• Proceedings of the KSR Conference
• /
• 2001.05a
• /
• pp.408-415
• /
• 2001

Hardening agent has been the traditional material for surface soil stabilization of soft ground. The aim of this study if to determine optimal mixture ratio of hardening agent in accordance with the required design specifications. Hardening agent consists of fly ash, gypsum, slag and cement for the ettringite hydrates and if effective for early stabilization of unconsolidated soil. The raw ground material is the clay that is widely found here and there in Korea. In this study, preliminary tests were performed to get optimal mixture ratio of stabilizer ingredient and marine clay in Jinhae was used to get physical and chemical properties. Laboratory tests of 50 stabilized soils were performed to get optimal mixture ratio for 16-stabilizer materials of 6 types, and mixture ratio of stabilizer ingredient and marine clay was determined.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.329-332
• /
• 2004

This study aims to manufacture non-sintering cement(NSC) by adding phosphogypsum(PG) and waste lime(WL) to granulated blast furnace slag(GBFS) as sulfate and alkali activators. This study also investigates the pore structure of NSC Matrix. The result of experiment of pore structure properties, showed no considerable difference for total pore volume by cement mixing ratio but shows a large distinction in distribution of pore diameter. On the whole, pore-diameter of paste of NSC show that occupation ratio of pore diameter below 10mm is larger and is smaller than OPC and BFSC at pore diameter of over 10nm. Such a reason is that the hydrate like CSH gel and ettringite formed dense pore structure of NSC matrix.

• Journal of Ocean Engineering and Technology
• /
• v.15 no.1
• /
• pp.92-97
• /
• 2001

Hardening agents have been the traditional material for surface soil stabilization of soft ground. This study aims at determining the optimal mixture ratio of the hardening agent in accordance with the required design specifications. Hardening agents which consists of fly ash, gypsum, slag and cement for the ettringite hydrates is effective for early stabilization of unconsolidated soil. The raw ground material is the clay that is widely found in Korea. In this study, preliminary tests were performed to get an optimal mixture ratio of the stabilizer ingredient and marine clay from Jinhae was used to get physical and chemical properties. Laboratory tests of 50 stabilized soils were performed to get an optimal mixture ratio for 16-stabilizer materials of 6 types, and a mixture ratio of the stabilizer ingredient and marine clay was determined.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.305-312
• /
• 2018

This study is about the development of a non-sintered binder (NSB) which does not require a sintering process by using the industrial by-products Phosphogypsum (PG), Waste Lime (WL) and Granulated Blast Furnace Slag (GBFS). In this report, through SEM analysis of the NSB paste hardening body, micropore analysis of paste using the mercury press-in method and microstructure observation were executed to consider the influence of the formation of the pore structure and the distribution of pore volume on strength, and the following conclusions were reached. 1) Pore structure of NSB paste of early age is influenced by hydrate generation amount by GBFS and activator. 2) Through observing the internal microstructure of NSB binder paste, it was found that the strength expression at early age due to hydration reaction was achieved with a large amount of ettringite serving as the frame with C-S-H gel generated at the same time. It was confirmed that C-S-H gel wrapped around ettringite, and as time passed, the amount generated continually increased, and C-S-H gel tightly filled the pores of hardened paste, forming a dense network-type web structure. 3) For NSB-type cement, the degree of formation of gel pores below $10{\mu}m$ had a greater influence on strength improvement than simple pore reduction by charging capillary pores, and the pore size that had the greatest effect on strength was micropores with diameter below $10{\mu}m$.

• Journal of the Korea Concrete Institute
• /
• v.28 no.3
• /
• pp.299-308
• /
• 2016

This paper presents an investigation of the mechanical and microstructural properties on hardened samples that were synthesized using blended binder(fly ash(FA) and blast furnace slag cement(BFSC)), alkali activator and sea water or distilled water. Binders were prepared by mixing the FA and BFSC in different blend weight ratios of 6:4, 7:3 and 8:2. Sodium hydroxide and sodium silicate were used 5 wt% of binder, respectively, as an alkaline activator. The compressive strength and absorption were measured at the age of 3, 7 and 28 days, and the XRD, TGA and MIP tests were performed at the age of 28 days. An increase in the content of BFSC leads to an increase in the quantities of ettringite and C-S-H formed, regardless of the type of mixing water. And it also shows higher strength due to the reduction of pores larger than ~50 nm. All hardened samples in this study have common hydration products of C-S-H, $Ca(OH)_2$ and calcite. Hydrocalumite of all reaction products formed was only present in hardened sample mixed with sea water. For each FA/BFSC mixing ratio, the compressive strength of hardened sample mixed with sea water was similar to that mixed with distilled water. It is proposed that the slight increase of strength of samples mixed with sea water is mainly due to the presence of hydrocalumite phase containing chlorine ion, contributing to the change of total porosity and pore size distribution in samples.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.4
• /
• pp.443-450
• /
• 2021

The effects of blast furnace slag(BFS) and desulfurized gypsum(FDG) on the compressive strength of CFBA, and self-hydration of CFBA were studied. CFBA has self-hydrating and hardening properties, and it can be seen that the compressive strength of CFBA can be improved by using appropriate amounts of BFS and FDG. In addition, the self-hardening properties of CFBA are similar to the hydration reaction of 4CaO·Al₂O₃·Fe₂O₃ (C₄AF), a cement clinker mineral, and when free-CaO, CaSO₄ and CaCO₃ coexist, Compressive strength of CFBA is expressed by the formation of calcium carbo compounds and hydrates of ettringite, calcium silicate, and calcium aluminate.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.5
• /
• pp.389-396
• /
• 2014

The set accelerator used for shotcrete at high pH environment often causes the dusting problem in practice. In this research, a slurry-type set accelerator was developed to avoid this problem and its effectiveness was investigated by applying it to shotcrete mortars. Set time, stiffening, compressive strength, and chloride ion penetration resistance were examined with different amounts of slag, used as partial replacement of cement. According to the experimental results, it was found that the earlier responses such as set time, stiffening, and 1-day compressive strength were probably affected by the amount of ettringite, formulated by the hydration between C12A7 and calcium sulfate polymorphs present in blast furnace slag. Whereas, it is believed that the result of compressive strength after 3 days was attributed to the hydration of tricalcium silicates. As for the results of a chloride ion penetration test, the partial replacement of cement with slag significantly reduced the total charge passed through the shotcrete mortar.

• Journal of the Korean Ceramic Society
• /
• v.39 no.7
• /
• pp.680-686
• /
• 2002

The solidification/stabilization mechanism of each cementious material was investigated. It was found that when $C_3$S was hydrated , the Pb element could be transferred to the insoluble Ca[Pb(OH)$_3$.$H_2O$]$_2$and the Cr element to the CaCr $O_4$$H_2O$. The addition of heavy metal tends to delay the hydration until initial 7 days. The Pb element as also delayed the hydration and the Cr element was substituted for the ettringite. On the occasion of the hydration of $C_4$ $A_3$ $S^{S}$, the Pb and Cr ions were solidified/stabilized by the substitution into the ettringite and/or monosulfate. Leaching of the Pb, Cr and Zn elements in the solidified material was extremely little, indicating that heavy metals were effectively solidified/stabilized in the hydrated cementious materials. Solidification/stabilization of heavy metal ions in the industrial wastes such as the STS, BF and COREX sludge was investigated. In case of the mixing ratio of cement and slag was 3 : 7, leaching of hazardous heavy metal ions was very little, indications that the solidification and stabilization was very successful.l.

• Journal of the Korean Ceramic Society
• /
• v.53 no.2
• /
• pp.206-214
• /
• 2016

This study aims to produce dolomitic hydraulic lime (D-NHL) using domestic low grade dolomitic limestone and to determine the effect of adding blast furnace slag (BFS) and gypsum as part of an investigation of the hydration properties of D-NHL to increase the mechanical properties. The main mineral phases of D-NHL as a hydraulic lime binder were $Ca(OH)_2$, $Mg(OH)_2$, $C_2S$, $C_3S$, and MgO residues. $Ca(OH)_2$ transformed into $CaCO_3$ in D-NHL paste over the period of 28 days, but the carbonation of $Mg(OH)_2$ and the hydration of $C_2S$ did not occur until hydration, after 28 days. Through an investigation of the hydration properties of D-NHL pastes mixed with BFS and gypsum, Al-based compounds such as calcium aluminate hydrates ($C_4AH_{13}$) and ettringite were observed at early hydration time. The compressive strength was improved due to the increased quantities of these hydration products. These results show that good performance results from the application of dolomitic hydraulic lime and that a high value product can be made from domestic waste materials.

• Journal of the Korean Ceramic Society
• /
• v.39 no.12
• /
• pp.1133-1137
• /
• 2002

The cement for solidification of the toxic waste was fabricated using a mixture of the waste concrete powder and blast furnace slag in the ratio of 1:1 and its hydrate morphology and compressive strength of the sample were evaluated in order to apply to the solidification of the COREX sludge. The X-ray diffraction analysis of the sample which prepared by the addition of 10% Portland cement and hemihydrate showed the presence of $Ca(OH)_2$, ettringite, gel-phase and C-S-H hydrate. Compressive strength of the sample exhibited enough high to use as a solidification cement. The strength of the sample was over 140 kgf/$m^2$ in 7 days in case of solidification of the COREX sludge and the sample possess sufficient morphology for the solidification and stabilization of the waste sludge.