• Korean Journal of Materials Research
• /
• v.9 no.3
• /
• pp.288-294
• /
• 1999

In the flip chip interconnection using solder bump, the Under Bump Metallurgy (UBM) is required to perform multiple functions in its conversion of an aluminum bond pad to a solderable surface. In this study, various UBM systems such as $Al 1\mu\textrm{m} / Ti 0.2\mu\textrm{m} / Cu 5\mu\textrm{m}, Al 1\mu\textrm{m} / Ti 0.2\mu\textrm{m} / Cu 1\mu\textrm{m}, al 1\mu\textrm{m}/Ni 0.2\mu\textrm{m} / Cu 1\mu\textrm{m} and Al 1\mu\textrm{m}/Pd 0.2\mu\textrm{m} / Cu 1\mu\textrm{m}$ for flip chip interconnection using the low melting point eutectic 63Sn-37Pb solder were investigated and compared to their metallurgical properties. $100\mu\textrm{m}$ size bumps were prepared for using an electroplating process. The effects of the number of reflows and aging time on the growth of intermetallic compounds(IMC) were investigated. $Cu_6Sn_5$ and $Cu_3Sn$ IMC were abserved after aging treatment in the UBM system with thick coper $(Al 1\mu\textrm{m}/Ti 0.2\mu\textrm{m}/Cu 5\mu\textrm{m})$. However only the $Cu_6Sn_5$ was detected in the UBM system with $1\mu\textrm{m}$ thick copper even after 2 reflow and 7 day aging at $150^{\circ}C$. Complete Cu consumption by Cu-Sn IMC growth gives rise to a direct contact between solder inner layer such as Ti, Ni and Pd, and hence to possibly cause reactions between two of them. In this study, however, only for the Pd case, IMC of PdSn. was observed by Cu consumption. UBM interfacial reactions with s이der affected the adhesion strength ot s이der balls after s이der reflow and annealing treatment.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.76-76
• /
• 2009

눈부신 전자산업의 발달로 대부분의 전자제품이 다기능/경박단소화 되고 있어, 고밀도 실장 기술인 양면 표면실장과 고집적 패키징 기술인 패키지 적층 공정의 적용이 점차 확대되고 있다. 따라서 양면 표면실장 및 패키지 적층 공정에 사용되는 저온 접합용 무연 솔더 즉, $183^{\circ}C$(Sn-37Pb 공정 솔더 융점) 이하의 융점을 가지는 저온 무연 솔더에 대한 관심이 높아지고 있다. 한편, 미세피치 적용 분야에 있어 ACF/P를 이용한 COG 접속 분야 외에도 최근 저온 접합용 무연 솔더를 이용한 접속 분야가 각광을 받고 있다. 따라서, 접속피치 미세화에 대응하기 위해 스크린 인쇄성을 향상시킬 수 있는 저온 무연 솔더 paste 제조 및 공정 기술의 개발이 필요한 실정이다. 현재 대표적인 저온 무연 솔더 조성은 Sn-Bi계($138^{\circ}C$ 융점)와 Sn-In계($120^{\circ}C$ 융점)이다. 하지만, 이들 조성의 신뢰성 등에 있어 개선의 여지가 있으므로 이를 해결하기 위한 무연솔더 조성의 개발이 필요하다. 이와 같은 관점에서, 본 연구는 $137^{\circ}C$의 융점을 갖는 Sn-57.6Ag-0.4Ag 저온 무연 솔더 paste를 $217^{\circ}C$의 융점을 갖는 Sn-3.0Ag-0.5Cu 솔더 paste와 비교하여 인쇄성, reflow 특성, void inspection, 미세조직 관찰 및 underfill 적용 등의 실험을 실시하였다.

• Journal of Welding and Joining
• /
• v.19 no.3
• /
• pp.305-310
• /
• 2001

UBM-coated Si-wafer was fluxlessly soldered with glass substrate in $N_2$ atmosphere using plasma cleaning method. The bulk Sn-37wt.%Pb solder was rolled to the sheet of $100\mu\textrm{m}$ thickness in order to bond a solder disk by fluxless 1st reflow process. The oxide layer on the solder surface was analysed by AES(Auger Electron Spectroscopy). Through rolling, the oxide layer on the solder surface became thin, and it was possible to bond a solder disk on the Si-wafer with fluxless process in $N_2$ gas. The Si-wafer with a solder disk was plasma-cleaned in order to remove oxide layer formed during 1st reflow and soldered to glass by 2nd reflow process without flux in $N_2$ atmosphere. The thickness of oxide layer decreased with increasing plasma power and cleaning time. The optimum plasma cleaning condition for soldering was 500W 12min. The joint was sound and the thicknesses of intermetallic compounds were less than $1\mu\textrm{m}$.

• Journal of the Microelectronics and Packaging Society
• /
• v.13 no.1 s.38
• /
• pp.63-72
• /
• 2006

Mobile products, such as cellular phones, PDA and notebook, are subjected to many different mechanical loads, which include bending, twisting, impact shock and vibration. In this study, a cyclic bending test of the BGA package was performed to evaluate the fatigue life. Special bending tester, which was suitable for electronic package, was developed using an electromagnetic actuator. A nonlinear finite element model was used to simulate the mechanical bending deformation of solder joint in BGA packages. The fatigue life of lead-free (95.5Sn4.0Ag0.5Cu) solder joints was compared with that of lead-contained (63Sn37Pb). When the applied load to the specimen is small, the lead-free solder has longer fatigue life than lead-contained solder. The fatigue crack is initialized at the exterior solder joints and is propagated into the inner solder joints.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1740-1743
• /
• 2007

In this study, two types of fatigue tests were conducted. First, cyclic bending tests were performed using the micro-bending tester. A four-point bending test method was adopted, because it induces uniform stress fields within a loading span. Second, thermal fatigue tests were conducted using a pseudo power cycling machine which was newly developed for a realistic testing condition. The pseudo-power cycling method makes up for the weak points in a power cycling and a chamber cycling method. Two compositions of solder are tested in all test condition, one is lead-free solder (95.5Sn4.0Ag0.5Cu) and the other is eutectic lead-contained solder (63Sn37Pb). In the cyclic bending test, the solder that exhibits a good reliability can be reversed depending on the load conditions. The lead-contained solders have a longer fatigue life in the region where the applied load is high. On the contrary, the lead-free solder sustained more cyclic loads in the small load region. A similar trend was detected at the thermal cycling test. A three-dimensional finite element analysis model was constructed. A finite element analysis using ABAQUS was performed to extract the applied stress and strain in the solder joints. A constitutive model which includes both creep and plasticity was employed. Thermal fatigue was occurred due to the creep. And plastic deformation is main damage for bending failure. From the inelastic energy dissipation per cycle versus fatigue life curve, it can be found that the bending fatigue life is longer than the thermal fatigue life.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.206-208
• /
• 2006

The reliability of BGA (ball grid array) package with OSP (organic surface preservative) surface finish under thermal cycle was investigated by using SEM (scanning electron microscopy), EDS(energy dispersive spectroscopy), image tool and ball shear test. The IMCs (intermetallic compounds) were increased with increasing number of thermal cycles. However, the shear strengths of solder ball were decreased with increasing number of thermal cycles. The order of solders which had the highest shear strength as follow: Sn-3.5wt%Ag-0.7wt%Cu, Sn-0.7wt%Cu, Sn-37wt%Pb.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.225-227
• /
• 2005

Sn-8wt%Zn-3wt%Bi (이하, Sn-8Zn-3Bi) 솔더의 장기 신뢰성을 평가하기 위하여 열 충격 시험을 행하였다. 열 충격 시험은 $-40^{\circ}C$에서 $80^{\circ}C$범위에서 1000 사이클 동안 하였다. 접합 기판으로는 각각 OSP(Organic Solderability Preservative), Sn 그리고 Ni/Au 처리를 한 PCB(Printed Circuit Board) 패드를 사용하였다. 접합에 사용한 부품은 1608 Chip(Multi Layer Chip Capacitor, Chip Resistor) 으로 전극 부위에 Sn-37wt%Pb, Sn 도금하여 사용하였다. 솔더링 후 1608 Chip의 전단 강도와 솔더링부에서 미세조직 및 IMC(Inter Metallic Compound) 변화를 관찰하였다. 측정결과, Sn-8Zn-3Bi 솔더의 초기 전단 강도는 기판의 표면처리에 상관없이 약 40N 이상이었다. 그리고 열충격 시험 1000 사이클 후에는 모든 기판에서 2N 정도 약간의 강도 저하를 보였다.

• Journal of Welding and Joining
• /
• v.16 no.6
• /
• pp.77-85
• /
• 1998

Effects of non-cleaning and cleaning fluxes on the wetting properties and defects at flow soldered joints were investigated. Non-cleaning flux (R-type of 3.3% solid content) and cleaning flux (RMA-type of 15% solid content) were used. Wetting test was accomplished by wetting balance method with changing surface state of wetting specimen, CU. Sn-37%Pb solder was used for wetting test and flow soldering. As experimental results, the wetting time for vertical force from the surface tension being zero was mainly affected by surface state of the wetting specimen. Non-cleaning flux had a good wettability compared with cleaning flux. In case of non-cleaning flux, conveyor speed had a great affection to defects of bridge, icicle, and poor solder.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.5
• /
• pp.373-378
• /
• 2003

With increasing environmental concerns, application of lead-free solder and fluxless soldering process have been taken attention from the electronic packaging industry. Plasma treatment is one of the soldering methods for the fluxless soldering, and it can prevent environmental pollution cased by flux. On this study fluxless soldering process under $Ar-H_2$plasma using lead free solders such as Sn-3.5 wt%Ag, Sn-3.5 wt%Ag-0.7 wt%Cu and Sn-37%Pb for a reference was investigated. As the plasma reflow has higher soldering temperature than normal air reflow, the effects of UBM(Under Bump Metallization) thickness on the interfacial reaction and bonding strength can be critical. Experimental results showed in case of the thin UBM, Au(20 nm)/Cu(0.3 $\mu\textrm{m}$)/Ni(0.4 $\mu\textrm{m}$)/Al(0.4 $\mu\textrm{m}$), shear strength of the soldered joint was relatively low as 19-27㎫, and it's caused by the crack observed along the bonded interface. The crack was believed to be produced by the exhaustion of the thin UBM-layer due to the excessive reaction with solder under plasma. However, in case of thick UBM, Au(20 nm)/Cu(4 $\mu\textrm{m}$)/Ni(4 $\mu\textrm{m}$)/Al(0.4 $\mu\textrm{m}$), the bonded interface was sound without any crack and shear strength gives 32∼42㎫. Thus, by increasing UBM thickness in this study the shear strength can be improved to 50∼70%. Fluxed reflow soldering under hot air was also carried out for a reference, and the shear strength was 48∼52㎫. Consequently the fluxless soldering with plasma showed around 65∼80% as those of fluxed air reflow, and the possibility of the $Ar-H_2$ plasma reflow was evaluated.

• Journal of Applied Reliability
• /
• v.5 no.3
• /
• pp.327-342
• /
• 2005

전자 패키지가 열을 받을 때 회로기판과 칩의 열팽창계수 차이에 의해 발생되는 응력은 솔더 조인트의 파손에 영향을 미친다. 본 연구에서는 이 영향을 정량적으로 규명하기 위하여 열충격시험기를 이용해 얻어진 솔더 조인트의 전기저항 변화와 수명과의 상관관계를 규명하였고, BGA솔더 조인트의 수명을 정량적으로 도출하였다. 또한 Sn-3.5Ag-0.5Cu 무연 솔더와 63Sn-37Pb 유연 솔더를 위의 실험에 동시에 적용시켜 건전성을 FORM(first-order reliability method)과 Weibull Function Model을 이용해 비교하였다.