• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.465-472
• /
• 1988

Alpha alumina powder with fine particle size and narrow particle size distribution was prepared by precipitation method using Al2(SO4)3.18H2O as a starting material. The alpha alumina powder was prepared by calcining aluminum hydroxide which was formed under various pH values. The sinterabilityof alpha alumina powder and the effect of MgO on the sinterability of alpha alumina powder were investigated. The sinterability of alpha alumina powder was the order of pH=10≒pH11>pH=7≒pH9, and alpha alumina obtained from boehmite which was prepared by precipitation method reached to 97.5% of theoretcal density by the pressureless sintering. The effect of MgO on volume shrinkage of alumina was very slight in the initial sintering stage but remarkable in the final sintering stage. It was also found that MgO controlled effectively the grain growth of alumina.

• Journal of the Korean Ceramic Society
• /
• v.31 no.8
• /
• pp.841-848
• /
• 1994

The sintering behavior of La-modified PbTiO3 ceramics was investigated in order to improve the poor sinterability of PbTiO3. Addition of La improved the sinterability. It was confirmed that this improvement was due to the decrease in tetragonality ratio c/a of crystal lattice. The variations of dielectric constant and pyroelectric coefficient were measured with temperature. It was observed that with the increase of La content, Curie temperature decreased and dielectric constant at room temperature increased. La-modified PbTiO3 ceramics had smaller pyroelectric figure of merits than those of pyroelectric materials in use. The effects of grain size on dielectric and pyroelectric properties were also investigated. The change of grain size had effect on maximum dielectric constant and pyroelectric coefficient, but is had little effect on pyroelectric figure of merit at room temperature. The closer examination near ferro-paraelectric phase transition temperature revealed that the behavior of phase transition approached a more relaxor character with the increase of La content and the decrease of grain size.

• Journal of the Korean Ceramic Society
• /
• v.30 no.10
• /
• pp.845-851
• /
• 1993

Low firing temperature substrate were synthesized through tape casting and sintering of glass with cordierite composition and then their properties were investigated. Even though the dielectric properties and XRD patterns of substrates, obtained by tape casting and sintering at 900~100$0^{\circ}C$ for various periods, were similar to those of substrates obtained by dry pressing, the sinterability was enhanced. The substrates were thin and the size was 0.6$\times$50$\times$50mm. From the results of dielectric properties, the sinterability and X-ray diffraction pattern, the proper condition for cofiring process with conductor, Cu, was 90$0^{\circ}C$ for 1h. The properties of the substrate are as follows; the dielectric constant was 5.31(at 1MHz), the dissipation factor was 0.0028, the apparent porosity was 0.28% and the main crystalline phase was $\alpha$-cordierite.

• Journal of the Korean Ceramic Society
• /
• v.32 no.2
• /
• pp.155-162
• /
• 1995

Solid oxide electrolytes of the MCe1-xGdxO3-x/2 (M: Ba, Mg. x=0.0-0.20) system were prepared using powders synthesized by the "liquid mix" method and calcined from the cross-linked polyacrylic polymer. The specimens were analyzed using XRD and SEM with EDX, and the sintering behavior of the electrolytes and their electrical conductivity were also studied. Although Mg-cerate is relatively inferior to Ba-cerate in the sinterability and chemical homogenity(EDX analysis data), both the Ba- and the Mg-cerate electrolytes at 80$0^{\circ}C$ show their maximum conductivities at x=0.10 and their values are in the same order of magnitude, i.e., 3.5$\pm$0.17.10-2(ohm.cm)-1.ohm.cm)-1.

• Journal of Powder Materials
• /
• v.12 no.4 s.51
• /
• pp.296-302
• /
• 2005

In order to improve mechanical properties, the hypereutectic Al-20 wt%Si based prealloy powder was prepared by gas atomization process. Microstructure and compressibility of the atomized Al-Si powder were investigated. The average powder size was decreased with increasing the atomization gas pressure. Size of primary Si particles of the as-atomized powder was about $5-8\;\mu{m}$. The as-atomized Al-Si powder such as AMB 2712 and AMB 7775 to increase compressibility and sinterability. Relative density of the mixed powder samples sintered at $600^{\circ}C$ was reached about 96% of a theoretical density.

• Journal of the Korean Ceramic Society
• /
• v.29 no.1
• /
• pp.1-8
• /
• 1992

The effect of CaO impurity on the microstructural evolution during the sintering of ultrapure alumina(>99.999%) was studied under "clean" firing conditions. The sinterability of undoped alumina was low, but its microstructure was maintained uniform. In the case of CaO-doped alumina, the distribution of grain size and that of grain boundary dihedral angle became wider, and facetted pores observed frequently. When MgO was doped in addition to CaO, the sinterability increased drastically and the uniform microstructural characteristics resumed. This study suggests that the effect of CaO is to induce inhomogeneous microstructures presumably by anisotropic segregation to grain boundaries and pore surfaces, and that MgO suppresses the anisotropic segregation of Ca.

• Journal of the Korean Ceramic Society
• /
• v.30 no.6
• /
• pp.429-432
• /
• 1993

Cr3C2 material is characterized by high chemical stability and poor sinterability with low strength [50~150MPa]. In his study, low melting temperature nickel powder was used to improve sinterability as well as strength. In addition, molydenum particles were added to the Ni-bonded Cr3C2 cermet pseudomatrix to increase resistance to fracture. The specimens made by hot-pressing under vacuum and strength was measured by 4-point bending. Indentation cracking and fractographic examination were conducted to study the interaction of the indentation cracks with the reinforcing particles. Toughening mechanisms and failure will be discussed in terms of crack/particle interactions and compared with previous works.

• The Korean Journal of Ceramics
• /
• v.1 no.2
• /
• pp.101-105
• /
• 1995

Electrical discharge machinable $Si_3N_4$ was fabricated with the addtion of 20-60 vol% TiN by gas pressure sintering. Their sinterability, microstructure, mechanical and electrical properties were characterized as a function of the TiN content. The addition of TiN up to 20 vol% increased the flexural strength and fracture toughness as compared with those of the monolithic Si3N4. For the TiN content higher than 40 vol%, the electrical resistivity was lower than $1062\Omega$.cm. The $Si_3N_4$ with the addition of 40 vol% of TiN appears to have the optimum considerable sinterability, mechanical and electrical properties, and machinability. A microstructural analysis showed that the enhanced toughening was due to the crack deflection.

• The Korean Journal of Ceramics
• /
• v.5 no.3
• /
• pp.217-223
• /
• 1999

Proten-conductive $SrZr_{0.95} Y_{0.05} O_{2.975}$ powder was prepared by citrate gel method its characteristics and sinterability were investigated. Amorphous gel could be obtained from a citric acid solution that $SrCO_3$ and metal nitrates were dissolved. The initial decomposition of the gel proceeded up to $250^{\circ}C$, followed by combustion of its decomposition products in the temperature range from $250^{\circ}C$ to $500^{\circ}C$. A well-crystallized perovskite phase with a stoichiometric composition after calcination at $1000^{\circ}C$. Sintering green compacts of this powder for 6 h showed a considerable densification to start at $1200^{\circ}C$ and resulted in 86.8% and 96.5% relative densities at $1400^{\circ}C$ and $1600^{\circ}C$, respectively. Whereas, the powder compacts prepared by solid state reaction had much lower relative densities, 73% at $1400^{\circ}C$ and 92% at $1600^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.32 no.10
• /
• pp.1212-1218
• /
• 1995

Al2O3-coated SiC composite powder and mechanically mixed Al2O3-SiC composite powder were synthesized using Al-isopropoxide and commercial SiC as the starting materials. Experiment results showed that the sinterability of Al2O3-coated SiC composite powder was more improved than the mechanically mixed Al2O3-SiC composite powder by the effect of homogeneous coating of alumina around SiC particles. Hence, the mechanical properties of the former was also much more improved than the latter.