• Journal of Ocean Engineering and Technology
• /
• v.21 no.5
• /
• pp.33-38
• /
• 2007

The welding methods have been applied in the most structural products from multi-field of automobile, ship construction and construction, and so on. The structure steel must have enough strength of structure. In this study, SS400 steel and STS304 steel were used to estimate the corrosion characteristics of the weld thermal cycle simulated HAZ. To evaluate the corrosion characteristics, also, the materials with two conditions were used in 3.5% NaCl. The one is to the drawing with diameter of ${\Phi}10$ and the other is to the residual stress removal treatment. The electrochemical polarization test and immersion test were carried out. From test results, corrosion potential, corrosion current density, weight loss ratio and corrosion rate were measured. In the kinds of SS400 steels, corrosion potential of weld thermal cycle simulated specimens after the heat treatment showed somewhat the direction of noble potential. And in the base metal to be drawing weight loss ratio and corrosion rate occurred higher than the other kinds. In the kinds of STS304 steels, the result of base metal to be drawing was similar to results of SS400 steels, too. Two kinds of $750^{\circ}C$ and $1300^{\circ}C$ of weld thermal cycle simulation after the heat treatment were rather higher than the other kinds in weight loss ratio and corrosion rate.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.9 s.180
• /
• pp.2381-2386
• /
• 2000

Surface replication is playing an important role in the assessment of creep damage and remaining life of high temperature components. As the replication procedures, however, have not been standardized in domestic industry, its standardization is proposed in this study. For this purpose, the 2.25Cr-IMo steel was heat treated(5 min at 1,300 0C and oil quenched) to produce a simulated HAZ microstructure, and crept in air at 575 0C and under 120 MPa to produce artificial cavities. Then, the effect of surface preparation procedures on the quality of replicas was investigated using this sample. As a result, it was demonstrated that the presence of cavities may be observed readily or missed depending on the surface preparation procedures followed. Therefore it is essential to repeat three polishing/etching cycles at least in order to reveal cavitation damage accurately, even though it may be tedious or time-consuming.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.390-396
• /
• 2000

The dynamic elastic constants of the simulated weld HAZ (heat-affected zone) of SA 508 Class 3 reactor pressure vessel (RPV) steel were investigated by resonant ultrasound spectroscopy (RUS). The resonance frequencies of rectangular parallelepiped samples woe calculated from the initial estimates of elastic stiffness $c_{11},\;c_{12}\;and\;c_{44}$ with an assumption of isotropic property, dimension and density. Through the comparison of calculated resonant frequencies with the measured resonant frequencies by RUS, very accurate elastic constants of SA 508 Class 3 steel were determined by iteration and convergence processes. Clear differences of Youngs modulus and shear modulus were shown from samples with different thermal cycles and microstructures. Youngs modulus and shear modulus of samples with fine-grained bainite were higher than those with coarse-grained tempered martensite. This tendency was confirmed from other results such as micro-hardness test.

• Journal of Welding and Joining
• /
• v.34 no.6
• /
• pp.47-54
• /
• 2016

Post-Weld Heat Treatment (PWHT) cracking susceptibility in the weld heat-affected zone (HAZ) of reduced activation ferritic-martensitic (RAFM) steels was evaluated through stress-rupture tests. 9Cr-1W based alloys including different C, Ta and Ti content were prepared. The coarse grained heat-affected zone (CGHAZ) samples were simulated with welding condition of 30 kJ/cm heat input. CGHAZ samples consisted of martensite matrix. Stress rupture experiments were carried out using a Gleeble simulator at temperatures of $650-750^{\circ}C$ and at stress levels of 125-550 MPa, corresponding to PWHT condition. The results revealed that PWHT cracking resistance was improved by Ti addition, i.e., Ti contributed to the formation of fine and stable MX precipitates and suppression of coarse M23C6 carbides, resulting in improvement of stress rupture ductility. Meanwhile, rupture strength increased with increasing solute C content.