• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.284-284
• /
• 2015

반도체 Ball Grid Array(BGA)에 사용되던 종래의 Solder Ball은 Sn96.3 Ag3.0 Cu0.7의 용융솔더를 이용하여 제작하고 있다. 이는 SMT Reflow공정에서 BGA Ball의 퍼짐현상으로 인해 원래의 Ball Height에 영향을 미쳐 접합불량의 원인이 되고 있다. 이러한 문제를 해결하기 위해 Copper Core Ball위에 SnAgCu 삼원합금도금공정을 이용해 문제점을 해결하고자 했으며, 본 실험을 통해 구현한 CCSB를 이용해 SMT Reflow를 진행한 결과 종래의 BGA Ball보다 우수한 효과를 확인할 수 있었다.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.3
• /
• pp.143-148
• /
• 1993

Composition and microstructures of Silver-Tin alloy deposits from a pyrophosphate bath were studied under the D.C. electrolysis conditions. Cathode current efficiency and throwing power of alloy deposits de-creased with increasing current density. Tin content of Ag-Sn alloy deposits decreased noticeably with the cur-rent density and with decreasing pH. The preferred orientation of the deposits tended to change in sequence of (110)longrightarrow(111)longrightarrow(100) texture with increasing the cathode overpotential. The surface structure of alloy deposits showed the smooth surface structure with fine crystallites.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.84-87
• /
• 2003

Since Pb-free solder alloys have been used extensively in microelectronic packaging industry, the interaction between UBM (Under Bump Metallurgy) and solder is a critical issue because IMC (Intermetallic Compound) at the interface is critical for the adhesion of mechanical and the electrical contact for flip chip bonding. IMC growth must be fast during the reflow process to form stable IMC. Too fast IMC growth, however, is undesirable because it causes the dewetting of UBM and the unstable mechanical stability of thick IMC. UP to now. Ni and Cu are the most popular UBMs because electroplating is lower cost process than thin film deposition in vacuum for Al/Ni(V)/Cu or phased Cr-Cu. The consumption rate and the growth rate of IMC on Ni are lower than those of Cu. In contrast, the wetting of solder bumps on Cu is better than Ni. In addition, the residual stress of Cu is lower than that of Ni. Therefore, the alloy of Cu and Ni could be used as optimum UBM with both advantages of Ni and Cu. In this paper, the interfacial reactions of Sn-3.5Ag-0.7Cu solder on Ni-xCu alloy UBMs were investigated. The UBMs of Ni-Cu alloy were made on Si wafer. Thin Cr film and Cu film were used as adhesion layer and electroplating seed layer, respectively. And then, the solderable layer, Ni-Cu alloy, was deposited on the seed layer by electroplating. The UBM consumption rate and intermetallic growth on Ni-Cu alloy were studied as a function of time and Cu contents. And the IMCs between solder and UBM were analyzed with SEM, EDS, and TEM.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.85-91
• /
• 2002

Even though electroless Hi and Sn-Ag-Cu solder are widely used materials in electronic packaging applications, interfacial reactions of the ternary Ni-Cu~Sn system have not been known well because of their complexity. Because the growth of intermetallics at the interface affects reliability of solder joint, the intermetallics in Ni-Cu-Sn system should be identified, and their growth should be investigated. Therefore, in present study, interfacial reactions between electroless Ni UB7f and 95.5Sn-4.0Ag-0.5Cu alloy were investigated focusing on morphology of the IMCs, thermodynamics, and growth kinetics. The IMCs that appear during a reflow and an aging are different each other. In early stage of a reflow, ternary IMC whose composition is Ni$_{22}$Cu$_{29}$Sn$_{49}$ forms firstly. Due to the lack of Cu diffusion, Ni$_{34}$Cu$_{6}$Sn$_{60}$ phase begins growing in a further reflow. Finally, the Ni$_{22}$Cu$_{29}$Sn$_{49}$ IMC grows abnormally and spalls into the molten solder. The transition of the IMCs from Ni$_{22}$Cu$_{29}$Sn$_{49}$ to Ni$_{34}$Cu$_{6}$Sn$_{60}$ was observed at a specific temperature. From the measurement of activation energy of each IMC, growth kinetics was discussed. In contrast to the reflow, three kinds of IMCs (Ni$_{22}$Cu$_{29}$Sn$_{49}$, Ni$_{20}$Cu$_{28}$Au$_{5}$, and Ni$_{34}$Cu$_{6}$Sn$_{60}$) were observed in order during an aging. All of the IMCs were well attached on UBM. Au in the quaternary IMC, which originates from immersion Au plating, prevents abnormal growth and separation of the IMC. Growth of each IMC is very dependent to the aging temperature because of its high activation energy. Besides the IMCs at the interface, plate-like Ag3Sn IMC grows as solder bump size inside solder bump. The abnormally grown Ni$_{22}$Cu$_{29}$Sn$_{49}$ and Ag$_3$Sn IMCs can be origins of brittle failure.failure.

• Korean Journal of Dental Materials
• /
• v.44 no.4
• /
• pp.337-348
• /
• 2017

In this study, the effect of cooling rate control on the change in hardness of the multi-purpose Ag-Pd-Zn-In-Sn alloy during porcelain firing simulation and post-firing heat treatment was investigated, and the following results were obtained. Softening of the multi-purpose Ag-Pd-Zn-In-Sn alloy during porcelain firing simulation was suppressed by controlling the cooling rate. When the cooling rate was adjusted to stage 0(firing chamber moves immediately to upper end position), the alloy was softened during porcelain firing simulation, and the hardness was greatly increased by the additional post-firing heat treatment. When the cooling rate was adjusted to stage 3(firing chamber remains closed), the alloy was not softened even after porcelain firing simulation, and the hardness was apparently lowered by the additional post-firing heat treatment. The apparent increase in hardness in the post-firing heat treated alloy after porcelain firing simulation at cooling rate of stage 0 attributed to the active precipitation. The apparent decrease in hardness in the post-firing heat treated alloy after porcelain firing simulation at cooling rate of stage 3 attributed to the fact that the precipitates were solutionized into the matrix by the post-firing heat treatment.

• Journal of Welding and Joining
• /
• v.26 no.5
• /
• pp.43-48
• /
• 2008

Characteristics of Sn-1.7%Bi-0.7%Cu-0.6%In (hereafter, SBIC) lead-free solder was investigated in this study. The results from SBIC were compared to other lead-free solders such as Sn-3.5%Ag-0.7%Cu (hereafter, SAC), Sn-0.7%Cu (hereafter, SC), and lead-bearing Sn-37%Pb (hereafter, SP) alloy. Tensile properties of bulk solder, wettability, spreading index, bridge and dross were evaluated. As experimental results, tensile strength and elongation of SBIC was 62.5MPa and 21.5%, respectively. The tensile strength was comparable to that of SP solder. The wetting time of SBIC was 1.2 sec at $250^{\circ}C$, and its wetting properties including wetting force were as good as the SAC alloy. However, wettability of the SC was not so good as the SBIC and SAC. The spreading index of SBIC at $250^{\circ}C$ was 71 %, and it was similar level to those of SAC and SC solders. Bridging was not found for all solders of SBIC, SAC and SC in the range from 240 to $260^{\circ}C$. In dross test at $250^{\circ}C$ for an hour, the amount of dross produced from SBIC was about 57% compared to that from SAC.

• The Journal of Korean Academy of Prosthodontics
• /
• v.32 no.3
• /
• pp.378-395
• /
• 1994

The purpose of this study was to investigate the effect of various metal surface treatments and adhesive systems on the flexural bond strength of composite resin to Au-Ag-Cu-Pd alloy. The specimens were divided into nine groups by the combinations of surface treatment methods and adhesive systems. The types of surface treatment in this study were alumina blasting only, alumina blasting-Sn plating, alumina blasting-heating and three kinds of adhesive system used in this study were Silicoater system(Heraeus Kulzer GmbH,Germany), Superbond C & B(Sun Medical Co.,Ltd.,Japan) and Cesead opaque primer(Kurary Co.,Ltd.,Japan). After surface treatments and adhesive systems were applied, each specimen was built up with Dentacolor composite resin (Heraeus Kulzer GmbH,Germany). Four-point flexural bond strength was measured by Instron universal testing machine (Model 4301,U.S.A.) and modes of failure were observed by SEM(JEOL,SSM-840A,Japan). The obtained results were as follows: 1. The group that was bonded with Superbond C & B after alumina blasting-heating shelved the highest bond strength with significant difference among the groups, except the group with Cesead opaque primer after alumina blasting-Sn plating(P<0.05). 2. In the groups bonded with Cesead opaque primer, there was significant difference only in the bond strength between the alumina blasting-Sn plating group and alumina blasting group, where the former showed a higher bond strength(P<0.05). 3. In the groups bonded with Silicoater system, there were no significant differences in bond strength regardless of the surface treatment method(P<0.05). 4. In SEM evaluation, the groups of high bond strength, especially bonded with Superbond C & B after alumina blasting-heating and Cesead opaque primer after alumina blasting-Sn plating, revealed mainly cohesive-adhesive failure, whereas the others showed the tendency of adhesive failure.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2004.09a
• /
• pp.233-241
• /
• 2004

A new alloy definition will be presented concerning increasing demands for the board level reliability of miniaturized interconnections. The damage mechanism for LFBGA components on different board finishes is not quite understood. Further demands from mobile phones are the drop test, characterizing interface performance of different package constructions in relation to decreased pad constructions and therefore interfaces. The paper discusses the characterization of interfaces based on SnPb, SnPbXYZ, SnAgCu and SnAgCuInNd ball materials and SnAgCuInNd as solder paste, the stability after accelerated tests and the description of modified interfaces strictly related to the assembly conditions, dissolution behavior of finishes on board side and the influence of intermetallic formation. The type of intermetallic as well as the quantity of intermetallics are observed, primaliry the hardness, E modules describing the ability of strain/stress compensation. First results of board level reliability are presented after TCT-40/+150. Improvement steps from the ball formulation will be discussed in conjunction to the implementation of lead free materials In order to optimize ball materials for area array devices accelareted aging conditions like TCTs were used to analyze the board level reliability of different ball materials for BGA, LFBGA, CSP, Flip Chip. The paper outlines lead-free ball analysis in comparison to conventional solder balls for BGA and chip size packages. The important points of interest are the description of processability related to existing ball attach procedures, requirements of interconnection properties and the knowledge gained the board level reliability. Both are the primary acceptance criteria for implementation. Knowledge about melting characteristic, surface tension depend on temperature and organic vehicles, wetting behavior, electrical conductivity, thermal conductivity, specific heat, mechanical strength, creep and relaxation properties, interactions to preferred finishes (minor impurities), intermetallic growth, content of IMC, brittleness depend on solved elements/IMC, fatigue resistance, damage mechanism, affinity against oxygen, reduction potential, decontamination efforts, endo-/exothermic reactions, diffusion properties related to finishes or bare materials, isothermal fatigue, thermo-cyclic fatigue, corrosion properties, lifetime prediction based on board level results, compatibility with rework/repair solders, rework temperatures of modified solders (Impurities, change in the melting point or range), compatibility to components and laminates.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.4
• /
• pp.1-9
• /
• 2002

The metallurgical reaction properties between the pad consisted of 0.5 $\mu\textrm{m}$Au/5 $\mu\textrm{m}$Ni/Cu layers on a conventional ball grid array (BGA) substrate and In-15 (wt.%)Pb-5Ag solder ball were characterized during the reflow process and solid aging. During the reflow process of 1 to 5 minutes, it was observed that thin $AuIn_2$ or Ni-In intermetallic layer was formed at the interface of solder/pad. The dissolution rate of the Au layer into the molten solder was about $2\times 10^{-3}$ $\mu\textrm{m}$/sec which is remarkably low in comparison with a eutectic Sn-37Pb solder. After solid aging treatment for 500 hrs at $130^{\circ}C$, the thickness of $Ni_{28}In_{72}$ intermetallic layer was increased to about 3 $\mu\textrm{m}$ in all the conditions nevertheless the initial reflow time was different. These result show that In atoms in the solder alloy were diffused through the $AuIn_2$ phase to react with underlaying Ni layer during solid aging treatment. From the microstructural observation and shear tests, the reaction properties between In-15Pb-5Ag alloy and Au/Ni surface finish were analyzed not to trigger Au-embrittlement in the solder joints unlike Sn-37Pb composition.

• The Journal of Korean Academy of Prosthodontics
• /
• v.27 no.1
• /
• pp.143-179
• /
• 1989

To observe the bonding behavior of palladium-based alloys to porcelain; 1. Pd-Co binary alloy with the higher cobalt content, 2. Pd-Co binary alloy with the lower cobalt content, 3. Pd-Ag-Sn ternary alloy, 4. Pd-Ag binary alloy, 5. Pd-Cu-Au ternary alloy and 6. Pd-Cu binary alloy were made as 6 groups of experimental alloys. Each group of alloy was divided into 4 sub-groups such as one sub-group that was not degassed and three sub-groups that degassed for 5 minutes, 10 minutes and 15 minutes. On each specimen, weight changes after degassing, morphological changes of oxide layer by changing the degassing time, compositional changes at metal-ceramic interface and bond strength of metal-ceramic measured with planar shear test were observed and compared. The results of the present study allow the following conclusions to be drawn: 1. The alloy showing the greatest bond strength was Pd-Cu alloy without gold and bond strength was decreased by alloying gold to them. 2. Although Pd-Co alloy showed the most prominent oxidation behavior, bond strength of them to porcelain was not greatly high by the formation of porosities at metal-ceramic interfaces. 3. Likewise tin, cobalt formed the peaks on line profiles at metal-ceramic interface, however copper did not exhibit such peaks on line profiles. 4. Mainly, oxide layer on Pd-Co alloy was composed with cobalt, and for Pd-Co alloy with higher cobalt content the rise of bond strength was not significant by increased degassing time. 5. On Pd-Ag alloy not containing tin, during degassing for 15 minutes silver content was increased at metal-ceramic interface. 6. As an oxidized element, tin formed the oxide layers that widen their area by increasing the degassing time, while cobalt and copper showed the morphological changes of particle or crystal on oxide layer.