• 열처리공학회지
• /
• 제35권2호
• /
• pp.74-81
• /
• 2022

This study aims to mitigate the microstructural heterogeneity arising from the manufacture of magnesium alloy plates using the twin roll casting (TRC) process. Homogenization was introduced through hot rolling and heat treatment, followed by confirmation of observed changes in the microstructure. Following the TRC process, the hot rolled 2mm plate exhibited a dendritic cast structure tilted in the roll rotation direction, while central segregation were developed. This nonuniform structure and central segregation disappeared upon heat treatment, followed by recrystallization to form uniform and fine grains. Abnormal grain growth (AGG) was observed over the course of heat treatment; grains exhibiting AGG occupied up to 75% of the total area after having held the sample at 400℃ for 64 h. The formation of coarse grains was also observed during heat treatment at 340℃ over a relatively long duration, though the maximum grain size was significantly smaller than that corresponding to the heat treatment at 400℃. AGG in the 400℃ heat treatment occurred because of movement of the grain boundary, which had been fixed prior as a result of the grain boundary fixing effect of the precipitation phase. The re-dissolution of the Ca₂Mg₅Zn₅ precipitated phase over the long duration of the high-temperature annealing process caused the surrounding grains to disappear and regrow.

• 한국지반공학회논문집
• /
• 제26권12호
• /
• pp.19-30
• /
• 2010

벤토나이트는 팽윤성이 좋고 투수계수가 낮아 수직 밀폐형 지중 열교환기 시공 시 보어홀(borehole)의 뒤채움재로 널리 사용되고 있다. 본 연구에서는 국내에서 사용되는 3가지 벤토나이트를 선정하여 배합비에 따른 점도와 열전도도를 평가하였다. 시공 조건에 따라 다양한 벤토나이트 뒤채움재의 함수비를 고려하여 점도와 열전도도 특성을 규명하기 위해 벤토나이트를 배합비(벤토나이트 무게/(벤토나이트+물) 무게) 5%, 10%, 15%, 20%, 25%로 배합하고 시간에 따른 점도와 열전도도를 측정하였다. 그리고 벤토나이트 뒤채움재가 해안지역에서 시공될 경우 지하수의 염도에 의한 영향을 검토하기 위해 배합수의 NaCl 농도가 0.1M, 0.25M, 0.5M일 때 벤토나이트 뒤채움재의 침강 특성을 관찰하였다. 벤토나이트 뒤채움재의 낮은 점도로 인해 천연규사와 같은 첨가재가 지중 열교환기 바닥에 침전될 경우 발생할 수 있는 재료분리 현상을 저점도 벤토나이트 뒤채움재를 사용하여 실험을 통해 규명하였으며 그 결과 다음과 같은 결론을 얻을 수 있었다. (1) 벤토나이트 뒤채움재의 점도는 시간이 지남에 따라 또는 배합비가 증가함에 따라 상승하는 경향을 나타내며 벤토나이트 뒤채움재의 열전도도는 배합비가 증가하면 상승하지만 통일한 배합비에서는 시간에 따른 변화가 미미하다. (2) 벤토나이트 뒤채움재의 팽창지수가 높을수록 배합수의 NaCl 농도에 따른 침강율은 상대적으로 낮게 나타난다. (3) 저점도 벤토나이트 뒤채움재는 첨가재의 재료분리로 인해 보어홀 내의 깊이별 첨가재 분포를 비균질하게 하므로 보어홀 상부의 열전도도가 하부에 비해 작게 나타날 수 있는 가능성이 있다.

• 한국재료학회지
• /
• 제24권9호
• /
• pp.488-494
• /
• 2014

The effect of tungsten (W) addition on the hardenability of low-carbon boron steels was investigated using dilatometry, microstructural observations and secondary ion mass spectroscopy. The hardenability was discussed with respect to transformation behaviour aspects depending on the segregation and precipitation of boron at austenite grain boundaries. A critical cooling rate producing a hardness corresponding to 90 % martensite structure was measured from a hardness distribution plot, and was used as a criterion to estimate hardenability at faster cooling rates. In the low-carbon boron steel, the addition of 0.50 wt.% W was comparable to that of 0.20 wt.% molybdenum in terms of critical cooling rate, indicating hardenability at faster cooling rates. However, the addition of 0.50 wt.% W was not more effective than the addition of .0.20 wt.% molybdenum at slower cooling rates. The addition of 0.20 wt.% molybdenum completely suppressed the formation of eutectoid ferrite even at the slow cooling rate of $0.2^{\circ}C/s$, while the addition of 0.50 wt.% W did not, even at the cooling rate of $1.0^{\circ}C/s$. Therefore, it was found that the effect of alloying elements on the hardenability of low-carbon boron steels can be differently evaluated according to cooling rate.

• Journal of Welding and Joining
• /
• 제13권2호
• /
• pp.122-131
• /
• 1995

The effects of cooling rate on the microstructures, precipitation of Cu-cluster, .epsilon.-Cu and impact toughness of high strength low alloy(HSLA) steel were studied using hardness tester, impact tester, DSC(differential scanning calorimetry), AES(auger electron spectroscopy) and TEM(transmission electron microscopy). Not only the Cu-precipitates but also the segregation of Cu, As, Sb, P, S, N, Sn along grain boundary were not observed at the specimens heat treated from 800.deg. C to 300.deg. C with the cooling time of 12-125 sec. The Cu-cluster, .epsilon.-Cu are formed by introducing ageing after cooling and the effect of precipitates on hardening increase after cooling was the same in all cooling rate. The peak hardness was obtained at an ageing of 500.deg. C in all cooling conditions. The impact energy become higher as the cooling time increases. This fact can be explained to be due to the tempering effect applied on the cooling stage since the present alloy has a relatively high Ms temperature and the local high concentration of the retained austenite.

• 한국재료학회지
• /
• 제12권4호
• /
• pp.248-253
• /
• 2002

Effect of Sn addition on the fatigue properties of Al-Cu-Mn cast alloy was investigated by low and high cycle fatigue tests. Fatigue life showed the maximum value of 5450cycles in the Al-Cu-Mn alloy containing 0.10%Sn, but decreased rapidly beyond 0.20% of Sn additions. It was found that the fatigue strength was 132MPa and fatigue ratio was 0.31 in the alloy containing 0.10%Sn. Metallographic observation revealed that the fatigue crack initiated at the surface and propagated along the grain boundary. This propagation path was attributed to the presence of PFZ along the grain boundary. The tensile strength increased from 330MPa in 7he Sn-free Al-Cu-Mn cast alloy to 429MPa in the alloy containing 0.10%Sn. But above 0.20%Sn additions, tensile strength was decreased by the segregation of Sn.

• E2M - 전기 전자와 첨단 소재
• /
• 제10권7호
• /
• pp.659-667
• /
• 1997

The influence of SiO$_2$on the microstructure and electrical properties of zinc oxide varistor was investigated. Zn$_2$SiO$_4$third phase in the sintered body was found at grain boundaries, multiple grain junctions, and occasionally within ZnO grains. This phase acted as a grain growth inhibitor, which retard the grain growth of the ZnO matrix by impeding migration on the grain boundaries. As SiO$_2$ addition increases, average grain size decreased from 40.6${\mu}{\textrm}{m}$ to 26.9${\mu}{\textrm}{m}$ due to the pinning effect by Zn$_2$SiO$_4$ and drag effect by Si segregation at grain boundaries, the breakdown voltage consequently increased. When SiO$_2$ addition is increased, interface state density decreased, however, the barrier height increased by decrease of donor concentration, as a result, the nonlinear exponent increased and leakage current decreased. While, as SiO$_2$ addition increase, it was found that the apparent dielectric loss factor shows a tendency of decrease. Wholly, electrical properties of zinc oxide varistor can be said to be improved by SiO$_2$addition.

• 대한전자공학회논문지SD
• /
• 제44권5호
• /
• pp.1-7
• /
• 2007

Sol-gel 법으로 quartz 기판 위에 Al 도핑 농도와 열처리 온도에 따른 AZO 박막을 제작하였다. 1 % Al 이 도핑되고 550 $^{\circ}C$ 에서 열처리한 ZnO 박막에서 가장 우수한 (002) 배향성과 가장 평탄한 박막 (1.084 nm) 이 제작되었다. 모든 박막은 가시광 영역에서 약 80 % 이상의 투과율을 보였으며, Al 농도가 증가할수록 에너지 밴드 갭이 넓어지는 Burstein-Moss 효과가 관찰되었다. Hall 측정 결과, 순수한 ZnO 박막보다 Al 이 도핑된 ZnO 박막에서 캐리어 농도의 증가와 비저항 값의 감소가 나타났다. 또, Al 의 도핑 농도가 증가함에 따라 segregation 효과로 인한 캐리어 농도의 감소와 비저항 값의 증가가 관찰되었다. 1% Al 이 도핑되고 550 $^{\circ}C$ 에서 열처리한 ZnO 박막에서 가장 큰 캐리어 농도 ($1.80{\times}10^{19}\;cm^{-3}$) 와 가장 낮은 비저항 (0.84 ${\Omega}cm$) 값을 나타내었다.

• 한국주조공학회지
• /
• 제17권6호
• /
• pp.598-607
• /
• 1997

Fractional melting process involves heating an alloy within its liquid-solid region simultaneously ejecting liquid from the solid-liquid mixture. The extent of the purification obtained is comparable to that obtained in multi-pass zone refining. The new fractional melting process in which centrifugal force was used for separating the liquid from the mixture has been developed and applied to the purification of the metallic grade. Refining ratio depends on partition ratio, cake wetness and diffusion in the solid, and it was controlled by various processing parameters such as rotating speed and heating rate. The new parameter called "refining partition coefficient" has been suggested to estimate the effects of processing variables on the refining ratio. Because major impurities in MG-silicon such as Fe, Al, Ni have a low segregation coefficient, good purification effect is expected. The results of refining MG-silicon(98%) showed that 3N-Si was obtained in refined solid of 50% of the original sample.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.567-572
• /
• 2002

This research investigates experimentally an effect on the quality performances of the high flowing concrete according to binder types. The purpose of this study is to determine the optimum mix proportion of the high flowing concrete having good flowability, viscosity and no-segregation. For this purpose, two types using belite cement＋lime stone powder(LSP) and furnace slag cement+lime stone powder are selected and tested by design factors including water cement ratio, fine and coarse aggregate volume ratio. As test results of this study, the optimum mix proportion for binder types is as followings. 1) One type based belite cement ; water cement ratio $51^{\circ}C$, fine aggregate volume ratio $43^{\circ}C$ and coarse aggregate volume ratio $53^{\circ}C$, replacement ratio of LSP $42.7^{\circ}C$. 2) Another type based slag cement : water cement ratio $41^{\circ}C$, fine aggregate volume ratio $47^{\circ}C$ and coarse aggregate volume ratio $53^{\circ}C$, replacement ratio of LSP $13.5^{\circ}C$.

• 천문학회지
• /
• 제35권1호
• /
• pp.29-34
• /
• 2002

We have conducted UBVI CCD photometry of an intermediate-age open cluster NGC 559 to investigate the effect of dynamical evolution on the stellar distributions in NGC 559. Our photometry allows better estimates of distance and age of the cluster owing to much deeper photometry (V $\le$ 21) than previous ones. It is found that the luminosity function and mass function as well as the spatial stellar distributions are affected by the dynamical evolution. Mass segregation leads to the central concentration of the high mass stars, which results in the flattened mass function inside the half mass radius.