• Korean Journal of Materials Research
• /
• v.24 no.5
• /
• pp.271-276
• /
• 2014

Silica nano-powder (SNP) is an inorganic material able to provide high-performance in various fields because of its multiple functions. Methods used to synthesize high purity SNP, include crushing silica minerals, vapor reaction of silica chloride, and a sol-gel process using TEOS and sodium silicate solution. The sol-gel process is the cheapest method for synthesis of SNP, and was used in this study. First, we investigated the shape and the size of the silica-powder particles in relation to the variation of HCl and sodium silicate concentrations. After drying, the shape of nano-silica powder differed in relation to variations in the HCl concentration. As the pH of the solution increased, so did the density of crosslinking. Initially, there was NaCl in the SNP. To increase its purity, we adopted a washing process that included centrifugation and filtration. After washing, the last of the NaCl was removed using DI water, leaving only amorphous silica powder. The purity of nano-silica powder synthesized using sodium silicate was over 99.6%.

• YAKHAK HOEJI
• /
• v.39 no.1
• /
• pp.68-77
• /
• 1995

Aluminum magnesium silicate was synthesized by reacting the mixed solutions of sodium aluminate and magnesium chloride with sodium silicate solution in this study. The optimal synthesis conditions based on the yield of the product has been attained according to Box-Wilson experimental design. It was found that the optimal synthetic conditions of aluminum magnesium silicate were as follows: Reaction temperature=$69~81^{\circ}C$; concentration of two reactants, sodium aluminate and magnesium chloride= 13.95~14.44 w/w%; molar concentration ratio of the two reactants, [NaAlO$_{2}$]/MgCl$_{2}$]=3.63~4.00; reaction time= 12~15 min; drying temp. of the product=$70~76^{\circ}C$. Aluminum magnesium silicate synthesized under the optimal synthesis condition was dispersed in 0.75, 1.0 and 1.5w/w% aqueous solution or suspension of six dispersing agents, and the Theological properties of the dispersed systems prepared have been investigated at $15^{\circ}C$ and $25^{\circ}C$ using Brookfield LVT Type Viscometer. The acid-consuming capacity of the most excellent product was 272~278 ml of 0.1N-HCl per gram of the antacid. The flow types of 5.0 w/w% aluminum magnesium silicate suspension were dependent upon the kind and concentration of dispersing agents added. The apparent viscosity of the suspension was generally increased with concentration of dispersing agents and was not significantly changed or decreased as the temperature was raised. A dispersing agent, hydroxypropyl cellulose suspension, exhibited an unique flow behavior of antithixotropy. The flow behavior of the suspension dispersed in a given dispersing agent not always coincided with that of the dispersing agent solution or suspension itself.

• The Korean Journal of Ceramics
• /
• v.6 no.2
• /
• pp.120-123
• /
• 2000

The geopolymer technique may be a future-oriented technology for saving energies and resources. This technique requires 3 fundamental elements so-called filler, hardener and geopolymer liquor being generally an alkaline silicate solution. Quartz powder, water quenched granulated blast furnace slag and sodium silicate solution prepared from $Na_2O\cdot2SiO_2$were chosen for these three elements. After mixing these starting materials in appropriate proportions, monoliths were prepared by casting at room temperature. Strength tests showed the following results for 28d age speciment: 7.9-12.7 MPa in flexural strength and 20.2-32.8 MPa in compressive strength, depending on geopolymer liquor/solid ratio, P/S and fineness of the quartz powders used.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.11a
• /
• pp.627-630
• /
• 2005

This paper examines degradation properties of alkali-activated alumino-silicate composite body by NAS solution exposed to high temperature. Activators include sodium hydroxides and sodium silicate solution. In the result of experiment, flexural and compressive strength of AAS base mortar exposed to high temperature ($400\~600^{\circ}C$) was higher than alumina cement base mortar. Particularly, In case of compressive strength, alumina cement base mortar was decreased by about $60\~70\%$. While, AAS base mortar exposed to high temperature ($400\~600^{\circ}C$) was higher than that curing by room temperature. The above results showed that AAS base inorganic binder has a good mechanical properties exposed to high temperature($400\~600$).

• YAKHAK HOEJI
• /
• v.47 no.1
• /
• pp.5-9
• /
• 2003

Synthetic aluminum silicate was prepared by reacting aluminum sulfate solution with Sodium silicate solution in this study. The optimum synthesis conditions based on the yield of the product were established by applying Box-Wilson experimental design. The results were found to be as follows; Reactant temperature : 50∼72$^{\circ}C$, Concentration of two reactants : 10∼17.6％, Mole ratio of two reactants, [Sod. silicate]/[Al. sulfate) : 4.6∼5.0, Temperature of washing water : 25∼4$0^{\circ}C$, and Drying temperature of product : 50∼$65^{\circ}C$. The physical and chemical properties of synthetic aluminum silicate as medicine were investigated by means of chemical analysis, adsorption test and acid consuming capacity measurements.

• Journal of the Korean GEO-environmental Society
• /
• v.12 no.4
• /
• pp.17-24
• /
• 2011

For the purpose of cut off and ground stabilization, water glass chemical grouting method using sodium silicate has problems of weakening durability and ground water pollution because leaching was conducted when the homogel is exposed to the ground water as time elapses. The purpose of this study is to identify the effect of alkali silica sol ground injection materials, it was compared with the sodium silicate ground injection materials using water glasses. For sodium silicate and alkali silica sol by mixing each case is divided into four different specimens were made and tested. The characteristic of alkali silica sol ground injection material was analyzed by unconfined compression test and environmental impact statement of ordinary portland cement and blast furnace slag cement. Alkali silica sol specimens were made mixing A-solution and B-solution in the proportion of one on one. Through this study, alkali silica sol ground injection mixing blast furnace slag cement has excellent strength and environment-friendly.

• Journal of the Korean Ceramic Society
• /
• v.26 no.3
• /
• pp.361-370
• /
• 1989

Mullite powders were synthesized from the common solution of aluminum sulfate and sodium silicate solutions by the emulsion-hot kerosene technique. The reaction temperature and mechanism for mullitization and the characteristics of synthesized mullite powders were investigated. The effect of Na components introduced from sodium silicate solution on the physical property and microstructure of sintered mullite was also examined. It was proved that mullites were formed at 75$0^{\circ}C$ through the reaction mechanism of Na2O.2.2SiO2＋3.3Al2(SO4)3longrightarrow1.1(3Al2O3.2SiO2)＋Na2SO4＋8.9SO3. Synthetic mullite powders consisted of the compositiion of 3Al2O3.2SiO2 and showed highly agglomeration of hollow spherical particles of 1${\mu}{\textrm}{m}$ diameter. The density and fracture toughness of sintered mullites were somewhat reduced because of the effect of a very small amount of residual Na components.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.9
• /
• pp.3483-3485
• /
• 2011

• Korean Journal of Human Ecology
• /
• v.6 no.1
• /
• pp.27-34
• /
• 2003

We investigated the bacterial and chemical retting conditions of ramie grown in Hansan. Bacterial retting was done in troughs at a temperature of 30${\pm}$2$^{\circ}C$ for 1, 2, 3, 4, 5, 6 and 10 days. Chemical retting(CR) was done at the different conditions using sodium silicate (Na$_2$SiO$_3$), sodium carbonate(Na$_2$CO$_3$) and sodium hydroxide(NaOH) as alkali solutions. The retting solution was boiled during 1. 2, 4 and 6 hours respectively at the different concentration(0.5, 2.0, 4.0, 6.0. 8.0 %) with decorticated ramie stems submerged in it. The treated ramie was then rinsing with running tap water thoroughly, which was further soaker in 0.5% acetic acid (v/v) solution for three minutes and washed thoroughly with distilled water. Finally ramie was dried for 2 hours in vacuum oven at 100 $^{\circ}C$. To know change of ramie fiber characteristics retted at the different conditions, weight loss, fiber bundle strength were tested and color, texture, luster etc. were also sensually evaluated. The results were as follows. $.$ Weight loss of ramie retted in each alkali solutions were about 10%, 20% and 30% in sodium silicate, sodium carbonate and sodium hydroxide, respectively. $.$ Chemical retting was faster than bacterial retting, but the color of chemically retted ramies were worse than that of bacterially retted ramies. $.$ The combination of bacterial and chemical processing showed some merits. A combination of either 2 or 3 days of bacterial and then chemical retting might provide the best quality ramie. $.$ Ramie fiber became cottonized ramie when retted in 8% NaOH solution for 6-8hours.

• Nuclear Engineering and Technology
• /
• v.54 no.11
• /
• pp.4062-4071
• /
• 2022

Long-term aluminum (Al) corrosion tests were designed to investigate the condition that would generate severe Al corrosion and precipitation. Buffer agents of sodium tetraborate (NaTB), trisodium phosphate (TSP) and sodium hydroxide (NaOH) were adopted. The insulation materials, fiberglass and calcium silicate (Ca-sil), were examined to explore their effects on Al corrosion. The results show that significant precipitates were formed in both NaTB/TSP-buffered solutions at high pH. The precipitates formed in NaTB solution raise more concerns on chemical effects in GSI-191. A passivation layer formed on the surfaces of coupon in solution with the presence of insulations could effectively mitigate Al corrosion. The Fe-enriched intermetallic particles (IPs) embedded in coupon appeared to serve as seeds to readily induce precipitation via providing extra area for heterogeneous Al hydroxide precipitation. X-ray spectroscopy (EDS) and X-ray diffraction (XRD) analyses indicate that the precipitates are mainly boehmite (γ-AlOOH) and no direct evidence confirms the presence of sodium aluminum silicate or calcium phosphate.