• 한국세라믹학회지
• /
• 제25권1호
• /
• pp.59-65
• /
• 1988

To develop porous glass membranes used for a effective membrane-separation process, porous glasses and glass membranes were prepared from the sodium borosilicate parent glass by the phaseseparation technique and effects of heat-treatment and leaching conditions on their characteristics were investigated. The crack-free glass membranes could be fabricated from the 9.4 Na2-O-30.7 B2O3-59.2 SiO2-0.7 Al2O3(wt%) parent glass by heat-treatment at the lower temperature(550-570$^{\circ}C$) and for longer than 45 hrs for the phase separation, followed by leaching with 3N-HCl＋60% ethylene glycol solution at 90$^{\circ}C$ over 25 hrs. Porous glasses prepared in this work showed large specific surface areas(400㎡/g) and narrow pore size distribution with the mean pore radius of 14${\AA}$ enough for the application as reverse osmosis membranes. The salt-rejection efficiency and product-flux of the glass membranes heat-treated at 570$^{\circ}C$ for 80 hrs were found to be 51.8% and 270cc/㎡. hr, respectively. This result suggests that the porous glass membranes fabricated in this study could be applied for the reverse osmosis process.

• 방사성폐기물학회지
• /
• 제3권1호
• /
• pp.57-65
• /
• 2005

본 연구는 사용 후 핵연료의 금속전환 공정에서 발생되는 폐용융염을 고형화하는 방법으로 GRSS(Gel-Route Slabilization/Solidifcation)개념을 이용한 전처 리법을 제안하였다. Sodium silicate와 H3p04로 구성된 물질계에서는 SiO$_2$에 의해 형성되는 반응모듈 내에서 휘발성 핵종은 열적으로 안정한 화합물로 전환된다. 얻어진 생성물은 붕규산 유리매질과의 반응을 통하여 Li는 Li$_{3}$PO$\_4$ 형태로 유지되며 Cs 및 Sr은 유리매질내에 포용될 수 있다. 또한 sodium silicate, H$_{3}$PO$_4$ 및 ZrCl$_4$로 이루어진 물질계를 이용하여 내구성이 우수한 WZP 세라믹 고화매질을 합성하였다. $700^{circ}C$이상에서 NZP구조가 형성되며, Cs가 Li보다 우선하여 NZP구조를 형성하였다. 이상의 결과로부터, GRSS를 이용한 폐용융염의 전처리는 단순한 공정과 열적 안정성을 통하여 검증된 고화매질로 고형화가 가능토록하는 유효한 접근법이라 할 수 있으며, 수화학적 안정성의 검증을 통하여 ANL의 제올라이트를 이용한 고화법에 대한 대안이 될 것으로 기대된다.