• Journal of the Korea Concrete Institute
• /
• v.27 no.3
• /
• pp.265-272
• /
• 2015

In this study, a method to reduce temperature rise due to hydration in mass concrete is investigated. It is to use retarder (glucose) for reducing heat of hydration and to use calcium silicate hydrate (C-S-H) for compensating the retardation effect due to its role as a nucleation seed. For this purpose, the temperature rise of cement paste due to hydration was measured and the effect of using both C-S-H and glucose on setting and 28-day compressive strength of mortar specimens was investigated. According to the experimental results, using C-S-H and glucose caused the reduction in the maximum temperature but accelerated the time to reach the maximum temperature compared to that of retarded cement paste using glucose. In addition, using C-S-H and glucose did not show significant effect on 28-day compressive strength of mortar specimens, indicating that the method shown in this study can be a successful alternative to control maximum temperature rise in mass concrete.

• Journal of the Korean Geosynthetics Society
• /
• v.16 no.2
• /
• pp.47-54
• /
• 2017

This study aims to develop a bio-grouting material in a powder form like cement. Sand gel samples were produced with the ratio of sodium silicate No.3 to water (50 : 50, 35 : 65, 20 : 80), and the ratio of cement to bio-grouting material (100 : 0, 90 : 10, 70 : 30) to select a mixing ratio of bio-grouting, respectively, and then analyzed the geltime over time. The uniaxial compressive strength was evaluated to select and suggest a mixing ratio optimized for construction conditions. The indoor test reveals that preferred geltime and uniaxial compressive strength is obtained in 35 : 65 with respect to the ratio of sodium silicate No.3 to water, and 90 : 10 with respect to the ratio of cement to bio-grouting material to demonstrate best optimal mixing ratios.

• Geomechanics and Engineering
• /
• v.16 no.4
• /
• pp.375-384
• /
• 2018

Unconfined compressive strength (UCS) of high plasticity clayey soil mixed with 5 and 10 % of Portland cement and four chemical agents such as sodium hexametaphosphate, aluminum sulfate, sodium carbonate, and sodium silicate with 0, 5, 10, and 20% concentrations was comparatively evaluated. The individual and combined effects of the cement and chemical agents on the UCS of the soil mixture were investigated. The strength of the soil-cement mixture generally increases with increasing the cement content. However, if the chemical agent is added to the mixture, the strength of the cement-chemical agent-soil mixture tends to vary depending on the type and the amount of the chemical agent. At low concentrations of 5% of aluminum sulfate and 5% and 10% of sodium carbonate, the average UCS of the cement-chemical agent-soil mixture slightly increased compared to pure clay due to increasing the flocculation of the clay in the mixture. However, at high concentrations (20%) of all chemical agents, the UCS significantly decreased compared to the pure clay and clay-cement mixtures. In the case of high cement content, the rate of UCS reduction is the highest among all cement-chemical agent-soil mixtures, which is more than three times higher in comparison to the soil-chemical agent mixtures without cement. Therefore, in the mixture with high cement (> 10%), the reduction of the USC is very sensitive when the chemical agent is added.

• Journal of the Korea Concrete Institute
• /
• v.16 no.1 s.79
• /
• pp.70-78
• /
• 2004

Although set accelerating agents are used generally in New Austrian Tunneling Method, the standards for test methods and quality of set accelerating agents are not prescribed domestically. In this study, the proprieties of the various standards and the characteristics of set accelerating agents for shotcrete were evaluated. The alkali contents of set accelerating agents based on silicate, aluminate and cement were higher than those of alkali-free ones. From the result, it is thought that the quality control of aggregate should be enhanced and that the number of test cycle of alkali-aggregate reaction should be increased. The setting times of cement paste with set accelerating agents based on silicate and alkali-free ones were different largely with mixing methods. Compressive strength of mortar with set accelerating agents based on silicate, aluminate and cement at one day satisfied the specifications of Korea Concrete Institute. However, the strength ratio compared to control mix at 28 days showed as $50{\~}65\%$ except for the alkali-free set accelerating agents. As a results of setting time and strength test, the establishment of domestic standards that can reflect the characteristics of materials and construction methods of tunnels and that can increase quality of set accelerating agents is required immediately.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.103-111
• /
• 2012

One of the basic physical properties of the hardened cement paste, the rigidity, is deteriorated during concrete matrix forming, depending on the replacement rate of the crushed stone powder, and due to drying shrinkage. Therefore, the concrete containing crushed stone powder has been limitedly used as non-structural construction material. To improve these disadvantages, a hydrothermal reaction employing method can be considered. High-temperature and high-pressure water is involved in the hydrothermal reaction in the mixing with specific materials. The rigidity improving mechanism is related to the synthesis of calcium silicate. The calcium silicate is produced through reaction between calcium compounds and the silicic acid. Various kinds of calcium silicate can be produced depending on the CaO/$SiO_2$ mole ratio, the temperature of the hydrothermal synthesis, the pressure, and the reaction time. The product of the synthesis mechanism, tobermorite crystal, plays a pivotal role for the rigidity reinforcement. The crushed stone powder, analyzed in this study, contains 50 to 60% of $SiO_2$ and 10 to 20% $Al_2O_3$. The composite rate is appropriate to create the tobermorite crystal through formation of hardened cement matrix under the hydrothermal synthetic conditions and with the CaO in the cement. Moreover, further reinforcement was promoted using the property of material under the identical density through promoting the formation of tobermorite crystal.

• The Journal of Korean Academy of Prosthodontics
• /
• v.8 no.1
• /
• pp.90-94
• /
• 1968

The author attempted to study the role of liners as a barrier against the penetration of the acids released from the liquid of dental cements. Six different kinds of liners were used in this study and the depth of penetration of the acids of phosphate and silicate cements were measured ands following conclusions were obtained. 1. All the liners successfully prevented penetration of the acids released from phosphate and silicate cements. 2. When silicate cements were placed into the cavity without any liners, free acids were liberated continuously and thus may give injuries to the pulp tissue.

• Computers and Concrete
• /
• v.16 no.1
• /
• pp.125-140
• /
• 2015

This paper describes the numerical calculation of elastic properties of a simulated microstructure of cement paste from very early age, when most previous models fail to give accurate results. The development of elastic properties of tricalcium silicate pastes was calculated by discretising a numerical resolution-free 3D vector microstructure to a regular cubic mesh. Due to the connections formed in the microstructure as an artefact of the meshing procedure, the simulated elastic moduli were found to be higher than expected. Furthermore, the percolation of the solids was found to occur even before hydration started. A procedure to remove these artefacts, on the basis of the information available in the vector microstructures was developed. After this correction, a better agreement of the experimental results with calculations was obtained between 20% and 40% hydration. However, percolation threshold was found to be delayed significantly. More realistic estimates of percolation threshold were obtained if either flocculation or a densification of calcium silicate hydrate with hydration was assumed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.625-628
• /
• 2006

It is known that cement production not only consumes large amount of energy but also contributes substantially to the green house gas emission. Therefore, there is a demand to develope a new technology to produce energy efficient and environmental conscious cements. The most recent, wood wool ceramic board is being applied in various building material field, for example thermal insulating and acoustic absorption material. This paper focused on improvement of alumino-silicate binder's physical properties for wood wool ceramic board. As the result of this experiment, what we could obtain best fitted alumino-silicate binder's properties such as initial setting time, flow and compressive strength of 3 days aged, was 58min, 110% and 66.0Mpa. This result can be applicable to commercial wood wool ceramic board.

• Journal of the Korean Ceramic Society
• /
• v.21 no.2
• /
• pp.143-148
• /
• 1984

In this study we mainly dealt with the effects of organic retarder(calcium lignosulfate) on the early hydration process of clinker minerals. From a consideration of the hydration process of tricalcium silicate $(C_3S)$ tricalcium silicate $(C_3S)$-tricalcium aluminate $(C_3A)$ tricalcium silicate $(C_3S)$-tetracalcium aluminof-errite $(C_4AF)$ systems with calcium lignosulfate the following results were obtained. 1. when 0.25wt% of CLS was added to $C_3S$ the hydration process was progressed normally but adding of 0.5wt% its hydration was greatly retarded. 2. The hydration of $C_3S$-$C_3A$ system was progressed normally up to 0.5wt% but by adding gypsum its hydration was retarded slightly. 3. The hydration of $C_3S$-$C_4AF$ system was greatly retarded even with 0.25wt% of CLS but by adding gypsum its hydration process was recovered normally.

• Journal of the Korea Institute of Building Construction
• /
• v.24 no.2
• /
• pp.181-191
• /
• 2024

In the realm of cement manufacturing, concerted efforts are underway to mitigate the emission of greenhouse gases. A significant portion, approximately 60%, of these emissions during the cement clinker sintering process is attributed to the decarbonation of limestone, which serves as a fundamental ingredient in cement production. Prompted by these environmental concerns, there is an active pursuit of alternative technologies and admixtures for cement that can substitute for limestone. Concurrently, initiatives are being explored to harness technology within the cement industry for the capture of carbon dioxide from industrial emissions, facilitating its conversion into carbonate minerals via chemical processes. Parallel to these technological advances, economic growth has precipitated a surge in construction activities, culminating in a steady escalation of construction waste, notably waste concrete. This study is anchored in the innovative production of calcium silicate cement clinkers, utilizing finely powdered waste concrete, followed by a thorough analysis of their mineral phases. Through X-ray diffraction(XRD) analysis, it was observed that increasing the substitution level of waste concrete powder and the molar ratio of SiO₂ to (CaO+SiO₂) leads to a decrease in Belite and γ-Belite, whereas minerals associated with carbonation, such as wollastonite and rankinite, exhibited an upsurge. Furthermore, the formation of gehlenite in cement clinkers, especially at higher substitution levels of waste concrete powder and the aforementioned molar ratio, is attributed to a synthetic reaction with Al₂O₃ present in the waste concrete powder. Analysis of free-CaO content revealed a decrement with increasing substitution rate of waste concrete powder and the molar ratio of SiO₂/(CaO+SiO₂). The outcomes of this study substantiate the viability of fabricating calcium silicate cement clinkers employing waste concrete powder.