• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.311-312
• /
• 2012

PEO(Plasma Electrolytic Oxidation) 방법으로 인한 마그네슘 합금의 산화막 코팅시 Sodium Aluminate의 역할을 알아보았다. 전해액 내에 Sodium Aluminate 의 농도가 증가할수록 Plasma arc 발생에 필요한 전압의 상승이 빨라졌으며 그 산화막이 치밀해짐을 알 수 있었다. 또한 치밀한 산화막의 기공률은 분석하여 이를 내식성 결과와 비교함으로써 산화막의 기공률이 내식성에 미치는 영향을 고찰해보았다.

• Journal of the Korean Society for Heat Treatment
• /
• v.25 no.5
• /
• pp.227-232
• /
• 2012

Magnesium alloy have good physical properties such as good castability, good vibration absorption, high strength/weight ratios. Despite the desirable properties, the poor resistance of Mg alloy impedes their use in many various applications. Therefore, magnesium alloy require surface treatment to improve hardness, corrosion and wear resistance. Plasma Electrolytic Oxidation (PEO) is one the surface treatment methods to form oxide layer on Mg alloy in alkali electrolyte. In comparison with Anodizing, there is environmental process having higher hardness and faster deposition rate. In this study, the characteristics of oxide film were examined after coating the AZ31 Mg alloy through the PEO process. We changed concentration of sodium aluminate into $K_2ZrF_6$, KF base electrolyte. The morphologies of the coating layer were characterized by using scanning electron microscopy (SEM). Corrosion resistance also investigated by potentiodynamic polarization analysis. As a result, propertiy of oxide layer were changed by concentration of sodium aluminate. Increasing with concentration of sodium aluminate in electrolyte, the oxidation layer was denser and the pore size was smaller on the surface.

• Advances in concrete construction
• /
• v.11 no.1
• /
• pp.73-80
• /
• 2021

Rice Husk Ash (RHA) geopolymer paste activated by sodium aluminate were characterized by X-ray diffractogram (XRD), scanning electron microscope (SEM), energy dispersion X-Ray analysis (EDAX)and fourier transform infrared spectroscopy (FTIR). Five series of RHA geopolymer specimens were prepared by varying the Si/Al ratio as 1.5, 2.0, 2.5, 3.0 and 3.5. The paper focuses on the correlation of microstructure with hardened state parameters like bulk density, apparent porosity, sorptivity, water absorption and compressive strength. XRD analysis peaks indicates quartz, cristobalite and gibbsite for raw RHA and new peaks corresponding to Zeolite A in geopolymer specimens. In general, SEM micrographs show interconnected pores and loosely packed geopolymer matrix except for specimens made with Si/Al of 2.0 which exhibited comparatively better matrix. Incorporation of Al from sodium aluminate were confirmed with the stretching and bending vibration of Si-O-Si and O-Si-O observations from the FTIR analysis of geopolymer specimen. The dense microstructure of SA2.0 correlate into better performance in terms of 28 days maximum compressive strength of 16.96 MPa and minimum for porosity, absorption and sorptivity among the specimens. However, due to the higher water demand to make the paste workable, the value of porosity, absorption and sorptivity were reportedly higher as compared with other geopolymer systems. Correlation regression equations were proposed to validate the interrelation between physical parameters and mechanical strength. RHA geopolymer shows comparatively lower compressive strength as compared to Fly ash geopolymer.

• Applied Chemistry for Engineering
• /
• v.22 no.2
• /
• pp.214-218
• /
• 2011

Zeolite A was synthesized from coal fly ash by the microwave heating as well as the conventional heating method. The effects of reaction time, the amount of sodium aluminate, and the reaction temperature on the crystallization of zeolite A were investigated. The optimum crystallization time was about 3 to 6 h in the temperature range of $80{\sim}100^{\circ}C$. The amount of sodium aluminate was found to be optimum when the molar ratio $SiO_2/Al_2O_3$ of starting solution was in the range of 0.44 to 1.05 at above $90^{\circ}C$, However, The more amount of sodium aluminate was required to get zeolite A at $80^{\circ}C$. Although the rate of crystallization was slightly faster in the microwave heating than that in the conventional heating, the reaction time need to obtain fully crystallized zeolite A was similar in both methods. Therefore, the influence of the microwave heating was not so large compared with the conventional heating in the synthesis of zeolite A from coal fly ash.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.05a
• /
• pp.323-328
• /
• 2002

Rapid set accelerators are widely used in tunnel construction, however quality criteria of and dosage are not well established. The density and solid content of admixtures, setting time and compressive strength of paste and mortar with admixtures were investigated to establish the quality criteria. While the early strength of mortar with sodium-silicate, sodium-aluminate and calcium aluminate type admixtures that have high alkali content are very high, but long-term strength are low. Aggregates of shotcrete has to be carefully selected. Sodium-silicate type admixture need longer setting time than the others.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.2
• /
• pp.240-247
• /
• 2015

Zeolite A was prepared from coal fly ash upon NaOH fusion treatment, followed by hydrothermal treatment. The effects of treatment conditions such as NaOH/ash ratio, fusion temperature, the amount of sodium aluminate added, hydrothermal treatment temperature and time on the type and the crystallinity of zeolites were investigated. The optimal NaOH/ash weight ratio and fusion temperature to produce high crystalline zeolite A were 1.2 and $550^{\circ}C$, respectively. The dissolution of $Si^{4+}$ and $Al^{3+}$ from the fused fly ash was not affected by stirring time. The type of synthetic zeolites was found to be dependent on the amount of sodium aluminate added. The low amount of sodium aluminate favored zeolite X, while a single phase zeolite A was produced by increasing the amount sodium aluminate. Zeolite A was transformed into hydroxysodalite with increasing hydrothermal treatment time and temperature. A high crystalline zeolite A could be obtained by decreasing the temperature increasing time up to the reaction temperature.

• Advances in concrete construction
• /
• v.11 no.1
• /
• pp.81-88
• /
• 2021

Rice Husk Ash (RHA) geopolymer paste activated by sodium aluminate were characterized by X-ray diffractogram (XRD), scanning electron microscope (SEM), energy dispersion X-Ray analysis (EDAX)and fourier transform infrared spectroscopy (FTIR). Five series of RHA geopolymer specimens were prepared by varying the Si/Al ratio as 1.5, 2.0, 2.5, 3.0 and 3.5. The paper focuses on the correlation of microstructure with hardened state parameters like bulk density, apparent porosity, sorptivity, water absorption and compressive strength. XRD analysis peaks indicates quartz, cristobalite and gibbsite for raw RHA and new peaks corresponding to Zeolite A in geopolymer specimens. In general, SEM micrographs show interconnected pores and loosely packed geopolymer matrix except for specimens made with Si/Al of 2.0 which exhibited comparatively better matrix. Incorporation of Al from sodium aluminate were confirmed with the stretching and bending vibration of Si-O-Si and O-Si-O observations from the FTIR analysis of geopolymer specimen. The dense microstructure of SA2.0 correlate into better performance in terms of 28 days maximum compressive strength of 16.96 MPa and minimum for porosity, absorption and sorptivity among the specimens. However, due to the higher water demand to make the paste workable, the value of porosity, absorption and sorptivity were reportedly higher as compared with other geopolymer systems. Correlation regression equations were proposed to validate the interrelation between physical parameters and mechanical strength. RHA geopolymer shows comparatively lower compressive strength as compared to Fly ash geopolymer.

• Journal of the Korean Ceramic Society
• /
• v.23 no.6
• /
• pp.1-6
• /
• 1986

The hydration of $C_3A$ and $C_3A-CaSO_4$.$2H_2O$ was investigated with varying concentration (0.1-1.0%) of sodium gluconate solution. gluconate solution. Sodium gluconate accelerates cation dissolution from $C_3A$ for the first several minutes but depresses the rate of heat evolution in the course of $C_3A$ hydration. The hydration of $C_3A$ in the presence of sodium gluconate was modified such that the formation of the intermediate hydrate C4AH$\chi$ crystal was much reduced and most of the product became amorphous. The retardation of $C_3A-CaSO_4$.$2H_2O$ hydration in the presence of sodium gluconate was controlled by the competitive adsorption between gluconate anion and $SO_4^{-2}$ onto $C_3A$ surface.

• Advances in environmental research
• /
• v.5 no.2
• /
• pp.141-151
• /
• 2016

Large amounts of aluminum hydroxide ($Al(OH)_3$) exist in water purification sludge (WPS) because of the added aluminum coagulant in water treatment process. Notably, $Al(OH)_3$ is an amphoteric compound, can be dissolved in its basic condition using sodium hydroxide to form aluminate ions ($Al(OH)_4{^-}$). However, in a process in which pH is increasing, the humid acid can be dissolved easily from WPS and will inhibit the recovery and reuse of the dissolved aluminate ions. This study attempts to fix this problem by a novel approach to separate $Al(OH)_4{^-}$ ions using nanofiltration (NF) technology. Sludge impurity in a alkaline solution is retained by the NF membrane, such that the process recovers $Al(OH)_4{^-}$ ions, and significantly decreases the organic matter or heavy metal impurities in the permeate solution. The $Al(OH)_4{^-}$ ion is an alkaline substance. Experimental results confirm that a recovered coagulant of $Al(OH)_4{^-}$ ion can effectively remove kaolin particles from slightly acidic synthetic raw water.

• YAKHAK HOEJI
• /
• v.39 no.1
• /
• pp.68-77
• /
• 1995

Aluminum magnesium silicate was synthesized by reacting the mixed solutions of sodium aluminate and magnesium chloride with sodium silicate solution in this study. The optimal synthesis conditions based on the yield of the product has been attained according to Box-Wilson experimental design. It was found that the optimal synthetic conditions of aluminum magnesium silicate were as follows: Reaction temperature=$69~81^{\circ}C$; concentration of two reactants, sodium aluminate and magnesium chloride= 13.95~14.44 w/w%; molar concentration ratio of the two reactants, [NaAlO$_{2}$]/MgCl$_{2}$]=3.63~4.00; reaction time= 12~15 min; drying temp. of the product=$70~76^{\circ}C$. Aluminum magnesium silicate synthesized under the optimal synthesis condition was dispersed in 0.75, 1.0 and 1.5w/w% aqueous solution or suspension of six dispersing agents, and the Theological properties of the dispersed systems prepared have been investigated at $15^{\circ}C$ and $25^{\circ}C$ using Brookfield LVT Type Viscometer. The acid-consuming capacity of the most excellent product was 272~278 ml of 0.1N-HCl per gram of the antacid. The flow types of 5.0 w/w% aluminum magnesium silicate suspension were dependent upon the kind and concentration of dispersing agents added. The apparent viscosity of the suspension was generally increased with concentration of dispersing agents and was not significantly changed or decreased as the temperature was raised. A dispersing agent, hydroxypropyl cellulose suspension, exhibited an unique flow behavior of antithixotropy. The flow behavior of the suspension dispersed in a given dispersing agent not always coincided with that of the dispersing agent solution or suspension itself.