• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.563-566
• /
• 2000

The study is to examine the drying shrinkage reducing method of mortar using organic shrinkage reducing agent. According to the experiment result, when 2% and 4% of organic shrinkage reducing agent were added, 40% and 50% of the shrinkage rate of mortar were obtained. Also, in the cracking test of plate-shape specimen, the usage of shrinkage agent 2% reduced about 60% of the total cracking length compare to total cracking length the usage of portland cement, the usage of shrinkage agent 4% was not happened crack until 90 days. Accordingly, the usage of shrinkage agent show good effect in prevention of crack.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.5
• /
• pp.34-40
• /
• 2014

High-performance fiber-reinforced cement composite (HPFRCC) shows very high autogenous shrinkage, because it contains a low water-to-binder ratio (W/B) of 0.2 and high fineness admixture without coarse aggregate. Thus, it needs a method to decrease the cracking potential. Accordingly, in this study, to effectively reduce the shrinkage of HPFRCC, a total of five different ratios of SRA (1% and 2%), EA (5% and 7.5%), and a combination of SRA and EA (1% and 7.5%) were considered. According to the test results of ring-test, a combination of SRA and EA (1% and 7.5%) showed best performance regarding restrained shrinkage behavior without significant deterioration of compressive and tensile strengths. This was also verified by performing modified drying shrinkage crack test.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.10 no.3
• /
• pp.97-105
• /
• 2006

The autogenous shrinkage of high-performance concrete is important in that it can lead the early cracks in concrete structures. The purpose of the present study is to explore the autogenous shrinkage of high-performance concrete with admixture and to derive a realistic equation to estimate the autogenous shrinkage model of that. For this purpose, comprehensive experimental program has been set up to observe the autogenous shrinkage for various test series. Major test variables were the type and contents of admixture and water-cement ratio is fixed with 30%. The autogenous shrinkage of HPC with fly ash slightly decreased than that of OPC concrete, but the use of blast furnace slag increased the autogenous shrinkage. Also, the autogenous shrinkage of HPC is found to decrease with increasing shrinkage reduction agent and expansive additive. A prediction equation to estimate the autogenous shrinkage of HPC with admixture was derived and proposed in this study. The proposed equation show reasonably good correlation with test data on autogenous shrinkage of HPC with mineral and chemical admixture.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.11a
• /
• pp.293-296
• /
• 2004

In this study, to investigate autogenous shrinkage behavior of 120MPa UHSC at early ages, free and restrained shrinkage tests are performed for various strength levels(50MPa, 80MPa, 120MPa). For 120MPa, the effect of fly ash on autogenous shrinkage was also investigated. In order to assess the potential for early-age cracking in concrete and a mixtures susceptibility to shrinkage cracking, restrained ring test was carried out. Test results show that autogenous shrinkage of UHSC was much higher than that of HSC, VHSC and fly ash delayed cracking age in UHSC by decreasing autogenous shrinkage.

• Journal of the Korea Institute of Building Construction
• /
• v.4 no.4
• /
• pp.71-77
• /
• 2004

Drying Shrinkage has much complexity as it has relations with both internal elements of concrete and external factors. Therefore, experiments on Concrete Drying Shrinkage are carried out in this study under simplified circumstances applying temperature & Humidity test chamber which enables constant temperature and humidity. Comparative analyses have been made respectively according to the consequences aiming at modelling for prediction of Concrete Drying Shrinkage and making out measures to reduce it. Strain Rate of Drying Shrinkage of concrete under the condition of dry air appears to rise by about 20%-30% in proportion as the temperature rises $5^{\circ}C$ when the humidity was held below 10% compared under the condition of dry temperature & Humidity test chamber. Strain Rate of Drying Shrinkage in pit sand concrete increased 20% higher than measured when in river sand under the condition of 90-day material age. A general formula with two variables is derived as follow ${\varepsilon}={\alpha}_1＋{\beta}_1x_1＋{\beta}_2x_2＋{\beta}_3x_1^2＋{\beta}_5x_2^2$. and also graphed in 3 dimensions, enabling to apply to actual design and predict Strain Rate of Drying Shrinkage in concrete. The results of prediction of Rate of Drying Shrinkage by Response Surface Analysis are as follows. The coefficient of correlation of Drying Shrinkage in Concrete was over 90%.

• Journal of the Korean Geotechnical Society
• /
• v.15 no.6
• /
• pp.219-238
• /
• 1999

In the present study, laboratory tests including the seepage-induced consolidation test, suction test, and desiccation shrinkage test are performed to investigate characteristics of the desiccation shrinkage in reclaimed hydraulic fills. Soil samples for laboratory tests are obtained from three sites (districts of Haenam, Kogeum and Koheung in Chunnam area). Desiccation shrinkage settlement caused by three dimensional volume change is numerically evaluated using finite difference technique based on the governing equation proposed by Abu-Hejleh & Znidarcic. Also characteristics of the desiccation shrinkage analyzed from the test results are used as input data for numerical evaluations. Further predicted total settlements including the self-weight consolidation settlement are compared with values measured at the site of Haenam district. Finally, effects of parameters related to the desiccation shrinkage on settlements are examined.

• Advances in concrete construction
• /
• v.14 no.2
• /
• pp.139-151
• /
• 2022

Filling materials poured into precast member joint are subjected to restraint stress by the precast member and joint reinforcement. The induced stress will likely cause cracks at early ages and performance degradation of the entire structure. To prevent these issues and design reasonable joints, it is very important to analyze and evaluate the restrained shrinkage cracks of filling materials at various restraint conditions. In this study, a new time zero-that defines the shrinkage development time of a filling material-is proposed to calculate the accurate amount of shrinkage. The tensile stresses and strengths at different ages were compared through the ring test (AASHTO PP34) to evaluate the crack potential of the restrained filling materials at various restraint conditions. The mixture which contained an expansive additive and a shrinkage reducing agent exhibited high resistance to shrinkage cracking owing to the high-drying shrinkage compensation effect. The high-performance, fiber-reinforced cement composite, and ultra-high-performance, fiber-reinforced cement composite yielded very high resistance to shrinkage and cracking owing to the pull-out property of steel fibers. To this end, multiple nonlinear regression analyses were conducted based on the test results. Accordingly, a modified tensile stress equation that considered both the geometric shape of the specimen and the intrinsic properties of the material is proposed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.393-396
• /
• 2005

This paper presents the results of drying shrinkage of concrete using shrinkage-reducingadmixture(DSRA) studied by the authors through mock-up test. DSRA is proportioned by expansive admixture and shrinkage reducing agent(SRA). Flowing concrete method is also applied to assist the concrete to reduce drying shrinkage by decreasing water content at the same time. The use of EA and SRA does not affect fluidity, bleeding and setting time. Compressive strength of concrete using EA along with SRA exhibited less than that of plain concrete. However, The compressive strength with combination of EA-SRA along with flowing concrete method shows comparable to that of plain concrete. The application of developed method can contribute to reducing drying shrinkage by as much as 30-40$\%$ compared with that of plain concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.04a
• /
• pp.231-236
• /
• 1998

In general, the drying shrinkage of polymer-modified mortars using redispersible polymer powders is much higher than that of unmodified mortar. The purpose of this study is to reduce the drying shringkage of polymer-modified mortars using a redispersible poly(ethylene-vinyl acetate) (EVA) powder, which is widely used for the manufacture of prepackaged-type polymer-modified mortar products at present. Polymer-modified mortars using the redispersible EVA powder with powdered shrinkage-reducing agent were prepared with various polymer-cement ratios and shrinkage-reducing agent contents, and tested for drying shrinkage and strength. From the test results, the drying shrinkage of the redispersible EVA powder-modified mortars with a powdered shrinkage agent is remarkably reduced with increasing shrinkage-reducing agent content, and becomes approximately a half of that of the redispersible EVA powder-modified mortars with the same polymer-cement ratios and without the shrinkage-reducing agent at a shrinkage-reducing agent content of 6%.

• Restorative Dentistry and Endodontics
• /
• v.29 no.4
• /
• pp.346-352
• /
• 2004

The purpose of present study was to evaluate the polymerization shrinkage stress and cuspal deflection in maxillary premolars resulting from polymerization shrinkage of composites and compomers. Composites and compomers which were used in this study were as follows: Dyract AP, Z100, Surefil. Pyramid, Synergy Compact, Heliomolar, Heliomolar HB, and Compoglass F. For measuring of polymerization shrinkage stress, Stress measuring machine (R&B, Daejon, Korea) was used. One-way ANOVA analysis with Duncan's multiple comparison test were used to determine significant differences between the materials. For measuring of cuspal deflection of tooth, MOD cavities were prepared in 10 extracted maxillary premolars. And reduction of intercuspal distance was measured by strain measuring machine (R&B, Daejon, Korea) One-way ANOVA analysis with Turkey test were used to determine significant differences between the materials. Polymerization shrinkage stress is $\mathbb{\ulcorner}$Heliomolar, Z100, Pyramid < Synergy Compact Compoglass F < Dyract AP < Heliomolr HB, surefil$\mathbb{\lrcorner}$ (P < 0.05). And cuspal delfelction is $\mathbb{\ulcorner}$Z100, Heliomolar, Heliomolar HB, Synergy Compact Surefil. < Compoglass F < Pyramid, Dyract AP$\mathbb{\lrcorner}$ (P < 0.05). Measurements of ploymerization shrinkage stress and those of cuspal deflection of the teeth was different. There is no correlation between polymerization shrinkage stress and cuspal deflection of the teeth(p > 0.05).