• Journal of the Korean institute of surface engineering
• /
• v.43 no.3
• /
• pp.148-153
• /
• 2010

Transparent conducting films having a hybrid structure of GZO/Metal/GZO were prepared on glass substrates by sequential deposition using DC magnetron sputtering. Silver, copper, aluminum and zinc thin films were used as the intermediate metal layers in the hybrid structure. The electrical and optical properties of hybrid transparent conducting films were investigated with varying the thickness of metal layer or GZO layers. With increasing the metal thickness, hybrid films showed a noticeable improvement of the electrical conductivity, which is mainly dependent on the electrical property of the metal layer. GZO(40 nm)/Ag(10 nm)/GZO(40 nm) film exhibits a resistivity of $5.2{\times}10^{-5}{\Omega}{\cdot}cm$ with an optical transmittance of 82.8%. For the films with Zn interlayer, only marginal reduction in the resistivity was observed. Furthermore, unlike other metals, hybrid films with Zn interlayer showed a decrease in the resistivity with increasing the GZO thickness. The optimal thickness of GZO layer for anti-reflection effect at a given thickness of metal (10 nm) was found to be critically dependent on the refractive index of the metal. In addition, x-ray diffraction analysis showed that the insertion of Ag layer resulted in the improvement of crystallinity of GZO films, which is beneficial for the electrical and optical properties of hybrid-type transparent conducting films.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.443-443
• /
• 2008

본 연구에서는 Ga-doped ZnO(GZO)-Ag-GZO 다층 투명전극을 Dual DC magnetron sputtering system을 이용 하여 유리기판 위에 상온에서 제작하여 Ag 두께에 따른 전기적, 광학적, 구조적 특성변화를 조사하였다. Hall effect measurement와 UV/Vis spectrometer로 전기적, 광학적 특성을 분석하였으며, X-ray diffraction(XRD)와FE-SEM분석을 통해 결정성과 표면 특성을 조사하였다. FE-SEM 분석결과 island 형태에서 continuous layer로 박막의 형상이 바뀌면서 다층 투명전극의 전기적, 광학적 특성에 영향을 미치는 것을 알 수 있었다. 본 실험에서 Ag 두께 12 nm에서 가장 최적화되어 유리기판위에 상온에서 증착되었음에도 불구하고 $5.5{\times}{\times}10^{-5}\Omega$-cm, $6\Omega$/sq. 의 매우 낮은 면저항과 비저항을 각각 나타내었고 550 nm 파장에서 87 % 의 높은 광 투과도를 나타내었다. 또한 두께 12 nm의 Ag가 삽입된 다층 투명전극을 polyethylene terephthalate (PET) 기판위에 성막하여 Bending test를 실시하여 0.1% 이하의 매우 낮은 저항변화를 확인함으로써 플렉시블 기반의 디스플레이나 태양전지의 투명 전극으로서의 응용 가능성을 확인하였고 마지막으로 최적화된 다층 투명전극을 유기물태양전지의 애노드에 적용하여 기존 ITO 애노드를 대체할 수 있는 투명전극으로서의 가능성을 제시하였다.

• Nuclear Engineering and Technology
• /
• v.55 no.6
• /
• pp.2139-2146
• /
• 2023

During reactor operation, the divertor must withstand unprecedented simultaneous high heat fluxes and high-energy neutron irradiation. The extremely severe service environment of the divertor imposes a huge challenge to the bonding quality of divertor joints, i.e., the joints must withstand thermal, mechanical and neutron loads, as well as cyclic mode of operation. In this paper, potassium-doped tungsten (KW) is selected as the plasma facing material (PFM), oxygen-free copper (OFC) as the interlayer, oxide dispersion strengthened copper (ODS-Cu) alloy as the heat sink material, and reduced activation ferritic/martensitic (RAFM) steel as the structural material. In this study, a vacuum brazing technology is proposed and optimized to bond Cu and ODS-Cu alloy with the silver-free brazing material CuSnTi. The most appropriate brazing parameters are a brazing temperature of 940 ℃ and a holding time of 15 min. High-quality bonding interfaces have been successfully obtained by vacuum brazing technology, and the average shear strength of the as-obtained KW/Cu and ODS-Cu alloy joints is ~268 MPa. And a fabrication route for manufacturing the flat-type divertor target based on brazing technology is set. For evaluating the reliability of the fabrication technologies under the reactor relevant condition, the high heat flux test at 20 MW/m² for the as-manufactured flat-type KW/Cu/ODS-Cu/RAFM mockup is carried out by using the Electron-beam Material testing Scenario (EMS-60) with water cooling. This paper reports the improved vacuum brazing technology to connect Cu to ODS-Cu alloy and summarizes the production route, high heat flux (HHF) test, the pre and post non-destructive examination, and the surface results of the flat-type KW/Cu/ODS-Cu/RAFM mockup after the HHF test. The test results demonstrate that the mockup manufactured according to the fabrication route still have structural and interfacial integrity under cyclic high heat loads.

• Korean Journal of Mineralogy and Petrology
• /
• v.33 no.1
• /
• pp.53-64
• /
• 2020

The Samgwang deposit has been one of the largest deposits in Korea. The deposit consists of series of host rocks including Precambrian metasedimentary rocks and Jurassic Baegunsa formation, which unconformably overlies the Precambrian metasedimentary rocks. The deposit consists of eight lens-shaped quartz veins which filled fractures along fault zones in Precambrian metasedimentary rock, which feature suggest that it is an orogenic-type deposit. Laminated quartz veins are common in the deposit which contain minerals including quartz, ankerite, white mica, chlorite, apatite, rutile, arsenopyrite, sphalerite, chalcopyrite and galena. The structural formulars of white micas from laminated quartz vein and wallrock alteration are determined to be (K_1.02-0.82Na_0.02-0.00Ca_0.00)(Al_1.73-1.58Mg_0.26-0.16Fe_0.23-0.10Mn_0.00Ti_0.03-0.01Cr_0.01-0.00)(Si_3.35-3.22Al_0.79-0.65)O₁₀(OH)₂ and (K_0.75-0.67Na_0.01Ca_0.00) (Al_1.78-1.74Mg_0.16-0.15Fe_0.15-0.13Mn_0.00Ti_0.04-0.02Cr_0.01-0.00)(Si_3.33-3.26Al_0.74-0.67)O₁₀(OH)₂, respectively. It suggest that white mica from laminated quartz vein has higher interlayer cation (K+Na+Ca) and Fe+Mg+Mn+Ti content in octahedral site compared to the white mica from the wallrock alteration. Compositional variations in white mica from laminated quartz vein can be caused by phengitic or Tschermark substitution ((Al³⁺)^VI+(Al³⁺)^IV <-> (Fe²⁺ or Mg²⁺)^VI)+(Si⁴⁺)^IV) and (Fe³⁺)^VI <-> (Al³⁺)^VI substitution. Ankerite from laminated quartz vein has compositional variations of FeO and MgO contents along crystal growth direction. The geochemical and textural features suggest that laminated quartz vein from the Samgwang gold-silver deposit was formed during ductile shear stage, which is an important main gold-silver ore-forming event in orogeinc deposit.