• Journal of the Korean Society of Industry Convergence
• /
• v.26 no.4_2
• /
• pp.571-576
• /
• 2023

In this study, the harmless crack size(a_hml) according to the residual stress depth was evaluated using the fatigue limit of SCM440 steel by quenching-tempering(QT) and induction hardening(IH), and threshold stress intensity factor of QT steel. Because the residual stress increased rapidly as the crack depth increased, a_hml was determined at the depth of all the crack aspect ratio(As) regardless of Type I-III, and a_hml also increased according to the residual stress depth. a_hml was minimal at As=1.0 and maximal at As=0.1, but was almost similar on each Type. a_hml was small the dependence on As.

• Journal of the Korean Society of Industry Convergence
• /
• v.9 no.1
• /
• pp.51-59
• /
• 2006

The study is diagnosis about fatigue failure phenomenon of heating coil spring (sup9) and heat treatment method that is used to crusher. Because more than 80~90% of damage announcement of breakdown of machine and construction is been caused in fatigue present state, fatigue failure became important leading person at design. Calculated design load is imposed repeatedly that fatigue breakdown is safe. Is phenomenon that change load is imposed in the construction continuously. Used coil spring applies heat 30minute by Quenching temperature $860^{\circ}C$ if see manufacturing process and temperature of gasoline of $50^{\circ}C$ keep after quench that know tempering a $460^{\circ}C$ 90minute a product be. If doto apply heat $950^{\circ}C$ material at rolling process historically before quenching, austenite formation clay pipe being done AGS(Austenite Grain Size) by 2.5~4 become. Apply heat quenching 30minute by $820^{\circ}C$ by improvement method and after quench that keep $50^{\circ}C$ in oil tempering if do $450^{\circ}C$, 90minute spring ideal formation sorbite formation of the river form and condition that satisfy most more than AGS 7 appeared. Also, we can secure authoritativeness through MT since shot peening processing.

• Journal of Ocean Engineering and Technology
• /
• v.25 no.6
• /
• pp.42-48
• /
• 2011

The present study makes three original contributions to nanoskinned Ti-6Al-4V materials. The nanoskins were fabricated on Ti-6Al-4V material using various surface treatments: deep rolling (DR), laser shot peening (LSP), and ultrasonic nanocrystal surface modification (UNSM). These surface treatments are newly developed techniques and are becoming more popular in industrial fields. A fatigue strength comparison at up to 106 cycles was conducted on these nanoskinned Ti-6Al-4V materials. Fatigue tests were carried out using MTS under axial loading tension-compression fatigue (R = -1, RT, 5 Hz, sinusoidal wave). The analysis of the crack initiation patterns in the nanoskinned Ti-6Al-4V materials found an interior originating crack pattern and surface originating crack type. Microscopic observation was mainly used to investigate the fatigue fractured sites. These surface modification techniques have been widely adopted, primarily because of the robust grade of their mechanical properties. These are mainly the result of the formation of a large-scale, deep, and useful compressive residual stress, the formation of nanocrystals by the severe plastic deformation (SPD) at the subsurface layer, and the increase in surface hardness.

• Tribology and Lubricants
• /
• v.33 no.5
• /
• pp.214-219
• /
• 2017

Abrasive fluidized bed machining (AFBM) is similar to general abrasive fluidized machining (AFM) in that it can perform polishing of the outer and inner surfaces of a 3-dimensional shape by the flow of particles. However, in the case of AFM, the shear force generated by the flow of the particles causes material removal, while in AFBM, the abrasive particles are suspended in the chamber to form a bed. AFBM can be used for deburring, polishing, edge contouring, shot peening, and cleaning of mechanical parts. Most studies on AFBM are limited to metals, and research on application of AFBM to plastic materials has not been performed yet. Therefore, in this study, we investigate the effect of rotating speed of the specimen and the air flow rate on the material removal characteristics during AFBM of polyacetal with a horizontal AFBM machine. The material removal rate (MRR) increases linearly with increase of the rotating speed of the main shaft because of the shear force between the particles of the fluidized bed and the rotation of the workpiece. The reduction in surface roughness tends to increase as the rotating speed of the main shaft increases. As the air flow rate increases, the MRR tends to decrease. At a flow rate of 70 L/min or more, the MRR remains almost constant. The reduction of the surface roughness of the specimen is found to decrease with increasing air flow rate.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.4
• /
• pp.443-449
• /
• 2012

Nanoskins were fabricated on a Ti-6Al-4V material by carrying out various surface treatments, i.e., deep rolling, laser shot peening, and ultrasonic nanocrystal surface modification (UNSM). These surface treatments are newly developed techniques and are becoming more popular for industrial applications. Fatigue tests were carried out using material test system (MTS); these tests included the axial loading tension-compression fatigue test (R = -1, RT, 5 Hz, sinusoidal wave) and rotating bending fatigue test (R = -1, RT, 3200 rpm). The analysis of the crack initiation pattern in the UNSM-treated material indicated that the crack was interior originating in the axial loading tension-compression cycle, and was surface originating in the bending fatigue test. UNSM treatment significantly improved the fatigue strength for the regime of above $10^6$ cycles that S-N curve of rotating bending stress clearly show the performance of a 5 mm titanium specimen after UNSM treatment is similar to that of an untreated 6 mm titanium specimen.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.5
• /
• pp.47-53
• /
• 2020

The purpose of this study was to increase product reliability by improving the durability of the breech block for a 30mm Automatic Gun. The breech block is a key component of a gun that functions as chambering, closing, and extracting. The breech block requires high reliability, which needs to be improved because cracks of a breech block can occur early in operation. Cause analysis confirmed that the crack is caused by repeated impacts. Therefore, the following improvement measures were studied, and the effects were demonstrated using a firing test. The energy of impact absorption was increased by changing the material, and the stress concentration was mitigated by increasing the value of R. In addition, the fatigue life was increased by adding Shot-peening, deleting chromium plating, and changing the forging method. The firing test did not show firing trouble for up to 5,000 rounds. The start timing of the crack was delayed, and the depth was small. Therefore, the improved product was more durable than the existing product. This study can be used as a useful reference when assessing the improvement of the durability of similar products, life study, and criteria for crack acceptance.