Multiferroic materials have attracted much attention due to their fascinating fundamental physical properties and technological applications in magnetic/ferroelectric data-storage systems, quantum electromagnets, spintronics, and sensor devices. Among single-phase multiferroic materials, $BiFeO_3 $ is a typical multiferroic material with a room temperature magnetoelectric coupling in view of high magnetic-and ferroelectric-ordering temperatures (Neel temperature $T_N$~647 K and Curie temperature $T_C$~1,103 K). Rare-earth ion substitution at the Bi sties is very interesting, which induces suppressed volatility of Bi ion and improved ferroelectric properties. At the same time, Fe-site substitution with magnetic ions is also attracting, and the enhanced ferromagnetism was reported. In this study, $Bi_{1-x}Dy_xFe_{0.95}Co_{0.05}O_3$ (x=0, 0.05 and 0.1) bulk ceramic compounds were prepared by solid-state reaction and rapid sintering. High-purity $Bi_2O_3$, $Dy_2O_3$, $Fe_2O_3$ and $Co_3O_4$ powders with the stoichiometric proportions were mixed, and calcined at $500^{\circ}C$ or 24 h to produce $Bi_{1-x}Dy_xFe_{0.95}Co_{0.05}O_3$. The samples were immediately put into an oven, which was heated up to $800^{\circ}C$ nd sintered in air for 30 min. The crystalline structure of samples was investigated at room temperature by using a Rigaku Miniflex powder diffractometer. The field-dependent magnetization measurements were performed with a vibrating-sample magnetometer. The electric polarization was measured at room temperature by using a standard ferroelectric tester (RT66B, Radiant Technologies).

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.250-250
• /
• 2012

Recently, multiferroic materials have attracted much attention due to their fascinating fundamental physical properties and potential technological applications in magnetic/ferroelectric data storage systems, quantum electromagnets, spintronics, and sensor devices. Among single-phase multiferroic materials, $BiFeO_3$, in particular, has received considerable attention because of its very interesting magnetoelectric properties for application to spintronics. Enhanced ferromagnetism was found by Fe-site ion substitution with magnetic ions. In this study, $BiFe_{1-x}Ni_xO_3$ (x=0 and 0.05) bulk ceramic compounds were prepared by solid-state reaction and rapid sintering. High-purity $Bi_2O_3$, $Fe_3O_4$ and NiO powders were mixed with the stoichiometric proportions, and calcined at $450^{\circ}C$ for 24 h to produce $BiFe_{1-x}Ni_xO_3$. Then, the samples were directly put into the oven, which was heated up to $800^{\circ}C$ and sintered in air for 20 min. The crystalline structure of samples was investigated at room temperature by using a Rigaku Miniflex powder diffractometer. The Raman measurements were carried out with a Raman spectrometer with 514.5-nm-excitation Ar+-laser source under air ambient condition on a focused area of $1-{\mu}m$ diameter. The field-dependent magnetization and the temperature-dependent magnetization measurements were performed with a vibrating-sample magnetometer. The x-ray diffraction study demonstrates the compressive stress due to Ni substitution at the Fe site. $BiFe_{0.95}Ni_{0.05}O_3$ exhibits the rhombohedral perovskite structure R3c, similar to $BiFeO_3$. The lattice constant of $BiFe_{0.95}Ni_{0.05}O_3$ is smaller than of $BiFeO_3$ because of the smaller ionic radius of Ni3+ than that of Fe3+. The field-dependent magnetization of $BiFe_{0.95}Ni_{0.05}O_3$ exhibits a clear hysteresis loop at 300 K. The magnetic properties of $BiFe_{0.95}Ni_{0.05}O_3$ were improved at room temperature because of the existence of structurally compressive stress.

• Journal of the Korean Society of Radiology
• /
• v.15 no.3
• /
• pp.391-399
• /
• 2021

Eu²⁺ doped polyphosphate NaSr(PO₃)₃ blue-emitting phosphors were synthesized by the conventional solid state method in a reductive atmosphere. The phase formation of NaSr(PO₃)₃ phosphors were characterized by using the X-ray powder diffraction (XRD) measurement. The photoluminescence emission and excitation spectra of the NaSr(PO₃)₃:Eu²⁺ phosphor, and decay curves were measured. Under the near-UV excitation, the phosphor exhibits a band emission around 420 nm assigned to the 4f⁶5d→f7(8S^7/2) transition of Eu²⁺. The temperature dependent emission spectra and decay curves were measured to elevate the thermal properties of the Eu²⁺ doped phosphors. The as-prepared NaSr(PO₃)₃:Eu²⁺ phosphors show a strong temperature dependent performance, which can serve as a promising temperature sensor.