• Journal of the Korean Society of Propulsion Engineers
• /
• v.18 no.4
• /
• pp.67-73
• /
• 2014

The dry sliding wear behavior of graphite that is used as the sealing material to cut off hot gas was evaluated as a function of applied load, sliding speed and temperature. The reciprocating wear tests were carried out at room temperature and elevated temperatures. An attempt has been made to develop a mathematical model by response surface methodology and an analysis of variance technique was applied to confirm the validity of the developed model. Also, the wear mechanism was compared through the observation of the worn surface by SEM analysis.

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1138-1145
• /
• 1998

The sliding wear behavior of Ni-base hardfacing alloy, Deloro 50, was investigated at the contact stresses of 15ksi and 30ksi under the various wear environments. In air at room temperature, Deloro 50 showed lower wear resistance than Stellite 6 even at 15ksi due to the occurrence of severe adhesive wear. This seems to be caused by the lower hardness and work- hardening rate of Deloro 50 than those of Stellite 6. In water at room temperature, Deloro 50 showed as good wear resistance as Stellite 6 at 15ksi. It was considered to be due to that water could effectively prevent metal to metal contact through contacting asperities. However, Deloro 50 showed severe adhesive wear at 30ksi in water at room temperature. It seems to be that the water could not suppress adhesion wear at 30ksi. At $300^{\circ}C$ in air, Deloro 50 exhibited higher wear resistance than Stellite 6 even at 30ksi. It was considered that the oxide glaze layers formed on wear surface during sliding, effectively prevented direct metal-to-metal contacts.

• Tribology and Lubricants
• /
• v.11 no.4
• /
• pp.21-27
• /
• 1995

The effects of interface boundary strength on wear and wear transition during sliding have been investigated in silicon carbide ceramics. Three different microstructures, i.e., solid state sintered silicon carbide, liquid phase sintered silicon carbide and liquid phase sintered silicon carbide composite reinforced with TiB$_{2}$ particulates, were designed by hot pressing. Examinations of crack patterns and fracture modes indicated that interface boundaries were relatively strong between silicon carbide grains in the solid state sintered silicon carbide, intermediate in the liquid phase sintered silicon carbide and weak between silicon carbide grains and TiB$_{2}$ particles in the composite. Wear data and examinations of worn surfaces revealed that the wear behavior of these silicon carbide ceramics could be significantly affected by the interface strength. In the solid state sintered silicon carbide, the wear occurred by a grooving process. In the liquid phase sintered silicon carbide and composite, on the other hand, an abrupt transition in wear mechanism from initial grooving to grain pull-out process occurred during the test. The transition occurred significantly earlier in the composite than in the carbide.

• Tribology and Lubricants
• /
• v.38 no.4
• /
• pp.170-178
• /
• 2022

Mechanical surface treatment is an excellent approach widely used to modulate and improve the performance and service life of bearings, gears, and frictional joints. The main purpose of this study is to investigate and compare the effect of ultrasonic nanocrystal surface modification (UNSM) and wonder process craft (WPC) on the surface and tribological properties of SUJ2 bearing steel. The surface roughness and hardness of the untreated and treated (UNSM- and WPC-treated) specimens were measured and compared. Their tribological properties were evaluated using a micro-tribometer under grease-lubricated and dry conditions against itself. Surface hardness measurement results revealed that both the UNSM- and WPC-treated specimens had a higher hardness than that of the untreated specimen. The surface roughness of the untreated specimen was reduced after UNSM and WPC treatments. Abrasive wear mode was observed on the surface of the specimens worn under grease-lubricated conditions, while adhesive wear mode was found on the surface of the specimens worn in dry conditions. According to the tribological test results, the friction coefficient and wear rate of the untreated specimens were reduced by the application of both the UNSM and WPC treatments under grease-lubricated and dry conditions.

• Tribology and Lubricants
• /
• v.38 no.5
• /
• pp.199-204
• /
• 2022

This paper presents a numerical investigation of the influence of water molecule thickness on frictional behavior at the nanoscale using molecular dynamics simulation. Three different models, comprising water thin films of various thicknesses, were built, and indentation and sliding simulations were performed using the models. Various normal loads were applied by indenting the Si tip on the water film for the sliding simulation to evaluate the interplay between the water thin film thickness and the normal load. The results of the simulations showed that the friction force generally increased with respect to the normal load and thickness of the water thin film. The friction coefficient varied with respect to the normal load and the water film thickness. The friction coefficient was the smallest under a moderate normal force and increased with decreasing or increasing normal loads. As the water film became thicker, the contact area between the tip and water film became larger. Under well-lubricated conditions, the friction force was proportional to the contact area regardless of the water film thickness. As the normal force increased above a critical condition, the water molecules beneath the Si tip spread out; thus, the film could not provide lubrication. Consequently, the substrate was permanently deformed by direct contact with the Si tip, while the friction force and friction coefficient significantly increased. The results suggest that a thin water film can effectively reduce friction under relatively low normal load and contact pressure conditions. In addition, the contact area between the contacting surfaces dominates the friction force.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.26 no.3C
• /
• pp.171-180
• /
• 2006

To investigate the stabilizing effect of anchors against sliding, a series of the model test was carried out. An apparatus was developed to perform the model test of the slope reinforced by anchors. An instrumentation system has been applied on the anchors to measure the axial force during slope failure. The maximum stabilizing effect is revealed about 0.5% of the area ratio. The initial loss of anchor force is represented about 24% of initial jacking force. This result is equaled to the proposed range(10%~25%) of the field test result(Yun, 1997). The effective jacking force corresponds to 70% of the initial jacking force. Therefore, the initial jacking force should be determined more than 30% of the design jacking force. As the initial jacking force becomes increase, the reinforced slope is transferred to brittle failure behavior due to increasing the density of slope soils.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.205-206
• /
• 2002

In this paper we examined the contribution of mechanical and electrochemical factors in corrosive wear for Zr-alloy against $Al_2O_3$ ball in $Na_2SO_4$ solution. Normal load and the area of metallic specimen was varied to change the corrosion behavior. At the commence of sliding, the potential drop took place, which increased with load due to the great exposure of fresh surface. Wear volume was linearly proportional to load. The corrosion factor was about 15%. By increasing the Aa/Ac ratio, corrosion factor to total wear decreases and saturates above Aa/Ac=0.15.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.153-154
• /
• 2002

Wear map of silver coatings on AISI 52100 has been constructed to delineate the wear transition behavior with the change in operating conditions in various environments. Three main regimes were clearly identified: (i) elastic/plastic deformation of silver coating without failure. (ii) mild wear regime after initial failure of silver coating and (iii) severe wear regime. In the mild wear regime, the contact surfaces were covered with transfer layers of agglomerated wear particles. The transfer layer acted as a protective layer and resulted in low friction even after the initial failure of the coated films, whose characteristics were strongly dependent on both the operating and environmental conditions. Also, the existence of the critical sliding speed, above which no transfer layer was able to form, was discussed in the work.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.225-226
• /
• 2002

In this work, the friction and wear behavior under' various lubrication regimes were investigated. The objective of this work is to develop an Accelerated Life Test (ALT) method for the durability evaluation of a machine element which is operated under lubrication. Electric contact resistance and frictional forces were measured with respect to a wide range of the loads and speeds under various lubrication regimes using a pin-on-disk type tribotester. From the experimental results, it could be found that an effective and reliable ALT method could be achieved by controlling the lubrication regime through the measurements of friction coefficient and contact resistance with respect to load and sliding speed.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.185-186
• /
• 2002

Fretting of fuel rod cladding material, Zircaloy-4 tube, in PWR nuclear power plants must be reduced and avoided. Nowadays the introduction of surface treatments or coatings is expected to be an ideal solution to fretting damage since fretting is closely related to wear. corrosion and fatigue. Therefore. in this study the fretting wear experiment was performed using TiAlN coated Zircaloy-4 tube as the fuel rod cladding and uncoated Zircaloy-4 as on of grids, especially concentrating on the sliding component. Fretting wear resistance of TiAlN coated Zircaloy-4 tubes was improved compared with that of TiN coated tubes and uncoated tubes and fretting wear mechanisms were brittle fracture and plastic flow at lower slip amplitude but severe oxidation and spallation of oxidative layer at higher ship amplitude.