• Journal of the Korean Ceramic Society
• /
• v.44 no.3 s.298
• /
• pp.137-141
• /
• 2007

$La_{2}O_{3}-TiO_{2}-SiO_{2}$ glass, a type that could not obtained so far by the conventional melting method, was prepared successfully using a sol gel process. Glass derived with the sol-gel process has compositions of $5La_{2}O_{3}-5TiO_{2}-90SiO_{2},\;5La_{2}O_{3}-10TiO_{2}-85SiO_{2}$, and $5La_{2}O_{3}-20TiO_{2}75SiO_{2}$. The UV-visible absorption edge of all glass compositions was below 400 nm. The measured density is in the range of 2.55-2.89, and was nearly identical to the calculated density and the refractive index of the glasses derived from the sol-gel ranges from 1.545 to 1.645. The molar additive coefficient of $TiO_{2}$ measured in this ternary system is lower than the calculated value, while the value of $La_{2}O_{3}$ is higher.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.33 no.1
• /
• pp.70-74
• /
• 2000

Agar for microbiological medium was prepared with pilot-scale for industrial application by the process of microfiltration ($0.4 {\mu}m\;pore size$) in $40{\~}50{\circ}C$, washing with sot water, and treatment with $0.25\;N NaOH\;at\;70{\circ}C$. Transparency, gel strength, viscosity, sulfate content, and syneresis ratio of agar prepared from Gelidium amansii was compared with commercial agar for microbiological medium. Gel strength and transparency were increased with processing, however, it's viscosity, sulfate content, and syneresis ratio were reduced. The final agar product was superior to commercial agar for microbiological medium.