{-5}M{\sim}10^{-3}M$) were deposited onto a carbon-coated copper grid and dried, twisted structures with diameters of ~200-300 nm were imaged by TEM and AFM. We presume that the structures comprised a chain of the amphiphile dimers formed via successive hydrogen bonding between the 1H of the imidazole group and 3N of the neighboring one. In a solution of pH 4, entangled fibers with diameters of several nanometers were observed by TEM. In a pH 10 solution, film-like aggregates formed exclusively. The 1H-imidazole amphiphiles hydrolyzed tetraethoxysilane to induce gelation to form fibrous and spherical silica structures at neutral pH in aqueous solutions. No silica was formed when imidazole was used instead of the amphiphiles, suggesting that the selfassembled aggregates of the amphiphiles were responsible for the gelation.

• Journal of the Korean Ceramic Society
• /
• v.32 no.8
• /
• pp.909-914
• /
• 1995

From alumina powder and TEOS, $\alpha$-Al2O3/SiO2 composite powder for reaction-sintered mullite was synthesized by heterogeneous coagulation and surface coating, and investigated the mullitization reaction and sintering behavor of these powders. In $\alpha$-Al2O3/SiO2 composite powder prepared by heterogeneous coagulation, each alumina particles were surrounded by silica particles of 50~60 nm in size. And the alumina particles in composite powder prepared by surface coating were coated by uniform silica layer with thickness of 50 nm. In both methods, mullitization reaction was completed at 1$650^{\circ}C$ for 3h, and specimen sintered above 145$0^{\circ}C$ was about 95% fo the theoretical relative density. Mullite grains formed from the reaction with composite powders showed spherical shape with a size of 1~2${\mu}{\textrm}{m}$.

• Korean Journal of Soil Science and Fertilizer
• /
• v.20 no.4
• /
• pp.309-314
• /
• 1987

This study was conducted to examine mineralogical aspects on anthractite and bituminous coal-fired power-plant ashes as a source of mineral fertilizer. Fly ashes contain dominant amounts of silica and alumina and considerable quantitites of potassium and boron. However, potassium and silica present in unavailable forms for plant growth. X-ray, DTA, and IR analysis of ash particles indicated the formation of new mineral, mullite with shape of which were spherical in the surface morphologies of SEM. Detailed SEM investigation showed the presence of imbedded blocky shape silicate material.

• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.195-200
• /
• 1989

The Silica-Carbon mixture was made with addition of carbon black in the composition which monodispersed spherical fine silica was formed by the hydrolysis of ethylsilicate, mole ratio of Carbon/Alkoxide was 3.1 and $\beta$-SiC powder was synthesized by reacting this mixture at 1,350~1,50$0^{\circ}C$ in Ar atmosphere. The results of this study are as follow : (1) The purity of synthesized $\beta$-SiC powder was above 99.98% and it was in cubic modification with lattice constant of 4.3476$\AA$. (2) The rate-controlling steps varied with the reaction temperature for the syntehsis of $\beta$-SiC in this study ; nucleation and growth of $\beta$-SiC at 1,350~1,40$0^{\circ}C$, interfacial reaction at 1,45$0^{\circ}C$ and diffusion described by Jander Equation at 1,50$0^{\circ}C$. (3) When the rate-determining step was nucleation and growth, the activation energy was about 87.8kcal/mol.

• Elastomers and Composites
• /
• v.47 no.1
• /
• pp.43-53
• /
• 2012

A suspension copolymerization of styrene and butyl methacrylate (BMA) in the aqueous phase was conducted at a selected temperature between 65 and $95^{\circ}C$. Hydrophobic silica was selected as a stabilizer and azobisisobutyronitrile (AIBN) as an initiator. Optimum dispersion of silica in water was obtained at pH 10 while polymerization reaction was run at pH 7. TGA and EDS measurements revealed that 90% of silica functioned as a stabilizer and 10% were incorporated into polymeric particles. Average particle diameter decreased with increasing amounts of stabilizer. Molecular weights displayed an increase when the stabilizer concentration reached 1.67 wt%. An increase in the initiator concentration and/or reaction temperature raised the reaction rate but decreased molecular weights. Particle diameter was nearly independent of the initiator concentration and reaction temperature. An increase in the BMA proportion decreased the glass transition temperature and increased the particle diameter with irregularity in shape. Incorporation of carbon black into the particles composed of styrene and BMA prolonged the reaction time before reaching completion. We have confirmed that a suspension copolymerization of styrene and BMA with hydrophobic silica as a stabilizer can produce spherical composite particles with $1-30{\mu}m$ in diameter containing carbon black.

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.5
• /
• pp.252-255
• /
• 2012

In order to characterize insulation properties of epoxy/micro-silica/nano-silicate composite (EMNC), long-term and short-term AC treeing tests were carried out undr non-uniform electric field generated between needle-plate electrodes. In a long-term test, a 10 kV (60 Hz) electrical field was applied to the specimen positioned between the electrodes with a distance of 2.7 mm in an insulating oil bath at $30^{\circ}C$, and a typical branch type electrical tree was observed in the neat epoxy resin and breakdown took place at 1,042 min after applying the 10 kVelectrical field. Meanwhile, the spherical tree with the tree length of $237{\mu}m$ was seen in EMNC-65-0.3 at 52,380 min (36.4 day) and then the test was stopped because the tree propagation rate was too low. In the short-term test, an electrial field was applied to a 3.5 mm-thick specimen at an increasing voltage rate of 0.5 kV/s until breakdown in insulating oil bath at $30^{\circ}C$ and $130^{\circ}C$, and the data was estimated by Weibull statistical analysis. The electrical insulation breakdown strength for neat epoxy resin was 1,763 kV/mm at $30^{\circ}C$, while that for EMNC-65-0.3 was 2,604 kV/mm, which was a modified value of 47%. As was expected, the breakdown strength decreased at higher test temperatures.

• Particle and aerosol research
• /
• v.8 no.2
• /
• pp.89-95
• /
• 2012

Spherical mesoporous silica particles, of which main pore diameter was 3.8 nm, were successfully prepared by spray pyrolysis from aqueous silicic acid. The effect of precursor concentration, reaction temperature, and the addition of urea and PEG on the particle diameter and pore properties such as pore diameter, total pore volume, and specific surface area were investigated by using FE-SEM, particle size analyzer, and nitrogen absorption-desorption analysis. With an increase of the precursor concentration from 0.2 M to 0.7 M, the average particle diameter, total pore volume, and specific surface area of the porous silica particles increased from 0.56 to $0.96\;{\mu}m$, 0.434 to $0.486\;cm^3/g$, 467.8 to $610.4\;m^2/g$, respectively. Within the temperature range $(600\;^{\circ}C{\sim}800\;^{\circ}C)$, there was no significant difference in the pore diameter, total pore volume, and specific surface area. In addition, the addition of urea as an expansion aid led to slight increases in particle diameter, pore diameter, and specific surface area. However, when the polyethylene glycol (PEG) as an organic template was used, the total pore volume of porous particles increased dramatically.

• Korean Chemical Engineering Research
• /
• v.54 no.4
• /
• pp.459-464
• /
• 2016

In this study, the electrochemical characteristics of porous silicon/carbon composite anode were investigated to improve the cycle stability and rate performance in lithium ion batteries. In this study, the effect of TEOS and $NH_3$ concentration, mixing speed and temperature on particle size of nano silica was investigated using $St{\ddot{o}}ber$ method. Nano porous Si/C composites were prepared by the fabrication processes including the synthesis of nano $SiO_2$, magnesiothermic reduction of nano $SiO_2$ to obtain nano porous Si by HCl etching, and carbonization of phenolic resin. Also the electrochemical performances of nano porous Si/C composites as the anode were performed by constant current charge/discharge test, cyclic voltammetry and impedance tests in the electrolyte of $LiPF_6$ dissolved inorganic solvents (EC:DMC:EMC=1:1:1vol%). It is found that the coin cell using nano porous Si/C composite has the capacity of 2,006 mAh/g and the capacity retention ratio was 55.4% after 40 cycle.

• Elastomers and Composites
• /
• v.47 no.4
• /
• pp.318-328
• /
• 2012

In this study, the one-component curable polyurethane resin was manufactured using blocked isocyanate and hybrid technology. To prepare the one-component curable hybrid polyurethane, silica hybrids including hydroxyl group was synthesized, and the size, shape and distribution of hybrid particle in polyurethane resin were confirmed. Then the dissociation property, mechanical property and molding property of blocked isocyanate were investigated. The dissociation property of blocked isocyanate in one-component curable polyurethane became better as the heating temperature and treatment time increased. The synthesized silica hybrid had spherical appearance and size of 23~27 nm in diameter, and it was observed that the hybrid particles were homogeneously distributed in polyurethane structure. In the case of hybrid polyurethane, the mechanical property, anti-abrasion and thermal property were higher than those of general polyurethane, and it was observed that the mechanical property was maintained when the plasticizer was introduced.

• Computers and Concrete
• /
• v.4 no.6
• /
• pp.425-436
• /
• 2007

This study is mainly focused on applying Fuller's ideal gradation curve to theoretically design blended ratio of all solid materials of a reactive powder mortar (RPM), also known as reactive powder concrete (RPC), with the aid of error function, and then to study the effect of fly ash/slag on the performance of RPM. The solid particle is assumed to be spherical particles. Then, the void volume of paste ($V_{\nu}$) and the paste content with specific quality can be obtained. As conclusion, under Fuller's ideal grading curve, the amount of fly ash/slag mixture is higher than that with silica fume along due to it better filled the void within solid particle and obtains higher packing density.