• 한국분말재료학회지
• /
• 제19권2호
• /
• pp.122-126
• /
• 2012

The Fe-based self-fluxing alloy powders and TiC particles were ball-milled and subsequently compacted and sintered at various temperatures, resulting in the TiC particle-reinforced Fe self-fluxing alloy hybrid composite, and the microstructure and micro-hardness were investigated. The initial Fe-based self-fluxing alloy powders and TiC particles showed the spherical shape with a mean size of approximately 80 ${\mu}m$ and the irregular shape of less than 5 ${\mu}m$, respectively. After ball-milling at 800 rpm for 5 h, the powder mixture of Fe-based self-fluxing alloy powders and TiC particles formed into the agglomerated powders with the size of approximately 10 ${\mu}m$ that was composed of the nanosized TiC particles and nano-sized alloy particles. The TiC particle-reinforced Fe-based self-fluxing alloy hybrid composite sintered at 1173 K revealed a much denser microstructure and higher micro-hardness than that sintered at 1073 K and 1273 K.

• 해양환경안전학회지
• /
• 제19권5호
• /
• pp.538-544
• /
• 2013

본 연구에서는 ALBC3 합금에 Ni기 자용성 합금으로 내마모성 및 내캐비테이션 특성을 향상시키기 위하여 용사코팅 후 열처리를 실시하여 캐비테이션 특성을 평가하였다. 본 연구 결과, 자용성 합금 코팅층이 높은 경도를 나타내어 내마모성이 우수할 것으로 판단되나, 다공질의 조직으로 인해 열악한 내캐비테이션 특성을 나타냈다. 따라서 열처리 조건의 최적화가 중요하며, 본 조건에서는 열처리 온도를 높여 자용성 합금 내 B와 Si의 유동성을 증가시킴으로써 기공이나 결함을 제거하여 특성개선 효과를 기대할 수 있을 것으로 판단된다.

• 동력기계공학회지
• /
• 제1권1호
• /
• pp.70-79
• /
• 1997

Ni-base self-fluxing alloy powder particles were flame sprayed onto the SS400 mild steel substrate surface. The effects of both substrate temperature and spraying distance on the splat behavior of sprayed particles were examined. The results obtained are summarized as follows: 1) In the splat behavior of Ni-base self-fulxing alloy particles sprayed onto the SS400 mild steel substrate, splashing was observed under the room temperature condition. On the contrary, it showed circular plate pattern in the substrate temperature range over 373K. 2) It was cleared that there was close relationship between mechanical properties of coating layer and splat behavior of sprayed particles. 3) From the experimental results, optimum spraying conditions showed excellent mechanical properties in the case of Ni-base self fluxing alloy sprayed onto the SS400 mild substrate were 473K of substrate temperature and 250mm of spraying distance.

• 동력기계공학회지
• /
• 제2권2호
• /
• pp.35-40
• /
• 1998

In this study, the author investigated the effects of strengthening treatments on the mechanical properties of plasma sprayed Ni-base self fluxing alloy. Strengthening treatments for sprayed specimens were carried out in 4 different temperature conditions in vacuum furnace. The mechanical properties, such as microhardness, thermal shock resistance and erosion resistance were tested for the sprayed specimens after strengthening treatments. And it was proved that the mechanical properties of coating layer were much improved by strengthening treatments.

• Journal of Advanced Marine Engineering and Technology
• /
• 제36권2호
• /
• pp.276-285
• /
• 2012

본 연구목적은 열간압연용 런-아웃 테이블 롤러 표면의 기계적 성질을 개선하기 위해 다공질 자용성 합금으로 피복하는 방법을 개발하는 것이다. 열간압연에서 런-아웃 테이블의 롤러 내구성을 높이기 위해서는 고온에서 롤러표면의 경도를 높게 유지해야 하고, 내마모성, 내식성, 내열성, 내소부성 및 내응착성의 향상을 유지하여야 한다. 또한, 고온의 열연 강판을 안정적으로 이송할 수 있도록 하기 위해서는 롤러표면에 적절한 마찰계수를 유지하도록 하여야 하고, 롤러와 강판 사이에 미끄럼 발생이 없어야 한다. 본 연구에서는 자용성 합금에 텅스텐카바이드를 첨가시켜 서메트화하여 롤러의 내마모성을 증대시켰고, 미세 철분말을 롤러표면에 피복하여 다공질을 만들어 마찰계수를 높이고 붙잡음성을 향상시켰다. 그 결과, Ni-Cr 피복 롤러에 비하여 다공질 자용성 합금 피복 롤러는 피복층에 철분이 5 ~ 10 wt%로 많이 함유되어 재용융 공정에서 전기로로 가열하여 일부분만 합금화되고 나머지는 산화 및 용해에 의해 탈락되어 다공질로 나타나 강판과의 붙잡음성을 향상시켰다.

• 한국표면공학회지
• /
• 제22권1호
• /
• pp.26-42
• /
• 1989

It has between investigated that the optimum spaying conditions, such as, spraying distance, fusing temperature and fusing time, ect, in a Ni-cr base self fluxing alloy sprayed on the mild steel substrate by oxygen-acetylenc flame spraying. Sprayed specimens on various conditions were fuused in a vacuum furnace and the results were as follows. The optimum spraying condition for excellent coating layer are obtained under spraying distances, fusing temperature and fusing and time ; 180~240mm,1050~110$0^{\circ}C$and 15~30min, respectively. The adhesive strength and surface hurface hardness of the as sprayed specimens were very low by mechanical bonding becaus of the diffusion layer during process. The carbides and borides and formed in the sprayed coating layer and densification of the layer was resulted from the elimination of pores and oxides. The hardness of sprayed coating layer, particularly in the high temperature, was superior to ordinary tool steels.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.199-199
• /
• 2013

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2011년도 전기공동학술대회 논문집
• /
• pp.226-226
• /
• 2011

• 대한기계학회논문집A
• /
• 제38권6호
• /
• pp.629-636
• /
• 2014

비정질합금이 가지고 있는 우수한 기계적 성질과 화학적 특성을 부품소재에 표면개질을 목적으로 고속화염 용사법으로 대면적 코팅층을 형성하였고 내열성이 높은 자융성합금과 초경합금 성분들을 적절히 혼합하여 비정질기지 복합재료를 제조하여 코팅들의 미세조직 관찰과 나노인덴테이션을 이용한 미세표면의 기계적 거동을 분석하였다. 각 코팅층의 미세조직을 관찰한 결과, 단일상 비정질 코팅에는 미용융 입자와 lamellae 영역이 존재하고 자융성합금이 고용된 복합재에는 in-situ $Cr_2Ni_3$ 석출물, 자융성합금과 초경합금성분이 함께 혼합된 코팅층은 석출물과 ex-situ WC 강화입자가 공존하였다. 이들 미세표면의 기계적 거동은 제 2 상이 고용된 비정질 기지 복합재의 코팅층의 기계적 특성이 전체적으로 향상되었다.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2009년 추계학술발표대회
• /
• pp.73-73
• /
• 2009

In this sutdy, a new class ACA(Anisotropic Conductive Adhesive) with low-melting-point alloy(LMPA) and self-organized interconnection method were developed. This developed self-organized interconnection method are achieved by the flow, melting, coalescence and wetting characteristics of the LMPA fillers in ACA. In order to observe self-interconnection characteristic, the QFP($14{\times}14{\times}2.7mm$ size and 1mm lead pitch) was used. Thermal characteristic of the ACA and temperature-dependant viscosity characteristics of the polymer were observed by differential scanning calorimetry(DSC) and torsional parallel rheometer, respectively. A electrical and mechanical characteristics of QFP bonding were measured using multimeter and pull tester, respectively. Wetting and coalescence characteristics of LMPA filler particles and morphology of conduction path were observed by microfocus X-ray inspection systems and cross-sectional optical microscope. As a result, the developed self-organized interconnection method has a good electrical characteristic($2.41m{\Omega}$) and bonding strength(17.19N) by metallurgical interconnection of molten solder particles in ACA.