• Journal of Welding and Joining
• /
• v.31 no.3
• /
• pp.31-38
• /
• 2013

The transition of serrated grain boundary and its effect on liquation behavior in the simulated weld heat-affected zone (HAZ) have been investigated in a wrought Ni-based superalloy Alloy 263. Recently, the present authors have found that grain boundary serration occurs in the absence of adjacent coarse ${\gamma}^{\prime}$ particles or $M_{23}C_6$ carbides when a specimen is direct-aged with a combination of slow cooling from solution treatment temperature to aging temperature. The present study was initiated to determine the interdependence of the serration and HAZ property with a consideration of this serration as a potential for the use of a hot-cracking resistant microstructure. A crystallographic study indicated that the serration led to a change in grain boundary character as special boundary with a lower interfacial energy as those terminated by low-index {111} boundary planes. It was found that the serrated grain boundaries are highly resistant to boron enrichment, and suppress effectively grain coarsening in HAZ. Furthermore, the serrated grain boundaries showed a higher resistance to susceptibility of liquation cracking. These results was discussed in terms of a significant decrease in interfacial energy of grain boundary by the serration.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.8 no.2
• /
• pp.97-103
• /
• 1984

Post weld heat treatment(PWHT) of weldment of the low alloy steel is carried out to remove residual stress existing in weldment and to improve fracture toughness, but it is often observed that there occurs grain boundary failure and that fracture toughness decreases in weld heat affected zone(HAZ)because of PWHT. In this paper, the effect of heating rate and holding time of PWHT on fracture toughness were evaluated by crack opening displacement (CDD)test and micro-hardness test under the constant stress simulated residual stress in HAZ of Cr-Mo steel. The experimental results are as follow; (1)Transition temperature of weld HAZ after PWHT was dependent upon heating rate greater than holding time, and fracture toughness was decreased with an increase of the heating rate. (2)Softening ration of the notch tip was increased with holding time within one hour and saturated after one hour, but under applied stress it was increasing continuously. (3)The average hardness value in weld HAZ was increased with heating rate of PWHT.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.422-425
• /
• 2005

This study predicts the heat-affected zone (HAZ) after electrical discharge machining. To predict HAZ, the temperature distribution is calculated using FEM. Heat flux is calculated from electrical energy, and it can be assumed Gaussian distribution. Plasma channel expands as time goes. Copper and NAK80 are used as the workpiece material. The depth of HAZ in simulation is determined by temperature distribution. The simulation results were compared with a developed actual single discharge crater. Through investigating the cross section of simulated & actual craters, the depth of HAZ in simulation and experiment are compared. Simulation model can predict the crater shape.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.17-22
• /
• 1997

ASME SA508 Class 3 원자로압력용기강을 대상으로, 용접열영향부(heat affected zone, HAZ)의 최고온도(peak temperature) 등온분포도(isothermal diagram)를 작성 및 해석하였고, 재현(simulated) 열영향부 시험편을 제작하여 미세조직검사 및 기계적특성 시험을 실시하였다. 그 결과, 최고온도 등온분포도를 이용하여, 미소열영향부(subzone of HAZ)의 미세조직(microstructure)에 미치는 예열(preheat)온도와 용접입열량(weld heat input)의 크기 효과를 예측할 수 있었다. 또한, 재현 HAZ 의 기계적특성 시험결과, 용접용융선(fusion line) + 1 mm 이내의 위치로 대표되는 열 cycle 조건에서는 모재보다 양호한 강도와 인성을 보였고, 용접용융선 + 2~3mm부근에서 가장 미세한 조직(fine tempered lower bainite)과 우수한 충격인성을 나타냈다. 한편, 용접용융선 + 약 5mm 위치에서의 열 cycle 을 재현한 시험편에서는 미세조직의 변화(spheroidization of carbides)와 함께 인성 및 기계적 특성이 저하하여 모재보다 낮은 값을 보이는 것을 발견할 수 있었다.

• Proceedings of the KWS Conference
• /
• 2000.04a
• /
• pp.267-271
• /
• 2000

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.11 no.2
• /
• pp.314-321
• /
• 1987

Post weld heat treatment (PWHT) of weldment of the low alloy Cr-Mo steel, in general, is carried out not only to remove residual stress and hydrogen existing in weldment but to improve fracture toughness of weld heat affected zone (HAZ). There occur some problems such as toughness decrement and stress relief cracking (SRC) in the coarse grained region of weld HAZ when PWHT is practiced. Especially, embrittlement of structure directly relates to the mode of fracture and is appeared as the difference of fracture surface such as grain boundary failure. Therefore, in this paper, the effect of heating rate on PWHT embrittlement under the various kinds of stresses simulated residual stress in weld HAZ was evaluated by COD fracture toughness test and observation of fracture surface. Fracture toughness of weld HAZ decreased with increment of heating rate under no stress, but it was improved to increment of heating rate under the stress. Grain boundary failure didn't almost appear at the heating rate of 600.deg.C/hr but it appeared from being the applied stress of 294 MPa at 220.deg.C/hr and 196 MPa at 60.deg.C/hr.

• Advances in materials Research
• /
• v.7 no.3
• /
• pp.195-201
• /
• 2018

High Strength low alloy steels containing various levels of C, Nb and Mn were used and for each of which, a simulated double thermal cycle was applied with the same first peak temperature and different second peak temperatures to produce HAZ microstructure corresponding to multi-pass weld. Effect of double cycle second temperature on the microstructure was observed and compared with single cycle results obtained from previous works, it was found that the percentage of martensite austenite constituent (MA) increases by Nb addition for all steels with the same Mn content and the increase in Mn content at the same Nb content shows an increase in MA area fraction as well. MA area fraction obtained for the double cycle is larger than that obtained for the single cycle for all steels used which imply that MA will have great role in the brittle fracture initiation for double cycle and the inter-pass temperature should be controlled for medium and high-carbon Mn steel to avoid large area fraction of MA. The beneficial effects of Niobium obtained in single pass weld were not observed for the double cycle or multi pass welds.

• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.1
• /
• pp.53-64
• /
• 1995

A study was made to characterize the microstructures and mechanical properties of the base metal and the heat-affected zone(HAZ) in Cu-bearing HSLA-100 steel. The Gleeble thermal/mechanical simulator was used to simulated the weld HAZ. The relationship between microstructure and toughness of HAZ was studied by impact test, O. M, SEM, TEM, and DSC. The toughness requirement of military specification value was met in all test temperatures for the base metal. The decrease of HAZ toughness comparing to base plate is ascribed to the coarsed-grain and the formation of bainite. Obliquely sectioned Charpy specimens show that secondary crack propagate easily along bainite lath. Improved toughness(240J) at HAZ of $Tp_2=950^{\circ}C$ is due to the fine grain, and reasonable toughness(160~00J) in the intercritical reheated HZA is achieved by the addition of small amount of carbon which affects the formation of "M-A". Cu precipitated during ageing for increasing the strength of base metal is dissolved during single thermal cycle to $1,350^{\circ}C$ and is precipitated little on cooling and heating during subsequent weld thermal cycle. Thus, the decrease of toughness does not occur owing to the precipitation of Cu.

• Proceedings of the KWS Conference
• /
• 1997.10a
• /
• pp.160-162
• /
• 1997

• Journal of Welding and Joining
• /
• v.33 no.6
• /
• pp.6-12
• /
• 2015

Thermal fatigue life of the automobile exhaust manifold is directly affected by the restraint force according to the structure of exhaust system and bead shape of the welded joints. In the present study, the microstructural changes and precipitation behavior during thermal fatigue cycle of the 18wt% Cr ferritic stainless steel weld heat affected zone (HAZ) considering restraint stress were investigated. The simulation of weld HAZ and thermal fatigue test were carried out using a metal thermal cycle simulator under complete constraint force in the static jig. The change of the restraint stress on the weld HAZ was simulated by changing the shape of notch in the specimen considering the stress concentration factor. Thermal fatigue properties of the weld HAZ were deteriorated during cyclic heating and cooling in the temperature range of $200^{\circ}C$ to $900^{\circ}C$ due to the decrease of Nb content in solid solution and coarsening of MX type precipitates, laves phase, $M_6C$ with coarsening of grain and softening of the matrix. As the restraint stress on the specimen increased, the thermal fatigue life was decreased by dynamic precipitation and rapid coarsening of the precipitates.