• Resources Recycling
• /
• v.26 no.6
• /
• pp.45-49
• /
• 2017

Most Waste slurry is produced in the process of silicon manufacturing for semiconductor industry, containing silicon (Si) and silicon carbide (SiC). Waste slurry is simply stored with solidifying by cement or buried. On the other hand, it was suggested in this study that the waste slurry should be used for heating source as supplementary material in steel making process. The waste slurry was refined and pulverized, which was recycled into SiC-based sludge briquette. Chemical composition for SiC-based sludge briquette was analyzed and the feature of heating source was observed in accordance with the injection time and input amount. As a result, SiC-based sludge briquette in terms of low cost and high efficiency had an effect on increasing liquid steel temperature in steel making plants.

• Journal of the Korean Ceramic Society
• /
• v.48 no.2
• /
• pp.189-194
• /
• 2011

Metallurgical grade silicon was recovered from slurry waste for ingot sawing process by acid leaching and thermal treatment. SiC abrasive was removed by gravity concentration and centrifugation. Metal impurities were removed by the acid leaching using HF/HCl. The remaining SiC was separated by the thermal treatment at $1600^{\circ}C$ in an inert atmosphere by the difference in melting points. The purity of the obtained silicon was found to be around 99.7%.

• Resources Recycling
• /
• v.19 no.5
• /
• pp.44-49
• /
• 2010

SiC powders have been recovered from silicon-containing waste slurry by carbothermal reduction method with carbon black. Large amount of silicon-containing waste slurry is generated from Solar Cell industry. In an environmental and economic point of view, retrieve of the valuable natural resource from the silicon waste is important. In this study, SiC powder recovered by the reaction ball-milled silicon powder from waste and carbon black at $1350^{\circ}C$ for 3h under vacuum condition. Physical properties of samples have been characterized using SEM, XRD, Particle size analyzer and FT-IR spectroscopy.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.4 no.3
• /
• pp.145-149
• /
• 2003

The enamel coated panels could be used to construct huge size tank in order to improve the fermentation effects of liquid wastes(food and night soil of cow and pig) and to minimize the construction fee. In order to joint the panels, water proofed volts, nuts and silicon adhesive were used. We applied these enamel coated panels to construct the slurry store tank.

• Korean Chemical Engineering Research
• /
• v.50 no.2
• /
• pp.310-316
• /
• 2012

The chromaticity of polyethylene glycol (PEG) generated from the recyling of a silicone slurry waste was improved by using activated carbon powder and a carbon filter. The color change of the PEG waste was investigated by changing the amount of adsorbent, adsorption time and temperature. The surface area of activated carbon did not have a significant impact on improving the color of the PEG waste. According to the results for the APHA color variation of the PEG waste changing the amount of the carbon adsorbent, the optimal usage to achieve the low APHA value was 100~150 mg-C/g-PEG. From the investigatnion on the effect of the adsorption temperature range from $25^{\circ}C$ to $100^{\circ}C$, it was found that the optimal temperatures were $40{\sim}50^{\circ}C$ in terms of achieving the lowest APHA value. The variation of the APHA color was investigated by changing the operation condition of the activated carbon filters. The use of ACF was a good way to enhance the chromaticity of the PEG waste. As a result, the APHA value of the PEG waste (APHA=53 at the initial waste) was reduced to be 10 through the ACF purification. It was also confirmed that the performance of the used carbon adsorbent can be recovered by the washing with purified water.

• Resources Recycling
• /
• v.12 no.3
• /
• pp.25-30
• /
• 2003

The synthesis of SiC used for the parts of the gas turbine and the heat exchanger, was carried out. In this study, wire cutting slurry of silicon wafer and the graphite rod of spent zinc-carbon battery were applied to the starting materials for the synthesis. The powders of Si or Si+SiC were obtained from the waste material by filtration, gravity separation and magnetic separation. Graphite powder was produced by dismantling, grinding and gravity separation from spent zinc-carbon battery. The synthesis of SiC could be completed from the mixture powders of Si and C or Si+SiC and C at the condition of equivalent ratio of Si and C, atmosphere of Ar or vacuum, temperature of above 1$600^{\circ}C$ and 2 hours reactions. The purity of synthesized Si-C was above 99%.