• 한국재료학회지
• /
• 제18권7호
• /
• pp.357-361
• /
• 2008

Microstructure and mechanical properties of WC-3 wt% Co cemented carbides, fabricated by a spark plasma sintering (SPS) process, were investigated in this study. The WC-3 wt%Co powders were sintered at $900{\sim}1100^{\circ}C$ for 5min under 40MPa in high vacuum. The density and hardness were increased as the sintering temperature increased. WC-3 wt%Co compacts with a relative density of 97.1% were successfully fabricated at $1100^{\circ}C$. The fracture toughness and hardness of a compact sintered at $1100^{\circ}C$ were $21.6 MPa{\cdot}m^{1/2}$ and 4279 Hv, respectively.

• Transactions on Electrical and Electronic Materials
• /
• 제11권6호
• /
• pp.249-252
• /
• 2010

The ground amorphous powder was consolidated into a dense sintered body with a typical ultrafine $Al_2O_3-GdAlO_3$ eutectic structure by spark plasma sintering (SPS). Sintered material with ultrafine and dense eutectic structure was obtained by an appropriate combination of rapid quenching and SPS at lower temperature and more quickly than by conventional sintering. The $Al_2O_3$-based rare earth eutectic ceramics for solar cell emitters are believed to have a higher efficiency and the $Al_2O_3$ based eutectic ceramics with ultrafine grains will be one of the promising materials showing excellent selective emitter characteristics.

• 한국분말재료학회지
• /
• 제7권3호
• /
• pp.161-167
• /
• 2000

Mechanically-alloyed NiAl powder and ball-milled (Ni+Al) powder mixture were sintered by spark-plasma sintering(SPS) process. Mechanical alloying was performed in a horizontal attritor for 20 h with rotation speed of 600 rpm. (Ni+Al) powder mixtures were prepared by ball milling for 1 and 10 h with 120 rpm. Both powders were sintered at $1150^{\circ}C$ for 5 min under $10^{-3}$ torr vacuum with 50 MPa die pressure in a SPS facility. Sintered densities of 97% and 99% were obtained from mechanically-alloyed NiAl powder and (Ni+Al) powder mixture, respectively. The sintered compact of (Ni+Al) powder mixture showed large grain size by a very rapid grain growth, while the grain size of mechanically-alloyed NiAl powder compact after sintering was extremely fine(80 nm). The difference in densification behavior of both powders were discussed.

• 한국결정성장학회지
• /
• 제10권2호
• /
• pp.152-158
• /
• 2000

상압 소결법(PLS, pressureless sintering) 및 방전가열 소결법(SPS, spark plasma sintering)으로 소결한 {{{{ {ZrB }_{2 } - ZrC }}}} 복합체의 미세구조를 SEM-EBSP 법에 의해 결정기하학적으로 분석하였다. PLS법에 의해 소결된 복합체에서 {{{{ { ZrB}_{2 } }}}}의 (1010) 면은ND(시편에 수직인 방향)로 배향되었고, ZrC 경우 (101) 및 (111)면이 ND방향으로 배향되었다. 한편 SPS법에 위해 소결된 {{{{ { ZrB}_{2 } }}}}의 (0001)A면은 ND방향으로 강하게 배향되었다. ZrC인 경우 (001) 면만이 ND방향으로 배향되었다. PLS법에 의한 소결체의 결정립은 특정방위에 대해 약한 배향을 갖으면서, {{{{ { ZrB}_{2 } }}}}와 ZrC상 계면의 구조적 조화가 우수한 반면, SPS법에 의한 소결체의 결정립들은 특정방향으로 강하게 배향되는 경향을 보인다.

• Archives of Metallurgy and Materials
• /
• 제65권3호
• /
• pp.1045-1049
• /
• 2020

This research describes effects of Si addition on microstructure and mechanical properties of the Al-Cr based alloys prepared manufactured using gas atomization and SPS (Spark Plasma Sintering) processes. The Al-Cr-Si bulks with high Cr and Si content were produced successfully using SPS sintering process without crack and obtained fully dense specimens close to nearly 100% T. D. (Theoretical Density). Microstructure of the as-atomized Al-Cr-Si alloys with high contents of Cr and Si was composed multi-phases with hard and thermally stable such as Al₁₃Cr₄Si₄, AlCrSi, Al₈Cr₅ and Cr₃Si intermetallic compounds. The average hardness values were 703 Hv for S5, 698 Hv for S10 and 824 Hv for S20 alloy. Enhancement of hardness value was resulted from the formation of the multi-intermetallic compound with hard and thermally stable and fine microstructure by the addition of high Cr and Si using rapid solidification and SPS process.

• 한국분말재료학회지
• /
• 제15권4호
• /
• pp.285-291
• /
• 2008

Fe based ($Fe_{68.2}C_{5.9}Si_{3.5}B_{6.7}P_{9.6}Cr_{2.1}Mo_{2.0}Al_{2.0}$) amorphous powder were produced by a gas atomization process, and then ductile Cu powder fabricated by the electric explosion of wire(EEW) were mixed in the liquid (methanol) consecutively. The Fe-based amorphous - nanometallic Cu composite powders were compacted by a spark plasma sintering (SPS) processes. The nano-sized Cu powders of ${\sim}\;nm$200 produced by EEW in the methanol were mixed and well coated with the atomized Fe amorphous powders through the simple drying process on the hot plate. The relative density of the compacts obtained by the SPS showed over 98% and its hardness was also found to reach over 1100 Hv.

• 한국분말재료학회지
• /
• 제23권3호
• /
• pp.195-201
• /
• 2016

Composite materials consisting of pure aluminum matrix reinforced with different amounts of graphite particles are successfully fabricated by mechanical ball milling and spark plasma sintering (SPS) processes. The shrinkage rates of the composite powders vary with the amount of graphite particles and the lowest shrinkage value is observed for the composite with the highest amount of graphite particles. The current slopes of time increase with increase in the amount of graphite particles whereas the current slopes of temperature show the opposite trend. The highest thermal conductivity is achieved for the composite with the least amount of graphite particles. Therefore, the thermal properties of the composite materials can be controlled by controlling the amount of the graphite particles during the SPS process.

• 한국재료학회지
• /
• 제17권3호
• /
• pp.132-136
• /
• 2007

Oxidation resistance of sintered ${\beta}-FeSi_{2}$ was investigated at intermediate temperature range in air atmosphere. Fully dense and porous bodies of ${\beta}-FeSi_{2}$ samples were fabricated by using the Spark Plasma Sintering (SPS). They were annealed at $900^{\circ}C$ for 5days to obtain ${\beta}-FeSi_{2}$ phase. The bulk samples were oxidized at $800,\;900\;and\;950^{\circ}C$ in air atmosphere. The high temperature oxidation tests reveal that amorphous $SiO_{2}$ layer, similar to Si was formed and grew parabolically on ${\beta}-FeSi_{2}$. Accelerated oxidation is not observed as well as cracks and grain boundary oxidation. Granular ${\varepsilon}-FeSi$ was developed below the oxide layer as a result of oxidation of ${\beta}-FeSi_{2}$. Oxidation resistance of sintered ${\beta}-FeSi_{2}$ was excellent for high-temperature thermoelectric application.

• 한국분말재료학회지
• /
• 제12권1호
• /
• pp.43-50
• /
• 2005

Mechanical alloying using high-energy ball mill and subsequent spark plasma sintering (SPS) process was applied to Al-Fe-Cr and Al-Fe-Mo powder mixture to investigate effects of Cr and Mo addition on thermal stability of Al-Fe, and thereby to enhance its thermal stability up to $500^{\circC}$. Various analytical techniques including micro-Vickers hardness test, SEM, TEM, X-ray diffractometry and corrosion test were carried out. It was found that addition of Cr and Mo to Al-Fe system played a role of grain growth inhibitor of matrix Al and some precipitates such as $Al_3Fe$ during SPS and subsequent heat treatment. The inhibition of grain growth resulted in increased Vickers hardness and thermal stability up to $500^{\circC}$ comparing to those of Al-Fe alloy system.

• 한국재료학회지
• /
• 제13권6호
• /
• pp.352-359
• /
• 2003

In order to control the grain size, the spark plasma sintering technique is applied for the manufacturing of Cu-26.7Al-4.05AI(wt.%) shape memory alloy with pure Cu, Zn, and Al element powders. The sintering processes were carried out under different atmospheres. The sintered bodies were denser under Ar or Ar＋4%$H_2$gas atmosphere than under vacuum. With use of small-sized powders, a very small average grain size of 2∼3 $\mu\textrm{m}$ was obtained, but the single phase was not formed. With the large-sized powders the single austenitic phase was observed with the average grain size of $70∼72\mu\textrm{m}$. When the different size of raw powders was mixed, it is confirmed that the average grain size of the manufactured alloys was 15 $\mu\textrm{m}$ with single austenitic phase, but the distribution of grain size was not uniform.