• Journal of Magnetics
• /
• v.21 no.1
• /
• pp.12-19
• /
• 2016

The <100> oriented $Fe_{83}Ga_{17}$ alloys with various contents of NbC or B were prepared by directionally solidification method at the growth rate of $720mm{\cdot}h^{-1}$. With a small amount of precipitates, the columnar grains grew with cellular mode during directional solidification process, while like-dendrite mode of grains growth was observed in the alloys with higher contents of 0.5 at% due to the dragging effect of precipitates on the boundaries. The NbC precipitates disperse both inside grains and along the boundaries of $Fe_{83}Ga_{17}$ alloys with NbC addition, and the Fe2B secondary phase particles preferentially distribute along the grain boundaries in B-doped alloys. Precipitates could affect grain growth and improved the <100> orientation during directional solidification process. Small amount of precipitate element addition slightly increased the magnetostrictive strain, and a high value of 335 ppm under pre-stress of 15 MPa was achieved in the alloys with 0.1 at% NbC. Despite the fact that the effect on magnetic induction density of small amount of precipitates could be negligible, the coercivity markedly increased with addition of precipitate element for $Fe_{83}Ga_{17}$ alloy due to the retarded domain motion resulted by precipitates.

• Journal of Korea Foundry Society
• /
• v.12 no.3
• /
• pp.220-229
• /
• 1992

The degree of purification and the macrostructure of high purity aluminium were studied through the alternate stirring method in order to improve the nonuniformity of solute concentration in the unidirectional stirring method. The $2^3$ factorial design was done to examine the effects of experimental factors more qualitatively. In the relatively low stirring speed of 1500 rpm with alternate stirring mode, the uniform solute profile and refined grain structure were obtained due to strong washing effect and turbulent fluid flow. It was induced by the transition of the momentum boundary layer by alternation of the stirrer. It was concluded from this study that the alternate stirring mode was more effective to obtain the uniformity of solute even in the stirring speed of 1500 rpm. But the degree of purification decreased below the critical alternating period. When 2N(99.8wt.%) aluminium was used as the starting material the morphology of solid-liquid showed the cellular shape and the columnar grains were inclined to the direction of rotation. This inclined grain growth resulted from the difference of relative velocities of solid and liquid. The inclined angle was increased as the stirring speed increased and solidification proceeded. In the case of 4N aluminium, there was no inclined grain growth and it was confirmed from the macrostructure and SEM work that the morphology of solid-liquid interface was planar. From the factorial design, it was found that the alternate stirring mode showed poorer purification effect than that of unidirectional stirring mode at low speed(500 rpm). In addition, the factor that had the most significant effect on the degree of purification was the stirring speed.

• Journal of Korea Foundry Society
• /
• v.18 no.5
• /
• pp.439-449
• /
• 1998

Formation of oxide inclusions in the molten aluminium alloys during solidification is investigated. The oxidation tendency of both Al-4.5wt%Cu and Al-7wt%Si alloys is increased with melt temperature, particularly over $700^{\circ}C$. However, an Al-5wt%Mg alloy exhibits a decreasing mode over $800^{\circ}C$. The oxidation behavior with holding time shows the S curve shape for all of the alloys. It is shown that the mechanism of oxidation of Al-5wt%Mg alloy has a two step process different from that of Al-4.5wt%Cu and Al-7wt%Si alloys. The species and morphology of oxide inclusions in each alloy is also shown. The microstructure was more coarsened during solidification when the melt contains a large amount of oxide inclusion than when it doesn't. This result can be explained in terms of both the hindrance of heat extraction by oxide film formed on the aluminium melt and the difference of heat capacity between the aluminium melt and oxide inclusion during solidification.

• 연구논문집
• /
• s.29
• /
• pp.173-183
• /
• 1999

The vacuum investment casting process for a large gas turbine component, Inner Preswirl Support (IPS), was simulated by using commercial FEM package ProCAST(TM) with view factor radiation method. The solid fraction in mushy zone was directly measured by Differential thermal analysis(DTA-DSC mode). Three types gating design. considering liquid flow and heat release through it. were proposed. Solidification had begun at the ribs or thin sections of the IPS casting and advanced further through the upper and lower gates. The computed temperature gradient G and G/R values at 70% solidified temperature were used for prediction of microshrinkage formation during casting. The effect of mold preheat on the thermal history of the casting displayed minute effect on the microshrinkage formation.

• Journal of Welding and Joining
• /
• v.17 no.5
• /
• pp.89-96
• /
• 1999

The base metal and weld metal of alloy designed austenitic stainless steels were electrochemically tested in artificial sea water. Pitting resistance of 14 different stainless steels was evaluated by measuring pitting potential. The effect of alloy element to pitting potential was evaluated by changing chromium, nickel, sulfur content. The site of pitting initiation was observed by optical microscope. As a result of electrochemical test, pitting resistance of weld metal was higher than base metal, and rapidly cooled weld metal has higher pitting potential than slowly cooled weld metal. In case of primary δ-ferrite solidification, pitting potential was increased, but residual δ-ferrite was detrimental to pitting resistance. Chromium was more effective to pitting resistance than nickel, and sulfur was very detrimental element to pitting resistance.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.27 no.2
• /
• pp.132-140
• /
• 1991

The aim of this study was saving of chromium and nickel content in the austenitic stainless steels, SUS 316 and SUS 321. By control of primary solidification mode, new austenitic stainless steels with good weldability, high toughness and corrosion resistance could be developed. The main results obtained were as follows; 1. Hot crack resistance of laboratory melts was good and higher than imported austenitic stainless steel. 2. Cryogenic and room temperature toughness of laboratory melts were high and laboratory melts M-7 to M-9 showed very high toughness than SUS321 imported stainless steel. 3. Intergranular corrosion resistance of laboratory melts was higher than imported stainless steels, SUS316 and SUS321. 4. By this concept of controlling primary solidification mode, could save expensive alloy additives, chromium and nickel.

• Journal of Welding and Joining
• /
• v.32 no.6
• /
• pp.56-63
• /
• 2014

To develop and understand dissimilar metals joining of Stainless steel and Copper, ultra-high speed laser lap welding was studied using single mode fiber laser in this study. SUS304 and Cu have large differences in materials properties, and Cu and Fe have no intermetallic compounds by typical binary phase of Cu and Fe system. In this study, ultra-high speed lap welds of SUS304 and Cu dissimilar metals using single-mode fiber laser was generated, and weldability of the weld fusion zone was evaluated using a tensile shear test. To understand the phenomenon of tensile shear load, weld fusion zone of interface weld area and fracture parts after tensile shear test were observed using scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX) analysis system. And it was confirmed that Cu was easily melting and penetrating in the grain boundaries of SUS304 because of low melting temperature. And high thermal conductivity of copper occurred dissipate heat energy rapidly. These properties cause the solidification cracking in weld zone.

• 연구논문집
• /
• s.22
• /
• pp.115-125
• /
• 1992

Mechanical properties and microstructure were investigated on vacuum induction melted $Fe_3A1$base alloys of $DO_3$ structure. Specal emphasis were put on the effect of alloy chemistry, grain size and process(rolling, directional solidification) on mechanical properties of Fe-22.5-39at.%Al at elevated temperature between room temperature and $800^{\circ}C$. grain size of as-cast alloys is refined by rolling from 1mm to $80\mum$. Tensile strength of Fe-24.lat.%AI was about 404MPa at the critical ordering temperature, and the fracture strain of the alloy was 1-2% at room temperature. An inverse temperature dependence of the strength is noticed as-cast $Fe_3A1$. The presence of Cr and Zr do not affect the room temperature ductility and high temperature strength. Fracture strain of directionally solidified(DS) $Fe_3A1$ is about 1%at room temperature, but is about 60%at. $T_C$(550^{\circ}C)$. Tensile strength of DS alloy is lower than that of as-cast alloy at $530^{\circ}C$ and $430^{\circ}C$. Failure mode at room temperature varies from transgranular fracture to intergranular fracture with the addition of Al. the failure mode also varies from mixed(transgranular+ intergranular) mode between room temperature and $500^{\circ}C$ to intergranular mode above $550^{\circ}C$

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.19.2-19.2
• /
• 2011

ZnO nanowires have been fabricated by vapor-liquid-solidification with hot-walled pulsed laser deposition method. The diameter of ZnO nanowire has been systematically controlled simply by changing the thickness of Au catalyst. Field effect transistors with different diameter have been fabricated by using photolithography and e-beam lithography. The threshold voltage of ZnO nanowire FET showed enhanced mode and depleted mode depending on the diameter of ZnO nanowires. This is mainly due to the change of the carrier concentration depending on the size of nanowires. We have fabricated ZnO nanowire inverters using nanowire FETs. This simple method to fabricate ZnO nano-inverter will be useful to open the possibility of ZnO nanoelectronic applications.

• Journal of Korea Foundry Society
• /
• v.13 no.1
• /
• pp.71-80
• /
• 1993

Squeeze casting has advantages to improve mechanical properties of nonferrous castings without losing high productivity. Sound pore free structure makes it possible to be subjected to heat treatment and welding. This process became popular to produce lighter automobile parts alternating cast iron parts. It has, however, two disadvantages of segregation and scattered structure due to the solidified layers in sleeve. In this study segregation behavior of squeeze cast Al-7%Si-0.3%Mg alloy bars was investigated using HVSC machine under various injection conditions. Degree of segregation decreased with injection pressure and effect of injection velocity on it was small. Segregation mode of solute was strongly governed by solidification mode and flow pattern.