• Clean Technology
• /
• v.19 no.4
• /
• pp.410-415
• /
• 2013

The supercapacitors were fabricated using silver (Ag) nano paste and activated carbon paste on the polyimide (PI) film and 5% potassium polyacrylate (PAAK) was used for gel electrolyte. In this paper, the current collector film and the electrode film were fabricated using screen printing. The thickness of printed silver paste was $7.3{\mu}m$ and the sheet resistance has the range of $5-7m{\Omega}/square$. An activated carbon with a surface area of $1,968m^2/g$, an electronic conducting agent (SUPER P, TIMCAL) and poly (4-vinylphenol) were mixed in 2-(2-buthoxyethoxy) ethyl acetate (BCA) with a ratio of 7:1:3 to fabricate the electrode paste. To analyze electrochemical characteristics, cyclic voltammetry was performed to evaluate the stability of the devices under the voltage range of -0.5-0.5 V. The calculated specific capacitances were 44.04 and 8.62 F/g for 10 and 500 mV/s scan rates, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.278-278
• /
• 2007

Ag conductive thick film has been used in bus and address electrodes of PDP (Plasma display panel). In PDP fabrication, the firing temperature of electrode is normally $550{\sim}580^{\circ}C$. For the application of PDP industry, we investigated an Ag conductive thick film with firing temperature. Low melting glass frit was used in the conductive thick film. The thermal properties of Ag and frit were determined by a hot stage microscopy. Based on the our results, we suggest that the Ag conductive thick film should be considered of the firing temperature which is correlated to the shrinkage, conductivity, and shape of thick film.

• Bulletin of the Korean Chemical Society
• /
• v.11 no.3
• /
• pp.200-205
• /
• 1990

Chemically modified electrodes(CMEs), based on 2-imino-1-cyclopentane-dithiocarboxylic acid (icdc) containing carbon paste, have been characterized using cyclic voltammetric techniques. Ag(I) was chemically deposited on the CMEs, and voltammograms were obtained with the electrode in a separate buffer solution. The CME surface can be regenerated with exposure to acid and reused for deposition. In 10 deposition/measurement/regenerate cycles, the linear response have been reproduced up to $1{\times}10^{-6}$ M in linear sweep voltammetry and 1${\times}$10-8 M in differential pulse voltammetry with relative standard deviation of 5.2% and 12.4%, respectiveiy. The sensitivity increased with deposition time and scanning rate, and detection limit was $1{\times}10^{-7}M\;and\;1{\times}10^{-9}M$ at 20 minutes deposition in the linear sweep voltammetry and differential pulse voltammetry, respectively. The presence of some metal ions does not influence the silver ion response. Satisfactory results were obtained for the analysis of the silver ion for a variety of reference materials without interference of Hg ion at the condition of pH = 5-6.