• 한국진공학회지
• /
• 제4권S2호
• /
• pp.64-68
• /
• 1995

Silicon films were deposited at $430^{\circ}C$ by remote plasma chemical vapor deposition(RPECVD) with a gas mixture of $Si_2H_6/SiF_4/H_2$. The silicon films deposited without and with $SiF_4$ were characterized using atomic force microscopy(AFM), transmission electron microscopy(TEM) and X-ray diffraction(XRD). Both silicon films have the same rugged surface morphology, but, the silicon film deposited with $SiF_4$ exhibits more rugged. The silicon film deposited without $SiF_4$ is amorphous, whereas the silicon film deposited with $SiF_4$ is polycrystalline with very small needle-like grains which are perpendicular to the substrate and uniformly distributed in the thickness of the film. The silicon film deposited with $SiF_4$ was found to have a preferred orientation along the growth direction with the<110> of the film parallel to the <111> of the substrate. The effect of $SiF_4$ during RPECVD was discussed.

• 한국재료학회지
• /
• 제33권3호
• /
• pp.101-105
• /
• 2023

A mixture of elemental Co₅₀Si₅₀ powders was subjected to mechanical alloying (MA) at room temperature to prepare a CoSi thermoelectric compound. Consolidation of the Co₅₀Si₅₀ mechanically alloyed powders was performed in a spark plasma sintering (SPS) machine using graphite dies up to 800 ℃ and 1,000 ℃ under 50 MPa. We have revealed that a nanocrystalline CoSi thermoelectric compound can be produced from a mixture of elemental Co₅₀Si₅₀ powders by mechanical alloying after 20 hours. The average grain size estimated from a Hall plot of the CoSi intermetallic compound prepared after 40 hours of MA was 65 nm. The degree of shrinkage of the consolidated samples during SPS became significant at about 450 ℃. All of the compact bodies had a high relative density of more than 94 % with a metallic glare on the surface. X-ray diffraction data showed that the SPS compact produced by sintering mechanically alloyed powders for 40-hours up to 800 ℃ consisted of only nanocrystalline CoSi with a grain size of 110 nm.

• 마이크로전자및패키징학회지
• /
• 제5권1호
• /
• pp.101-110
• /
• 1998

큰 누설전류를 개선하고 누설전류 기구를 해석하기 위해 Pt/Ti/ SiO2/Si 기판상에서 2단계 sputtering 하여 PZT박막을 형성시켰다. 상온층과 perovskite의 두층으로 이루어진 PZT박막은 누설전류가 개선되었다. 특히 20nm의 상온층을 포함하는 PZT 박막은 유전상수 와 누설전류 특성이 모두 탁월한 것으로 나타났다. 이와 같은 조건에서 PZT 박막의 누설전 류 기구는 bulk 지배하는 기구로 바뀌었다.

• 한국표면공학회지
• /
• 제31권6호
• /
• pp.345-358
• /
• 1998

The evolution of surface roughness and morphology in epitaxial Si and $Si_{0.7}Ge{0.3}$ alloys grown by UHV opm-beam sputter deposition onto nominally-singular, [100]-, and [110]-mi-scut Si(001) was investigated by stomic force microscopy and trasmission electron microscopy. The evolution of surface roughness of epitaxial Si films grown at $300^{\circ}C$ is inconsistent with conventional scaling and hyperscaling laws for kineti roughening. Unstable growth leading to the formation of mounds separated by a well-defined length scale is observed on all substrates. Contraty to previous high-temperature growth results, the presence of steps during deposition at $300^{\circ}C$ increases the tendency toward unstable growth resulting in a much earlier development of mound structures and larger surface roughnesses on vicival substrates. Strain-induced surface roughening was found to dominate in $Si_{0.7}Ge{0.3}$ alloys grown on singular Si(001) substrates at $T_S\ge450^{\circ}C$ where the coherent islands are prererentially bounded along <100> directions and eshibt {105} facetting. Increasing the film thickness above critical values for strain relaxation leads to island coalescence and surface smoothening. At very low growth temperatures ($T_s\le 250^{\circ}C$), film surfaces roughen kinetically, due to limited adatom diffusiviry, but at far lower rates than in the higher-temperature strain-induced regime. There is an intermediate growth temperature range, however, over which alloy film surfaces remain extremely smooth even at thicknesses near critical values for strain relaxation.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1996년도 하계학술대회 논문집 C
• /
• pp.1943-1945
• /
• 1996

In this paper, we developed a modified direct bonding method for the application of vacuum devices. By the proposed method, we successfully bonded the following materials: Si-Si, Si-$SiO_2$-Si, glass-Si, and glass-$SiO_2$-Si. In our experiments, we used corning #7070 wafer type glass and (100) or (110) single crystalline silicon wafers. In order to enhance the initial bonding strength we contacted the materials to be bonded as D. I. water wetted on the surfaces and evaporated the water under the room temperature and atmosphere environment. Finally we realized the glass bonding by simple direct bonding method which has been performed by electrostatic bonding method until now.

• 한국세라믹학회지
• /
• 제29권10호
• /
• pp.822-826
• /
• 1992

SiO2 doped sapphire single crystals were grown by Verneuil method using feed material which prepared by adding SiO2 in Al2O3. Crystal growing were attempted with varing doping amount of SiO2 from 0.01 to 1.0 wt% and when the doping amount of SiO2 were 0.01~0.04 wt%, single crystals could be attained. Starting materials for feed powder were 99.99% purity alumina and extra pure SiO2 powder. Mixing these two materials by wet milling for 24 hours and drying the mixture and then was calcined at 900~110$0^{\circ}C$ for 2~4 hours. The grown crystals had yellowish color and were somewhat transparent. During growing process the flow range of oxygen was 5~7.5ι/min and of hydrogen was 13~25ι/min, the average growth rate was 7.0~11 mm/hr. The pressure of gases were fixed at 5psi. The color of crystal was appeared and mechanical property of sapphire was developed by doping of SiO2.

• 한국전기전자재료학회논문지
• /
• 제13권10호
• /
• pp.828-833
• /
• 2000

Growth characteristics and microstructure of AIN thin films grown by plasma assisted molecular beam epitaxy on Si substrates have been investigated. Growing temperature and substrate orientation were chosen as major variables of the experiment. Reflection high energy electron diffraction (RHEED), X-ray diffraction (XRD), atomic force microscopy (AFM) and transmission electron microscopy/diffraction (TEM/TED) techniques were employed to characterize the micorstructure of the films. On Si(100) substrates, AlN thin films were grown along the hexagonal c-axis preferred orientation at temperature range 850-90$0^{\circ}C$. However on Si(111), the AlN films were epitaxially grown with directional coherency in AlN(0001)/Si(111), AlN(1100)/Si(110), and AlN(1120)/Si(112) at 85$0^{\circ}C$ and the epitaxial coherencry seemed to be slightly distorted with increasing temperature. The microstructure of AlN thin films on Si(111) substrates showed that the films include a lot of crystal defects and there exist micro-gaps among the columns.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.111-114
• /
• 2000

Growth characteristics and microstructure of AlN thin films grown by plasma assisted molecular beam epitaxy on Si substrates have been investigated. Growing temperature and substrate orientation were chosen as major variables of the experiment. Reflection high energy electron diffraction (RHEED), X-ray diffraction (XRD), atomic force microscopy (AFM) and transmission electron microscopy/diffraction (TEM/TED) techniques were employed to characterize the microstructure of the films. On Si(100) substrates, AlN thin films were grown along the hexagonal c-axis preferred orientation at temperature range 850-90$0^{\circ}C$. However on Si(111), the AlN films were epitaxially grown with directional coherency in AlN(0001)/Si(111), AlN(1100)/Si(110), and AlN(1120)/Si(112) at 85$0^{\circ}C$ and the epitaxial coherencry seemed to be slightly distorted with increasing temperature. The microstructure of AlN thin films on Si(111) substrates showed that the films include a lot of crystal defects and there exist micro-gaps among the columns.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.187-187
• /
• 2007

This paper presents the electrical properties of SiGe HBTs designed with bottom collector and single metal layer structure for RF power amplifier. Base layer was formed with graded-SiGe/Si structures and the collector place to the bottom of the device. Bottom collector and single metal layer structures could significantly simplify the fabrication process. We studied about the influence of SiGe base thickness, number of emitter fingers and temperature dependence (< $200^{\circ}C$) on electrical properties. The feasible application in 1~2GHz frequency from measured data $BV_{CEO}$ ~10V, $f_r$~14 GHz, ${\beta\simeq}110$, NF~1 dB using packaged SiGe HBTs. We will discuss the temperature dependent current flow through the e-b, b-c junctions to understand stability and performance of the device.

• 한국재료학회지
• /
• 제3권2호
• /
• pp.158-165
• /
• 1993

실리콘박막의 상부에 고상반응에 의해 형성된 TiS$i_2$ 박막의 응집 거동에 미치는 기판 실리콘의 영향을 조사했다. 폴리실리콘과 어몰퍼스실리콘을 증착상태 또는 어닐링한 상태엣 TiS$i_2$를 형성시키고 90$0^{\circ}C$열처리에 따른 TiS$i_2$의 면저항값의 변화를 조사하고 XRD, SEM 및 TEM에 의한 실리콘의 조직관찰을 행했다. TiS$i_2$응집은 어몰퍼스실리콘 위의 경우가 더욱 심했다. 폴리실리콘을 어닐링하면 TiS$i_2$의 응집은 억제되며 고온에서 어닐링할수록 그 효과가 현저했다. 이는 폴리실리콘의 입도 변화보다는 증착시 존재하는 결함들이 열처리에 의해 감소된 때문이다. 폴리실리콘의 경우는 어닐링 전후에 상관없이 (110)집합조직인 주상정 조직을 갖고 있다. 어몰퍼스실리콘을 결정화시킨 경우는 (111)집합조직를 갖는 등축정 조직을 나타내었다. 실리콘의 표면에너지가 낮은 (111)면이TiS$i_2$ 막의 하부 폴리실리콘에 많이 존재할수록 응집은 촉진된다.